Surface treating method and composition for cement
Assignee: Construction Products Research Inc
•
Filing: 1981-06-11
•
Granted: 1982-12-28
•
Expires: 2001-06-11
Abstract
Abstract A method of treating the unset surface of Portland cement concrete to form thereon a hardened surface, that is an integral coating, skin, treatment or mass of high early compressive strength, without substantial shrinkage during setting while exhibiting reduced wet and dry volume changes in the hardened state and prossessing a high degree of impermeability to fluids, abrasion, erosion and chemical resistance and similar characteristics desired in a surface treatment having commercial usefulness in a construction industry. The hardened surface is obtained by dry shaking, that is, sprinkling a dry cementitious composition of alumina cement and gypsum on the unset Portland cement concrete. Additional components, such as viscosity controllers, surface active agents, retarders, accelerators, wet expansion inhibitors, gas generating or gas releasing agents, fly ash, plasticizers, pigments, water retentivity aids, fillers, and aggregates may be utilized to adjust the properties of the composition and impart selective improvement of specific properties.
Inventors
- 👤 Warner K. Babcock
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 14:37
CPC Classifications
C; C04; C04B; C04B41/00; C04B41/009; C04B28/00; C04B28/02; C04B28/06; C04B40/00; C04B40/02; C04B41/45; C04B41/50; C04B41/5076; C04B41/508; C04B41/60; C04B41/61; C04B41/65; E; E04; E04F; E04F15/00; E04F15/12; E04G; E04G21/00; E04G21/02; E04G21/06
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
47 words
A method for producing a hardened, fluid impermeable surface on Portland cement comprising selecting a treating composition comprising aluminous cement and gypsum, applying the treating composition in the dry state to the surface of unset Portland cement and allowing the Portland cement and treating composition to set.
Claim 2
Independent Claim
47 words
A method for producing a hardened, fluid impermeable surface on Portland cement comprising selecting a treating composition comprising aluminous cement and gypsum, applying the treating composition in the dry state to the surface of unset Portland cement and allowing the Portland cement and treating composition to set.
Claim 3
Dependent Claim
44 words
A method for producing a hardened, fluid impermeable surface on Portland cement as claimed in claim 1 wherein the aluminous cement is present in an amount ranging from 50 to 90 percent, by weight, based on the total weight of aluminous cement and gypsum.
Claim 4
Dependent Claim
43 words
A method for producing a hardened, fluid impermeable surface on Portland cement as claimed in claim 1 wherein the gypsum is present in an amount ranging from 10 to 50 percent, by weight, based on the total weight of aluminous cement and gypsum.
Claim 5
Dependent Claim
32 words
A method for producing a hardened, fluid impermeable surface on Portland cement as claimed in claim 1 further exhibiting improved abrasion resistance wherein the treating composition further comprises a salt of lithium.
Claim 6
Dependent Claim
25 words
A method for producing a hardened, fluid impermeable surface on Portland cement as claimed in claim 1 wherein the treating composition further comprises an accelerator.
Claim 7
Dependent Claim
25 words
A method for producing a hardened, fluid impermeable surface on Portland cement as claimed in claim 1 wherein the treating composition further comprises a retarder.
Claim 8
Dependent Claim
79 words
A method for producing a hardened, fluid impermeable surface on Portland cement as claimed in claim 2 or 3 or 4 wherein the aluminous cement is one selected from the group consisting of high alumina cement, calcium aluminate cement and cement whose main cementitious consitituent comprises monocalcium aluminate, and the gypsum is one selected from the group consisting of calcium sulfate, calcium sulfate anhydrate, calcium sulfate hemihydrate, calcium sulfate dihydrate, plaster of Paris, calcined gypsum and pressure calcined gypsum.
Claim 9
Dependent Claim
36 words
A Portland cement structure having a hardened, fluid impermeable surface formed thereon comprising Portland cement and a coating integral therewith comprising the reaction products of unset Portland cement and dry composition comprising aluminous cement and gypsum.
Claim 10
Dependent Claim
36 words
A Portland cement structure having a hardened, fluid impermeable surface formed thereon comprising Portland cement and a coating integral therewith comprising the reaction products of unset Portland cement and dry composition comprising aluminous cement and gypsum.
Claim 11
Dependent Claim
70 words
A Portland cement structure having a hardened, fluid impermeable surface as claimed in claim 11 wherein the aluminous cement is one selected from the group consisting of high alumina cement, calcium aluminate cement and cement whose main cementitious constituent comprises monocalcium aluminate, and the gypsum is one selected from the group consisting of calcium sulfate, calcium sulfate anhydrate, calcium sulfate hemihydrate, calcium sulfate dihydrate, plaster of Paris and calcined gypsum.
References Cited (Backward Citations)
US3861929A
Cited
US3775143A
Cited
US4012264A
Cited
US3922172A
Cited
US4010232A
Cited
US4045237A
Cited
US4094692A
Cited
US4157263A
Cited
US4216022A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-27 | 1986-06-28 | 1986-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-27 | 1990-06-28 | 1990-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-27 | 1994-06-28 | 1994-12-28 | $7700.00 | Window Closed / Lapsed |