Assignee: Applied Industrial Materials Corp
•
Filing: 1981-07-08
•
Granted: 1982-12-28
•
Expires: 2001-07-08
Abstract
Abstract A process for producing silicon in which a reaction mixture consisting, on the one hand, of hot-pressed briquettes of silicon dioxide (quartz) and carbon and, on the other hand, of granular quartz are introduced into an electric furnace and reacted so that silicon carbide is produced from the agglomerates and the silicon carbide then reacts with the quartz which fuses from the granular quartz to produce elemental silicon.
Inventors
- 👤 Gert-Wilhelm Lask
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 09:15
CPC Classifications
C; C01; C01B; C01B33/00; C01B33/02; C01B33/021; C01B33/023; C01B33/025
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
129 words
A process for the production of silicon which comprises the steps of: (a) hot-pressing briquettes from fine-grain quartz and coal to produce briquettes containing substantially 30 to 60% by weight carbon, the balance being substantially silicon dioxide; (b) forming a bed of said briquettes and granular quartz in an electric furnace whereby the granular quartz fills interstices between said briquettes; (c) heating said bed in said furnace to fuse said granular quartz at a temperature of about 1600° C. to effect an internal reaction between the quartz and carbon of the briquettes to transform the silicon dioxide of said briquettes to silicon carbide; and (d) thereafter reacting said silicon carbide with the fused quartz to produce silicon and carbon monoxide at a temperature between 1800° C. and 2000° C.
Claim 2
Dependent Claim
129 words
A process for the production of silicon which comprises the steps of: (a) hot-pressing briquettes from fine-grain quartz and coal to produce briquettes containing substantially 30 to 60% by weight carbon, the balance being substantially silicon dioxide; (b) forming a bed of said briquettes and granular quartz in an electric furnace whereby the granular quartz fills interstices between said briquettes; (c) heating said bed in said furnace to fuse said granular quartz at a temperature of about 1600° C. to effect an internal reaction between the quartz and carbon of the briquettes to transform the silicon dioxide of said briquettes to silicon carbide; and (d) thereafter reacting said silicon carbide with the fused quartz to produce silicon and carbon monoxide at a temperature between 1800° C. and 2000° C.
Claim 3
Dependent Claim
25 words
The process defined in claim 1 wherein fine-grain quartz and coal are briquetted in step (a) at a temperature of substantially 350° to 650° C.
Claim 4
Dependent Claim
20 words
The process defined in claim 2 wherein the briquettes are formed at a temperature of substantially 500° to 600° C.
Claim 5
Dependent Claim
22 words
The process defined in claim 1 wherein the briquettes formed in step (a) have a weight between 10 and 100 g each.
Claim 6
Dependent Claim
19 words
The process defined in claim 4 wherein said briquettes have a weight of substantially 20 to 60 g each.
Claim 7
Dependent Claim
20 words
The process defined in claim 5 wherein said granular quartz has a grain size of substantially 3 to 12 mm.
Claim 8
Dependent Claim
16 words
The process defined in claim 6 wherein said bed is formed with a maximum-density spherical packing.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-27 | 1986-06-28 | 1986-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-27 | 1990-06-28 | 1990-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-27 | 1994-06-28 | 1994-12-28 | $7700.00 | Window Closed / Lapsed |