Method for preparing zeolites
Assignee: Montedison SpA
•
Filing: 1980-12-09
•
Granted: 1982-12-28
•
Expires: 2000-12-09
Abstract
Abstract Preparation of zeolites having the formula: (1.5 +/- 0.6)M2/nO.Al2O3.Y SiO2. Z H2O wherein Y ranges from 20 to 90, Z ranges from 2 to 12, M is at least one cation and n ist the valence of M; said preparation comprises the admixing of diethyl-piperidinium hydroxide [(DEPP)<+>OH<->] or of a salt thereof with water and with: a) at least one sodium compound; b) at least one compound of aluminium; c) at least one compound of silicon; the respective molar ratios, expressed as ratios of oxides, being comprised in the following ranges: SiO2:Al2O3 = from 20 to 120 Na2O:SiO2 = from 0.07 to 0.50 (DEPP)2O:SiO2 = from 0.05 to 0.50 H2O:Na2O = from 50 to 600. The invention concerns also zeolites obtained by said preparation and their use for some acid-catalyzed conversions of hydrocarbons.
Inventors
- 👤 Raymond Le Van Mao
- 👤 Orlando Pilati
- 👤 Enrico Moretti
- 👤 Romano Covini
- 👤 Fausto Genoni
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 14:39
CPC Classifications
C; C07; C07C; C07C6/00; B; B01; B01J; B01J29/00; B01J29/04; B01J29/06; B01J29/70; B01J29/7049; B01J29/72; B01J29/76; C01; C01B; C01B39/00; C01B39/02; C01B39/023; C07C2/00; C07C2/54; C07C4/00; C07C4/02; C07C4/06; C07C4/08; C07C5/00; C07C5/22; C07C5/27; C07C5/2729; C07C5/2732; C07C5/2737; C07C5/32; C07C5/373; C07C5/393; C07C5/41; C07C2529/00; C07C2529/04; C07C2529/06; Y; Y02; Y02P; Y02P20/00; Y02P20/50; Y02P20/52
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
183 words
A method for preparing zeolites having the formula: (1.5±0.6)M.sub.2/n O.Al.sub.2 O.sub.3.ySiO.sub.2.zH.sub.2 O wherein y ranges from 20 to 90, z ranges from 2 to 12, M is at least one cation and n is the valence of M, and wherein Al and Si can be optionally replaced, at least partially, by Ga and Ge respectively, said method comprising the admixing of diethylpiperidinium hydroxide or of a salt thereof with H 2 O and with at least: (a) one sodium compound; (b) one compound of a metal selected from the group comprising Al, Ga and mixtures thereof; (c) one compound of an element selected from the group comprising Si, Ge and mixtures thereof, the molar ratios, expressed as ratios of oxides, being comprised within the following ranges: SiO 2 :Al 2 O 3 =from 20 to 120 Na 2 O:SiO 2 =from 0.07 to 0.50 (DEPP) 2 O:SiO 2 =from 0.05 to 0.50 H 2 O:Na 2 O=from 50 to 600, and wherein the resulting start mixture is heated, for crystallization purposes, at from 160° C. to 200° C. for at least 24 hours.
Claim 2
Independent Claim
183 words
A method for preparing zeolites having the formula: (1.5±0.6)M.sub.2/n O.Al.sub.2 O.sub.3.ySiO.sub.2.zH.sub.2 O wherein y ranges from 20 to 90, z ranges from 2 to 12, M is at least one cation and n is the valence of M, and wherein Al and Si can be optionally replaced, at least partially, by Ga and Ge respectively, said method comprising the admixing of diethylpiperidinium hydroxide or of a salt thereof with H 2 O and with at least: (a) one sodium compound; (b) one compound of a metal selected from the group comprising Al, Ga and mixtures thereof; (c) one compound of an element selected from the group comprising Si, Ge and mixtures thereof, the molar ratios, expressed as ratios of oxides, being comprised within the following ranges: SiO 2 :Al 2 O 3 =from 20 to 120 Na 2 O:SiO 2 =from 0.07 to 0.50 (DEPP) 2 O:SiO 2 =from 0.05 to 0.50 H 2 O:Na 2 O=from 50 to 600, and wherein the resulting start mixture is heated, for crystallization purposes, at from 160° C. to 200° C. for at least 24 hours.
Claim 3
Dependent Claim
48 words
A method according to claim 1, characterized by the following ranges of molar ratios: SiO 2 :Al 2 O 3 =from 40 to 85 Na 2 O:SiO 2 =from 0.07 to 0.25 (DEPP) 2 O:SiO 2 =from 0.10 to 0.20 H 2 O:Na 2 O=from 150 to 400.
Claim 4
Dependent Claim
26 words
A method according to claim 2, wherein the cation dilution ratios are as follows: r1=equal to or higher than 190. r2=equal to or higher than 90.
Claim 5
Dependent Claim
29 words
A method according to claim 2, wherein the sodium factor r2:r1 (SF) is from 0.20 to 0.60, and wherein the cation mineralization factor (CMF) is from 0.22 to 0.38.
Claim 6
Dependent Claim
21 words
A method according to claim 4, wherein SF is from 0.30 to 0.50 and wherein CMF is from 0.22 to 0.30.
Claim 7
Dependent Claim
21 words
A method according to claim 4, wherein SF is from 0.50 to 0.60 and wherein CMF is from 0.22 to 0.30.
Claim 8
Dependent Claim
21 words
A method according to claim 4, wherein SF is from 0.30 to 0.50 and wherein CMF is from 0.30 to 0.38.
Claim 9
Dependent Claim
29 words
A method according to claim 4, wherein the start mixture is heated, until crystallization, in only one step, at from 180° to 200° C., for at least 24 hours.
Claim 10
Dependent Claim
79 words
A method according to claim 4, wherein an aqueous solution is prepared, which contains the DEPP salt, Na aluminate and NaOH, secondly the solution is heated between 60° and 70° C., thirdly a solution containing SiO 2 is added, then the whole is heated for crystallization purposes and finally the crystallized zeolite is washed, dried and activated by means of heating in the air at a temperature from 450° C. to the temperature at which the structural collapse starts.
Claim 11
Dependent Claim
26 words
A method according to claim 4, characterized in that the DEPP salt is (DEPP)Br, (a) is NaOH, (b) is Na aluminate and(c) is a silica sol.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-27 | 1986-06-28 | 1986-12-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-27 | 1990-06-28 | 1990-12-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-27 | 1994-06-28 | 1994-12-28 | $7700.00 | Window Closed / Lapsed |