US4364877A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for producing fritted alumina members
Assignee: EUROPEENNE DES CERAMIQUES ALUMINEUSES "EUROCERL ZI Ste
•
Filing: 1981-01-27
•
Granted: 1982-12-21
•
Expires: 2001-01-27
Abstract
Abstract A process for producing fritted alumina members having a high optical transparency and a high mechanical strength of the type involving the production of the members from a high purity alumina powder to which has been added an organic binder and a small percentage of oxide, particularly of magnesium and/or rare earth, followed by the shaping thereof and subjecting them to two successive heat treatments, namely a first treatment in an oxidizing atmosphere to remove the binder and consolidate the particles and a second treatment at a higher temperature and in a hydrogen-rich atmosphere for obtaining fritting, wherein the second heat treatment takes place by continuously passing the said members through a kiln kept at a temperature between 1820° and 1970° C. at a constant translation speed between 3 and 50 millimeters per minute, the total time necessary for firing a member from the consolidated or slightly warm state up till its return to ambient temperature varying from approximately 30 minutes to a maximum of 5 hours.
Inventors
- 👤 Rene Clement
- 👤 Francis Gugliermotte
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:48
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/115; C04B35/622; C04B35/64
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
164 words
A process for producing fritted alumina members having a high optical transparency and a high mechanical strength from a high purity alumina powder to which has been added an organic binder and a small percentage of oxide, particularly of magnesium and/or rare earth, followed by the shaping thereof and subjecting them to two successive heat treatments, namely a first treatment in an oxidizing atmosphere to remove the binder and consolidate the particles and a second treatment at a higher temperature and in a hydrogen-rich atmosphere for obtaining fritting, wherein the second heat treatment takes place by continuously passing the said members at a constant translation speed between 3 and 50 millimeters per minute through a kiln kept at a temperature between 1820° and 1970° C. and having a heat gradient therein, the total time necessary for firing a member from the consolidated or slightly warm state up till its return to ambient temperature varying from approximately 30 minutes to a maximum of 5 hours.
Claim 2
Dependent Claim
164 words
A process for producing fritted alumina members having a high optical transparency and a high mechanical strength from a high purity alumina powder to which has been added an organic binder and a small percentage of oxide, particularly of magnesium and/or rare earth, followed by the shaping thereof and subjecting them to two successive heat treatments, namely a first treatment in an oxidizing atmosphere to remove the binder and consolidate the particles and a second treatment at a higher temperature and in a hydrogen-rich atmosphere for obtaining fritting, wherein the second heat treatment takes place by continuously passing the said members at a constant translation speed between 3 and 50 millimeters per minute through a kiln kept at a temperature between 1820° and 1970° C. and having a heat gradient therein, the total time necessary for firing a member from the consolidated or slightly warm state up till its return to ambient temperature varying from approximately 30 minutes to a maximum of 5 hours.
Claim 3
Dependent Claim
52 words
A process according to claim 1, wherein the members in the form of tubes are regularly displaced in the longitudinal direction with respect to the heat gradient, so that at any instant only a short portion of the material is at firing temperature from one to the other end of the member.
Claim 4
Dependent Claim
40 words
A process according to claim 1, wherein the members in the form of tubes are regularly displaced in the transverse direction with respect to the heat gradient, each member being completely raised to an increasing and then a decreasing temperature.
Claim 5
Dependent Claim
29 words
A process according to any one of the claims 1 to 3, wherein the kiln is exposed to a circulation of pure hydrogen during the passage of the members.
Claim 6
Dependent Claim
38 words
A process according to claim 4, wherein the kiln is exposed to a circulation of hydrogen to which are added small quantities of oxygen and/or carbon monoxide and/or nitrogen and/or water vapour during the passage of the members.
Claim 7
Dependent Claim
30 words
A process according to claim 4, wherein the oxide of magnesium and/or rare earth added to the pure alumina powder is in a proportion between 0.01 and 0.1% by weight.
Claim 8
Dependent Claim
33 words
A process according to claim 1, wherein said kiln includes a localized heat source and said second heat treatment includes maintaining said localized heat source at said temperature to provide said heat gradient.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-20 | 1986-06-21 | 1986-12-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-20 | 1990-06-21 | 1990-12-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-20 | 1994-06-21 | 1994-12-21 | $7700.00 | Window Closed / Lapsed |