Method for providing ceramic lining to a hollow body by thermit reaction
Assignee: National Institute of Advanced Industrial Science and Technology
•
Filing: 1980-11-06
•
Granted: 1982-12-14
•
Expires: 2000-11-06
Abstract
Abstract The invention provides a novel method for forming a ceramic lining layer on the inward surface of a hollow body such as a pipe. According to the invention, a thermit mixture, for example, composed of aluminum powder and an iron oxide is placed in the hollow space of the hollow body, which is rotated at a high speed so as that the thermit mixture is pressed against the wall of the hollow body by the centrifugal force and the thermit mixture is ignited, for example, by contacting with an acetylene flame. The thermit reaction of the thermit mixture propagates under the influence of the centrifugal force so that the molten metal formed from the reducible metal oxide and the ceramic oxide formed from the strongly reductive element are separated into stratified layers by virtue of their density difference with the ceramic oxide forming the innermost layer and the metal forming the intermediate layer between the ceramic oxide layer and the wall of the hollow body with strong bonding of the ceramic oxide layer upon solidification by cooling.
Inventors
- 👤 Osamu Odawara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 20:38
CPC Classifications
C; C23; C23D; C23D5/00; C23D5/10
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
225 words
A method for providing a ceramic lining of layer on the inner surface of a hollow metal body which comprises the steps of (a) placing a powdery thermit mixture comprising a strongly reductive element and a reducible metal oxide in the hollow space of the hollow body, (b) rotating the hollow body around an axis so that the powdery thermit mixture is pressed against the inner surface of the hollow body by centrifugal force to form a layer, (c) igniting the thermit mixture at least at one point of the layer thereof formed on the inner surface of the hollow body while still under the centrifugal force so that the thermit reaction of the thermit mixture takes place and the reducible metal oxide is reduced to a molten metal and the strongly reductive element is oxidized to an oxide which forms an innermost layer of ceramic material with the molten metal forming an intermediate layer between the inner surface of the hollow body and the innermost layer, (d) degassing the space within the hollow body by means of a vacuum to remove thermit reaction gasses and to remove gasses from the layers, and (e) then cooling the hollow body to solidify said intermediate and innermost layers and provide on the inner surface of the hollow body, stratified layers of the metal and the ceramic material.
Claim 2
Independent Claim
225 words
A method for providing a ceramic lining of layer on the inner surface of a hollow metal body which comprises the steps of (a) placing a powdery thermit mixture comprising a strongly reductive element and a reducible metal oxide in the hollow space of the hollow body, (b) rotating the hollow body around an axis so that the powdery thermit mixture is pressed against the inner surface of the hollow body by centrifugal force to form a layer, (c) igniting the thermit mixture at least at one point of the layer thereof formed on the inner surface of the hollow body while still under the centrifugal force so that the thermit reaction of the thermit mixture takes place and the reducible metal oxide is reduced to a molten metal and the strongly reductive element is oxidized to an oxide which forms an innermost layer of ceramic material with the molten metal forming an intermediate layer between the inner surface of the hollow body and the innermost layer, (d) degassing the space within the hollow body by means of a vacuum to remove thermit reaction gasses and to remove gasses from the layers, and (e) then cooling the hollow body to solidify said intermediate and innermost layers and provide on the inner surface of the hollow body, stratified layers of the metal and the ceramic material.
Claim 3
Dependent Claim
23 words
The method as claimed in claim 1 wherein the strongly reductive element is selected from the group consisting of aluminum, magnesium and silicon.
Claim 4
Dependent Claim
14 words
The method as claimed in claim 1 wherein the strongly reductive element is aluminum.
Claim 5
Dependent Claim
31 words
The method as claimed in claim 1 wherein the reducible metal oxide is selected from the group consisting of the oxides of iron, chromium, nickel, titanium, vanadium, zinc, copper and manganese.
Claim 6
Dependent Claim
17 words
The method as claimed in claim 1 wherein the reducible metal oxide is an oxide of iron.
Claim 7
Dependent Claim
25 words
The method as claimed in claim 1 wherein the thermit mixture is a stoichiometric mixture of the strongly reductive element and the reducible metal oxide.
Claim 8
Dependent Claim
25 words
The method as claimed in claim 1 wherein the thermit mixture is a non-stoichiometric mixture of the strongly reductive element and the reducible metal oxide.
Claim 9
Dependent Claim
31 words
The method as claimed in claim 7 wherein the thermit mixture contains at least 50% by weight of the stoichiometric mixture of the strongly reductive element and the reducible metal oxide.
Claim 10
Dependent Claim
42 words
The method as claimed in claim 1 wherein the hollow body is rotated around an axis at such a velocity that the thermit mixture placed in the hollow space of the hollow body receives a centrifugal force of at least 50 G.
Claim 11
Dependent Claim
20 words
The method as claimed in claim 9 wherein the centrifugal force is in the range from 100 to 200 G.
References Cited (Backward Citations)
US3551188A
Cited
US3974306A
Cited
US4048352A
Cited
US4117868A
Cited
US4142556A
Cited
US4150182A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-12-13 | 1986-06-14 | 1986-12-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-12-13 | 1990-06-14 | 1990-12-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-12-13 | 1994-06-14 | 1994-12-14 | $7700.00 | Window Closed / Lapsed |