Process for the production of fibrous activated carbon

Claim 2

A process for producing a fibrous activated carbon which comprises (1) spinning a dope of a polyacrylonitrile or a copolymer thereof comprising at least about 60 wt% acrylonitrile to thereby obtain an acrylonitrile-based fiber having a diameter of from 1.5 to 15 denier, (2) treating the acrylonitrile-based fiber with a solution of an iron compound to thereby obtain an acrylonitrile-based fiber containing the iron compound in the range satisfying the equation (1) ##EQU2## wherein X is the wt% content of comonomer in the acrylonitrile-based fiber and y is the wt% iron content, (3) preoxidizing the acrylonitrile-based fiber containing the iron compound at an initial heat-treatment temperature satisfying the equation (2) 28- 5X≦Z≦290-4X wherein X has the same meaning as in equation (1) and Z is the initial heat-treatment temperature (°C.), the iron compound preventing substantial coalescence during preoxidizing, and (4) then gas activating the preoxidized acrylonitrile-based fiber.

Claim 3

A process as in claim 1, wherein said copolymer comprises from about 6 to 40 wt% of at least one comonomer.

Claim 4

A process as in claim 1, wherein said copolymer comprises from about 8 to 15 wt% of at least one comonomer.

Claim 5

A process as in claim 1, wherein said fiber has a diameter of from 2.0 to 7.0 denier.

Claim 6

A process as in claim 1, wherein said iron compound is an iron salt or an iron-complex salt.

Claim 7

A process as in claim 1, wherein said iron compound is ferric or ferrous sulfate, ferric or ferrous chloride, ferric or ferrous nitrate, ferric or ferrous ammonium nitrate, ferric or ferrous oxide, sodium or potassium ferricyanide, or sodium or potassium ferrocyanide.

Claim 8

A process as in claim 1, wherein said acrylonitrile-based fiber containing an iron compound is obtained by impregnating a gel fiber of the acrylonitrile-based fiber after spinning and prior to drying with a solution of the iron compound.

Claim 9

A process as in claim 1, wherein said acrylonitrile-based fiber containing an iron compound is obtained by soaking the fibers with a solution of the iron compound.

Claim 10

A process as in claim 1, wherein said acrylonitrile-based fiber is in the form of a tow, felt, woven fabric, or nonwoven fabric.

Claim 11

A process as in claim 1, wherein said acrylonitrile-based fiber is in the form of a tow consisting of more than about 40,000 filaments.

Claim 12

A process as in claim 1, wherein said acrylonitrile-based fiber is in the form of felt, woven fabric, or nonwoven fabric having a weight of more than 150 g/cm 2 .

Claim 13

A process as in claim 1, wherein said acrylonitrile-based fiber is preoxidized until the equilibrium water content of said fiber reaches from 8 to 13%.

Claim 14

A process as in claim 1, wherein said preoxidized fiber is activated by heating in CO 2 , NH 3 , steam, or a mixed gas thereof at a temperature of from about 600° to 1,300° C.

Claim 15

A process as in claim 1, wherein said preoxidized fiber is activated until the specific surface area of the fibrous activated carbon reaches from about 300 to 2,000 m 2 /g.

Claim 16

A process as in claim 14, wherein said fibrous activated carbon contains from about 2 to 15 wt% nitrogen.

Claim 17

A process as in claim 1, wherein after preoxidation at said initial heat-treatment temperature the fiber is preoxidized at a higher temperature which is less than about 400° C.

Claim 18

A fibrous activated carbon containing an iron compound having a specific surface area of from about 300 to 2,000 m 2 /g, a nitrogen content of from about 2 to 15 wt%, a fiber strength of from about 25 to 35 Kg/mm 2 and a diameter of from about 3 to 30μ, said fibrous activated carbon being produced by the process which comprises (1) spinning a dope of a polyacrylonitrile or a copolymer thereof comprising at least about 60 wt% acrylonitrile to thereby obtain an acrylonitrile-based fiber having a diameter of from 1.5 to 15 denier, (2) treating the acrylonitrile-based fiber with a solution of an iron compound to thereby obtain an acrylonitrile-based fiber containing the iron compound in the range satisfying the equation (1) ##EQU3## wherein X is the wt% content of comonomer in the acrylonitrile-based fiber and y is the wt% iron content, (3) preoxidizing the acrylonitrile-based fiber containing the iron compound at an initial heat-treatment temperature satisfying the equation (2) 28- 5X≦Z≦290-4X wherein X has the same meaning as in equation (1) and Z is the initial heat-treatment temperature (°C.), the iron compound preventing substantial coalescence during preoxidizing, and (4) then gas activating the preoxidized acrylonitrile-based fiber.

Claim 19

A fibrous activated carbon containing an iron compound having a specific surface area of from about 300 to 2,000 m 2 /g, a nitrogen content of from about 2 to 15 wt%, a fiber strength of from about 25 to 35 Kg/mm 2 and a diameter of from about 3 to 30μ, said fibrous activated carbon being produced by the process which comprises (1) spinning a dope of a polyacrylonitrile or a copolymer thereof comprising at least about 60 wt% acrylonitrile to thereby obtain an acrylonitrile-based fiber having a diameter of from 1.5 to 15 denier, (2) treating the acrylonitrile-based fiber with a solution of an iron compound to thereby obtain an acrylonitrile-based fiber containing the iron compound in the range satisfying the equation (1) ##EQU3## wherein X is the wt% content of comonomer in the acrylonitrile-based fiber and y is the wt% iron content, (3) preoxidizing the acrylonitrile-based fiber containing the iron compound at an initial heat-treatment temperature satisfying the equation (2) 28- 5X≦Z≦290-4X wherein X has the same meaning as in equation (1) and Z is the initial heat-treatment temperature (°C.), the iron compound preventing substantial coalescence during preoxidizing, and (4) then gas activating the preoxidized acrylonitrile-based fiber.