Pressure sensitive adhesive compositions
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1981-11-09
•
Granted: 1982-11-30
•
Expires: 2001-11-09
Abstract
Abstract This invention relates to pressure sensitive adhesive compositions which includes a hydrogenated block copolymer such as Kraton G, about 25 to about 250 parts by weight of a hydrocarbon resin of a petroleum or coal tar distillate, aliphatic dienes and mono- and diolefins, cyclic olefins of 5 or 6 carbon atoms and hydrogenated poly cyclics per 100 parts by weight of the hydrogenated block copolymer, and about 25 to 200 parts by weight of a polybutene or polyisobutylene per 100 parts of the hydrogenated block copolymer, wherein said mixture of Kraton G, said hydrocarbon resin and said polybutene or polyisobutylene are dissolved in a non-reactive solvent at a concentration level of about 5 to about 25 grams per 100 mil of non-reactive solvent.
Inventors
- 👤 Pawan K. Agarwal
- 👤 Vincent L. Hughes
- 👤 Robert D. Lundberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:24
CPC Classifications
C; C09; C09J; C09J123/00; C09J123/02; C09J123/18; C09J123/20; C09J153/00; C09J153/02; C09J153/025; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/28
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
122 words
A solvent based pressure sensitive adhesive composition which comprises: (a) a hydrogenated block copolymer of polystyrene and a hydrogenated polydiene, said diene being selected from the group consisting of poly-butadiene and polyisoprene; (b) about 25 to about 250 parts by weight of a hydrocarbon resin of a petroleum or coal tar distillate per 100 parts by weight of said hydrogenated block copolymer; (c) about 25-200 parts by weight of polybutene or polyisobutylene per 100 parts of said hydrogenated block copolymer; and (d) a non-reactive solvent, the mixture of said hydrogenated block copolymer, said hydrocarbon resin, and said polyisobutylene or said polybutene being dissolved in a non-reactive solvent at a concentration level of about 5 to about 25 grams per 100 ml/non-reactive solvent.
Claim 2
Dependent Claim
122 words
A solvent based pressure sensitive adhesive composition which comprises: (a) a hydrogenated block copolymer of polystyrene and a hydrogenated polydiene, said diene being selected from the group consisting of poly-butadiene and polyisoprene; (b) about 25 to about 250 parts by weight of a hydrocarbon resin of a petroleum or coal tar distillate per 100 parts by weight of said hydrogenated block copolymer; (c) about 25-200 parts by weight of polybutene or polyisobutylene per 100 parts of said hydrogenated block copolymer; and (d) a non-reactive solvent, the mixture of said hydrogenated block copolymer, said hydrocarbon resin, and said polyisobutylene or said polybutene being dissolved in a non-reactive solvent at a concentration level of about 5 to about 25 grams per 100 ml/non-reactive solvent.
Claim 3
Dependent Claim
76 words
An composition according to claim 1 further including about 1 to about 150 parts by weight of a filler per 100 parts by weight of said hydrogenated block copolymer, said filler being selected from the group consisting of calcium carbonates, silicas, carbon blacks, clays and talcs and mixtures thereof and/or less than about 100 parts by weight of an oil having less than 2 weight percent per 100 parts by weight of said hydrogenated block copolymer.
Claim 4
Dependent Claim
34 words
An adhesive composition according to claim 1 or 2 wherein said hydrocarbon resin is made from monomers with 5 to 6 carbon atoms and consists of aliphatic dienes, mono and diolefins and cyclic olefins.
Claim 5
Dependent Claim
30 words
An adhesive composition according to claim 1 further including about 1 to about 150 parts by weight of a filler per 100 parts by weight of the hydrogenated block copolymer.
Claim 6
Dependent Claim
31 words
An adhesive composition according to claims 1 or 4 further including less than about 25 parts by weight of an oil per 100 parts by weight of the hydrogenated block copolymer.
References Cited (Backward Citations)
US3767608A
Cited
US3801531A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |