Cross-linked hydrogel copolymers for contact lenses
Assignee: COOPERVISION TECHNOLOGY Inc
•
Filing: 1979-11-29
•
Granted: 1982-11-30
•
Expires: 1999-11-29
Abstract
Abstract The invention relates to soft contact lenses having a water content of at least about 45% and comprising a hydrated copolymer of a major proportion of an hydroxyalkyl acrylate or methacrylate, up to 12% by weight of an ethylenically unsaturated acid or anhydride, a minor proportion of a cross-linking monomer and a minor proportion of styrene or a substituted styrene, the free acid or anhydride groups being in salt form.
Inventors
- 👤 Ivor B. Atkinson
- 👤 Barry C. Holdstock
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:13
CPC Classifications
G; G02; G02C; G02C7/00; G02C7/02; G02C7/04; Y; Y10; Y10S; Y10S425/00; Y10S425/808; Y10S526/00; Y10S526/93; Y10S526/936
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
104 words
A soft contact lens having a water content of at least about 30% by weight based on the weight of the hydrated lens, said lens being characterized by a high tensile strength and composed of a hydrated copolymer comprising units from a major proportion of an hydroxyalkyl acrylate or methacrylate, up to 12% by weight of an ethylenically unsaturated acid or anhydride based on the total weight of comonomers, a minor proportion of a cross-linking monomer, and from about 4 to about 30% by weight of styrene or a substituted styrene, with free acid or anhydride groups in the copolymer being in salt form.
Claim 2
Dependent Claim
104 words
A soft contact lens having a water content of at least about 30% by weight based on the weight of the hydrated lens, said lens being characterized by a high tensile strength and composed of a hydrated copolymer comprising units from a major proportion of an hydroxyalkyl acrylate or methacrylate, up to 12% by weight of an ethylenically unsaturated acid or anhydride based on the total weight of comonomers, a minor proportion of a cross-linking monomer, and from about 4 to about 30% by weight of styrene or a substituted styrene, with free acid or anhydride groups in the copolymer being in salt form.
Claim 3
Dependent Claim
39 words
A lens according to claim 1 wherein the unsaturated acid or anhydride is a carboxylic acid and or anhydride and the free carboxylic acid or anhydride groups are in the form of alkali or alkaline earth carboxylate salt groups.
Claim 4
Dependent Claim
34 words
A lens according to claim 2 wherein the unsaturated carboxylic acid or anhydride is present in the copolymer in an amount of from 0.5 to 12% by weight of the total weight of comonomers.
Claim 5
Dependent Claim
26 words
A lens according to claim 1 in which the water content of the hydrated copolymer is from 50 to 85% of the total weight of comonomers.
Claim 6
Dependent Claim
85 words
A contact lens which comprises a hydrated, sparingly cross-linked copolymer of a major proportion of an hydroxyalkyl acrylate or methacrylate, up to 12% by weight of an ethylenically unsaturated carboxylic acid or anhydride, up to about 5% of a cross-linking monomer and from about 4 to about 30% of styrene or substituted styrene, at least some of the carboxylic acid or anhydride groups in the copolymer being in salt form, the percentages of each comonomer being calculated by weight of the total weight of comonomers.
Claim 7
Dependent Claim
85 words
A contact lens which comprises a hydrated, sparingly cross-linked copolymer of a major proportion of an hydroxyalkyl acrylate or methacrylate, up to 12% by weight of an ethylenically unsaturated carboxylic acid or anhydride, up to about 5% of a cross-linking monomer and from about 4 to about 30% of styrene or substituted styrene, at least some of the carboxylic acid or anhydride groups in the copolymer being in salt form, the percentages of each comonomer being calculated by weight of the total weight of comonomers.
Claim 8
Dependent Claim
38 words
A lens according to claim 5 which is a graft copolymer of a hydrophobic styrene copolymer containing active centers copolymerized with one or more comonomers selected from hydroxy alkyl acrylates or methacrylates and cross-linked with a cross-linking monomer.
References Cited (Backward Citations)
US3876581A
Cited
GB1475605A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |