Electrolytic surface modulation
Assignee: Case Western Reserve University
•
Filing: 1981-11-10
•
Granted: 1982-11-30
•
Expires: 2001-11-10
Abstract
Abstract The surface of an electrically conductive substrate is electrolytically modulated to a predetermined profile by subjecting the surface to electrodeposition or electrodissolution through ionically conductive body portions of an ionic conductance resist which masks the surface. The rate of passage of ionic species to or from any given point along the masked surface is controlled by the trans-resist ionic conductance or resistance at that point. The predetermined surface profile is generated by providing the resist with a trans-resist ionic conductance or resistance profile which patterns the predetermined surface profile.
Inventors
- 👤 John C. Angus
- 👤 Kathleen M. Tomaswick
- 👤 Uziel Landau
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 23:21
CPC Classifications
G; G03; G03F; G03F7/00
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
158 words
A method of electrolytically modulating the surface of an electrically conductive substrate to a predetermined profile, comprising the steps of: (a) masking said surface with an ionic conductance resist having ionically conductive body portions and exhibiting a trans-resist ionic conductance or resistance profile which patterns said predetermined surface profile; (b) subjecting the masked surface to electrolytic treatment with an ionic solution so as to effect modulation of said surface by passage of ionic species to or from said surface, at least a substantial proportion of said passage occurring through said body portions of said resist, the rate of said surface modulating ionic species passage at any given point along the masked portion of said surface being controlled by the transresist ionic conductance or resistance at that point, said electrolytic treatment being carried out for a period of time sufficient to thereby generate said predetermined surface profile; and (c) removing said resist to thereby expose the resulting modulated surface.
Claim 2
Independent Claim
158 words
A method of electrolytically modulating the surface of an electrically conductive substrate to a predetermined profile, comprising the steps of: (a) masking said surface with an ionic conductance resist having ionically conductive body portions and exhibiting a trans-resist ionic conductance or resistance profile which patterns said predetermined surface profile; (b) subjecting the masked surface to electrolytic treatment with an ionic solution so as to effect modulation of said surface by passage of ionic species to or from said surface, at least a substantial proportion of said passage occurring through said body portions of said resist, the rate of said surface modulating ionic species passage at any given point along the masked portion of said surface being controlled by the transresist ionic conductance or resistance at that point, said electrolytic treatment being carried out for a period of time sufficient to thereby generate said predetermined surface profile; and (c) removing said resist to thereby expose the resulting modulated surface.
Claim 3
Dependent Claim
27 words
The method of claim 1, wherein said resist is composed of a substantially continuous body of material and exhibits a varying trans-resist ionic conductance or resistance profile.
Claim 4
Dependent Claim
32 words
The method of claim 2, wherein said resist is of varying thickness, and the trans-resist ionic conductance at any given point along said resist varies inversely with the thickness at that point.
Claim 5
Dependent Claim
75 words
The method of claim 2, wherein said resist is formed by exposing a photosensitive polymeric film to light through an optical mask exhibiting an optical density profile which patterns said predetermined surface profile, the variations in the amount of light received by different areas of the thus exposed film producing corresponding variations in the extent to which said areas become crosslinked, thereby serving to induce the requisite ionic conductance or resistance profile in said resist.
Claim 6
Dependent Claim
64 words
The method of claim 4, wherein the requisite ionic conductance or resistance profile is further developed in said resist by treating said exposed film with a solvent which selectively dissolves uncrosslinked portions of said film, whereby the resist is formed with variations in its thickness, the trans-resist ionic conductance at any given point along said resist varying inversely with the thickness at that point.
Claim 7
Independent Claim
32 words
The method of either of claims 4 or 5, wherein said photosensitive polymeric film is coated onto said surface being modulated prior to carrying out said exposure of said film to light.
Claim 8
Dependent Claim
14 words
The method of claim 1, wherein said electrolytic treatment is electrodeposition onto said surface.
Claim 9
Dependent Claim
15 words
The method of claim 7, wherein a metallic species is electrodeposited onto a metallic substrate.
Claim 10
Dependent Claim
14 words
The method of claim 1, wherein said electrolytic treatment is electrodissolution of said surface.
Claim 11
Dependent Claim
23 words
The method of claim 4 or 5, wherein the photosensitive polymeric film is exposed prior to being plated onto said surface being modulated.
References Cited (Backward Citations)
US3791858A
Cited
US3930857A
Cited
US3986939A
Cited
US4024631A
Cited
US4247377A
Cited
US4217183A
Cited
US4325780A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |