Flame spray powder
Assignee: Eutectic Corp
•
Filing: 1981-11-20
•
Granted: 1982-11-30
•
Expires: 2001-11-20
Abstract
Abstract A free-flowing self-bondable flame spray powder derived from an atomized alloy powder is provided in which the particles are characterized by aspherical shapes and have an average particle size within the range of about plus 400 mesh to minus 100 mesh. The aspherically shaped powder is further characterized by a specific surface of about 180 cm 2 /gr and higher and has a composition consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Inventors
- 👤 Burton A. Kushner
- 👤 Michael J. Jirinec
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 19:04
CPC Classifications
C; C23; C23C; C23C4/00; C23C4/04; C23C4/06; C23C4/067
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
111 words
A free-flowing self-bondable flame spray powder derived from an atomized alloy powder, said powder having particles characterized by aspherical shapes and having an average particle size within the range of about plus 400 mesh to minus 100 mesh, said aspherically shaped powder being further characterized by a specific surface of about 180 cm 2 /gr and higher, said flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Claim 2
Dependent Claim
111 words
A free-flowing self-bondable flame spray powder derived from an atomized alloy powder, said powder having particles characterized by aspherical shapes and having an average particle size within the range of about plus 400 mesh to minus 100 mesh, said aspherically shaped powder being further characterized by a specific surface of about 180 cm 2 /gr and higher, said flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Claim 3
Dependent Claim
73 words
The free-flowing self-bondable flame spray powder of claim 1, wherein the average particle size of said aspherical powder ranges from about 325 mesh to 140 mesh and wherein the alloy consists essentially of about 0.02% to 0.035% C, about 18% to 22% Mo, about 1.6% to 1.8% Si, about 3% to 6% W, about 7% to 10% Ti, about 17% to 20% Fe, about 0.2% to 0.4% V, and the balance essentially nickel.
Claim 4
Dependent Claim
21 words
The free-flowing self-bonding flame spray powder of claim 1, wherein the alloy additionally consists essentially of up to about 5% Cr.
Claim 5
Dependent Claim
105 words
A free-flowing self-bondable atomized flame spray powder having particles characterized by randomly irregular aspherical shapes and having an average particle size ranging from about 325 mesh to 140 mesh, said randomly irregular aspherically shaped powder being further characterized by a specific surface of about 250 cm 2 /gr and higher, said atomized flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Claim 6
Dependent Claim
105 words
A free-flowing self-bondable atomized flame spray powder having particles characterized by randomly irregular aspherical shapes and having an average particle size ranging from about 325 mesh to 140 mesh, said randomly irregular aspherically shaped powder being further characterized by a specific surface of about 250 cm 2 /gr and higher, said atomized flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Claim 7
Dependent Claim
54 words
The free-flowing flame spray powder of claim 4, wherein the alloy consists essentially of about 0.02% to 0.035% C, about 18% to 22% Mo, about 1.6% to 1.8% Si, about 3% to 6% W, about 7% to 10% Ti, about 17% to 20% Fe, about 0.2% to 0.4% V, and the balance essentially nickel.
Claim 8
Independent Claim
122 words
A method of producing an adherent metal coating on a metal substrate, said method comprising flame spraying a free-flowing powder derived from an atomized alloy and having particles characterized by aspherical shapes and an average particle size within the range of about plus 400 mesh to minus 100 mesh, said aspherically shaped powder being further characterized by a specific surface of about 180 cm 2 /gr and higher, said flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Claim 9
Independent Claim
122 words
A method of producing an adherent metal coating on a metal substrate, said method comprising flame spraying a free-flowing powder derived from an atomized alloy and having particles characterized by aspherical shapes and an average particle size within the range of about plus 400 mesh to minus 100 mesh, said aspherically shaped powder being further characterized by a specific surface of about 180 cm 2 /gr and higher, said flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickel.
Claim 10
Dependent Claim
72 words
The flame spray method of claim 6, wherein the average particle size of aspherical powder being sprayed ranges from about 325 mesh to 140 mesh and wherein the alloy consists essentially of about 0.02% to 0.035% C, about 18% to 22% Mo, about 1.6% to 1.8% Si, about 3% to 6% W, about 7% to 10% Ti, about 17% to 20% Fe, about 0.2% to 0.4% V, and the balance essentially nickel.
Claim 11
Dependent Claim
21 words
The method of claim 6, wherein the alloy powder being flame sprayed additionally consists essentially of up to about 5% Cr.
Claim 12
Independent Claim
119 words
A method of producing an adherent metal coating on a metal substrate, said method comprising flame spraying a free-flowing atomized powder having particles characterized by randomly irregular aspherical shapes and having an average particle size ranging from about 325 mesh to 140 mesh, said randomly irregular aspherically shaped powder being further characterized by a specific surface of about 250 cm 2 /gr and higher, said atomized flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickle.
Claim 13
Independent Claim
119 words
A method of producing an adherent metal coating on a metal substrate, said method comprising flame spraying a free-flowing atomized powder having particles characterized by randomly irregular aspherical shapes and having an average particle size ranging from about 325 mesh to 140 mesh, said randomly irregular aspherically shaped powder being further characterized by a specific surface of about 250 cm 2 /gr and higher, said atomized flame spray powder being formed of an alloy consisting essentially by weight of up to about 0.1% C, about 3% to 30% Mo, up to about 3% Si, up to about 6% W, about 2.5% to 12% Ti, about 10% to 22% Fe, up to about 0.4% V, and the balance essentially nickle.
Claim 14
Dependent Claim
55 words
The flame spray method of claim 9, wherein the alloy being sprayed consists essentially of about 0.02% to 0.035% C, about 18% to 22% Mo, about 1.6% to 1.8% Si, about 3% to 6% W, about 7% to 10% Ti, about 17% to 20% Fe, about 0.2% to 0.4% V, and the balance essentially nickel.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |