Method of adhering wallcovering using aqueous adhesive compositions
Assignee: Ciba Specialty Chemicals Water Treatments Ltd
•
Filing: 1981-05-27
•
Granted: 1982-11-30
•
Expires: 2001-05-27
Abstract
Abstract A liquid polymeric composition comprises a suspension in an organic liquid of particulate water insoluble but water swellable polymer, the particles being less than 10 microns in size. To reduce viscosity in water the swellable polymer may be a copolymer and/or a water soluble polymer may be included. A composition of polymer particles that are swellable and contain both soluble and insoluble polymer can be made by inverse emulsion polymerization. An aqueous adhesive, that may be made by mixing this composition with water, comprises water swollen particulate polymer that may be a copolymer and that may be used with a dissolved polymer in order to reduce the viscosity. Pregummed substrates, such as wallpaper, that can be rendered adhesive by contacting with water are obtained by applying the aqueous or non-aqueous composition to the substrate and drying it on the substrate. Wallcovering can be stuck to a surface using the aqueous adhesive.
Inventors
- 👤 John B. Clarke
- 👤 Peter Flesher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 01:24
CPC Classifications
C; C09; C09J; C09J157/00; C09J133/00; C09J133/24; C09J133/26; C09J7/00; C09J7/20; C09J7/21; C09J7/30; C09J7/32; Y; Y10; Y10T; Y10T428/00; Y10T428/28; Y10T428/2813; Y10T428/283; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T428/31895
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
117 words
In a method in which an aqueous adhesive composition and a wallcovering are applied to a surface and the wallcovering is thereby bonded to the surface, the improvement in which the aqueous adhesive composition consists essentially of, as its adhesive component, synthetic polymeric material present in an amount of from 1 to 10% consisting substantially only of water swollen, water insoluble particles of cross-linked synthetic polymer having a dry particle size of less than 10 microns and which remain as separate discrete particles, during use of said aqueous adhesive composition the polymeric material being such that a 3% dispersion of it in deionised water has a Brookfield viscosity at 20 rpm of at least about 10,000 cps.
Claim 2
Dependent Claim
117 words
In a method in which an aqueous adhesive composition and a wallcovering are applied to a surface and the wallcovering is thereby bonded to the surface, the improvement in which the aqueous adhesive composition consists essentially of, as its adhesive component, synthetic polymeric material present in an amount of from 1 to 10% consisting substantially only of water swollen, water insoluble particles of cross-linked synthetic polymer having a dry particle size of less than 10 microns and which remain as separate discrete particles, during use of said aqueous adhesive composition the polymeric material being such that a 3% dispersion of it in deionised water has a Brookfield viscosity at 20 rpm of at least about 10,000 cps.
Claim 3
Dependent Claim
120 words
In a method in which an aqueous adhesive composition and a wallcovering are applied to a surface and the wallcovering is thereby bonded to the surface, the improvement in which the aqueous adhesive composition consists essentially of, as its adhesive component, synthetic polymeric material present in an amount of from 1 to 10% consisting substantially only of water swollen, water insoluble particles of cross-linked synthetic polymer having a dry particle size of less than 10 microns and which remain as separate discrete particles, during use of said aqueous adhesive composition the polymeric material being such that a 3% dispersion of it in deionised water has a Brookfield viscosity at 20 rpm of from about 10,000 cps to about 80,000 cps.
Claim 4
Dependent Claim
120 words
In a method in which an aqueous adhesive composition and a wallcovering are applied to a surface and the wallcovering is thereby bonded to the surface, the improvement in which the aqueous adhesive composition consists essentially of, as its adhesive component, synthetic polymeric material present in an amount of from 1 to 10% consisting substantially only of water swollen, water insoluble particles of cross-linked synthetic polymer having a dry particle size of less than 10 microns and which remain as separate discrete particles, during use of said aqueous adhesive composition the polymeric material being such that a 3% dispersion of it in deionised water has a Brookfield viscosity at 20 rpm of from about 10,000 cps to about 80,000 cps.
Claim 5
Dependent Claim
29 words
A method according to claim 1 or claim 2 in which the swollen polymer is a copolymer of a cationic or anionic monomer with at least one other monomer.
Claim 6
Dependent Claim
27 words
A method according to claim 3 in which the swollen polymer is a copolymer of acrylamide or methacrylamide with an anionic monomer or with a cationic monomer.
Claim 7
Dependent Claim
21 words
A method according to claim 3 in which the swollen polymer is a copolymer of acrylamide or methacrylamide with sodium acrylate.
Claim 8
Dependent Claim
37 words
A method according to claim 3 in which the swollen polymer is a copolymer of acrylamide or methacrylamide with a cationic monomer that comprises aminoalkylated derivatives of acrylamide, methacrylamide, acrylate or methacrylate or a quaternised derivative thereof.
Claim 9
Dependent Claim
38 words
A method according to claim 1 or claim 2 in which the polymeric material consists substantially only of a cross-linked copolymer of 50 to 90 parts by weight acrylamide and 10 to 50 parts by weight sodium acrylate.
Claim 10
Dependent Claim
30 words
A method according to claim 1 in which a 3% dispersion of the polymeric material in deionised water has a Brookfield viscosity at 20 rpm of 20,000 to 50,000 cps.
Claim 11
Dependent Claim
36 words
A method according to claim 1 in which the aqueous composition has a Brookfield viscosity at 20 rpm of 20,000 to 50,000 cps and has a concentration of polymeric material of 2.2 to 10% by weight.
Claim 12
Dependent Claim
61 words
A method according to claim 1 or claim 2 in which the polymeric material includes also 1 to 19% by weight of a dissolved synthetic polymer that is ionic and in which the dissolved polymer has the same charge as the swollen polymer or is non-ionic or the swollen polymer is non-ionic and the dissolved polymer is anionic, cationic or non-ionic.
Claim 13
Dependent Claim
24 words
A method according to claim 10 in which the swollen and dissolved polymers are formed of the same recurring unit or mixture of units.
References Cited (Backward Citations)
US3218302A
Cited
GB1082969A
Cited
US3758641A
Cited
US3780006A
Cited
GB1383367A
Cited
GB1453951A
Cited
JPS52837A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-29 | 1986-05-31 | 1986-11-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-29 | 1990-05-31 | 1990-11-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-29 | 1994-05-31 | 1994-11-30 | $7700.00 | Window Closed / Lapsed |