Smoke and fire retardants for halogen-containing plastic compositions
Assignee: GLCC Technologies Inc
•
Filing: 1981-02-13
•
Granted: 1982-11-23
•
Expires: 2001-02-13
Abstract
Abstract A solid solution of zinc oxide and magnesium oxide and/or calcium oxide when added to a halogen-containing plastic composition serves as a smoke and/or fire retardant agent. This solid solution agent may be added to the plastic composition, preferably with an antimony compound.
Inventors
- 👤 Joseph M. G. Huang
- 👤 Robert J. Capwell
- 👤 Michael A. De Sesa
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 10:34
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C09; C09K; C09K21/00; C09K21/02
Claims Analysis
Total Claims: 30
Claim 1
Independent Claim
91 words
A flame and smoke resistant halogen-containing plastic composition, said composition containing therein from 0.5% to 10% of a solid solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 2
Dependent Claim
91 words
A flame and smoke resistant halogen-containing plastic composition, said composition containing therein from 0.5% to 10% of a solid solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 3
Dependent Claim
19 words
Composition according to claim 1 in which the composition contains a solid solution of zinc oxide and magnesium oxide.
Claim 4
Dependent Claim
19 words
Composition according to claim 1 in which the composition contains a solid solution of zinc oxide and calcium oxide.
Claim 5
Dependent Claim
21 words
Composition according to claim 1 in which the composition contains a solid solution of zinc oxide, magnesium oxide and calcium oxide.
Claim 6
Dependent Claim
87 words
Method of preparing a flame and smoke resistant halogen-containing plastic composition which comprises incorporating in said plastic composition from 0.5% to 10% of a solid solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 7
Dependent Claim
87 words
Method of preparing a flame and smoke resistant halogen-containing plastic composition which comprises incorporating in said plastic composition from 0.5% to 10% of a solid solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 8
Dependent Claim
17 words
Method according to claim 5 in which said solid solution employed contains zinc oxide and magnesium oxide.
Claim 9
Dependent Claim
17 words
Method according to claim 5 in which said solid solution employed contains zinc oxide and calcium oxide.
Claim 10
Dependent Claim
19 words
Method according to claim 5 in which said solid solution employed contains zinc oxide, magnesium oxide and calcium oxide.
Claim 11
Dependent Claim
111 words
A flame and smoke resistant agent for plastic compositions, said agent comprising a mixture of antimony trioxide and a solid solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, in which there are from 0.1 to 10 parts of antimony trioxide for each part of the solid solution present in said mixture, the parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 12
Dependent Claim
111 words
A flame and smoke resistant agent for plastic compositions, said agent comprising a mixture of antimony trioxide and a solid solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, in which there are from 0.1 to 10 parts of antimony trioxide for each part of the solid solution present in said mixture, the parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 13
Dependent Claim
25 words
The flame and smoke resistant agent of claim 9 wherein the solid solution has a specific surface area greater than about 16 M 2 /g.
Claim 14
Dependent Claim
72 words
A flame and smoke retardant composition comprising a solid solution of zinc oxide and at least one other oxide selected from the group consisting of calcium oxide, magnesium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, said solid solution having a specific surface area greater than about 10 M 2 /g.
Claim 15
Dependent Claim
72 words
A flame and smoke retardant composition comprising a solid solution of zinc oxide and at least one other oxide selected from the group consisting of calcium oxide, magnesium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being from 0.1 to 10 parts for each part of zinc oxide, said solid solution having a specific surface area greater than about 10 M 2 /g.
Claim 16
Dependent Claim
16 words
The composition of claim 11 wherein the solid solution consists of zinc oxide and calcium oxide.
Claim 17
Dependent Claim
32 words
The composition of claim 12 containing from about 50 weight percent zinc oxide and 50 weight percent calcium oxide to about 85 weight percent zinc oxide and 15 weight percent calcium oxide.
Claim 18
Dependent Claim
16 words
The composition of claim 11 wherein the solid solution consists of zinc oxide and magnesium oxide.
Claim 19
Dependent Claim
32 words
The composition of claim 14 containing from about 30 weight percent zinc oxide and 70 weight percent magnesium oxide to about 50 weight percent zinc oxide and 50 weight percent magnesium oxide.
Claim 20
Dependent Claim
18 words
The composition of claim 11 wherein the solid solution consists of zinc oxide, magnesium oxide and calcium oxide.
Claim 21
Dependent Claim
27 words
The composition of claim 16 containing from about 10 weight percent to 60 weight percent zinc oxide and 5 weight percent to 50 weight percent calcium oxide.
Claim 22
Independent Claim
110 words
A method of preparing a flame and smoke resistant halogen-containing plastic composition which comprises incorporating in said plastic composition from 0.25% to 10% of a solild solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being effective to provide the zinc oxide with sufficient heat stability to permit processing of the plastic composition at temperatures up to about 200° C., all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of above about 10 M 2 /g.
Claim 23
Independent Claim
110 words
A method of preparing a flame and smoke resistant halogen-containing plastic composition which comprises incorporating in said plastic composition from 0.25% to 10% of a solild solution of zinc oxide and an oxide selected from the group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being effective to provide the zinc oxide with sufficient heat stability to permit processing of the plastic composition at temperatures up to about 200° C., all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of above about 10 M 2 /g.
Claim 24
Independent Claim
101 words
A method of producing a flame and smoke retardant for use in halogen containing plastic compositions comprising calcining zinc oxide and another oxide selected from the group consisting of magnesium oxide, calcium oxide, and mixtures thereof at a temperature and for a time effective to produce a solid solution having flame and smoke retardant properties, said another oxide being present in an amount of about 0.1 to 10 parts by weight for each part of zinc oxide, wherein said temperature and time are sufficient to produce a solid solution having a specific surface area of above about 10 M 2 /g.
Claim 25
Independent Claim
101 words
A method of producing a flame and smoke retardant for use in halogen containing plastic compositions comprising calcining zinc oxide and another oxide selected from the group consisting of magnesium oxide, calcium oxide, and mixtures thereof at a temperature and for a time effective to produce a solid solution having flame and smoke retardant properties, said another oxide being present in an amount of about 0.1 to 10 parts by weight for each part of zinc oxide, wherein said temperature and time are sufficient to produce a solid solution having a specific surface area of above about 10 M 2 /g.
Claim 26
Dependent Claim
13 words
The method of claim 19 wherein the temperature is above about 500° C.
Claim 27
Dependent Claim
17 words
The method of claim 19 wherein the temperature is from about 500° C. to about 1000° C.
Claim 28
Dependent Claim
122 words
A flame and smoke resistant halogen-containing plastic composition, said composition containing therein from 0.25% to 10% of a solid solution of zinc oxide and an oxide selected from group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being effective to provide the zinc oxide with sufficient heat stability to permit processing of the plastic composition at temperatures up to about 200° C., said amount being from 0.1 to 10 parts magnesium oxide and calcium oxide for each part of zinc oxide, all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 29
Dependent Claim
122 words
A flame and smoke resistant halogen-containing plastic composition, said composition containing therein from 0.25% to 10% of a solid solution of zinc oxide and an oxide selected from group consisting of magnesium oxide, calcium oxide and mixtures thereof, the amount of magnesium oxide and calcium oxide present in said solid solution being effective to provide the zinc oxide with sufficient heat stability to permit processing of the plastic composition at temperatures up to about 200° C., said amount being from 0.1 to 10 parts magnesium oxide and calcium oxide for each part of zinc oxide, all of the percentages and parts expressed on a weight basis, said solid solution having a specific surface area of greater than about 10 M 2 /g.
Claim 30
Dependent Claim
24 words
The composition of claim 1, 11 or 22 wherein the solid solution has a specific surface area greater than about 16 M 2 /g.
References Cited (Backward Citations)
US2028980A
Cited
US2286744A
Cited
US3560441A
Cited
US3723139A
Cited
US3869420A
Cited
US3945974A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-22 | 1986-05-24 | 1986-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-22 | 1990-05-24 | 1990-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-22 | 1994-05-24 | 1994-11-23 | $7700.00 | Window Closed / Lapsed |