Aluminum electrical contacts and method of making same
Assignee: Rio Tinto France SAS
•
Filing: 1980-08-19
•
Granted: 1982-11-23
•
Expires: 2000-08-19
Abstract
Abstract The invention relates to elements of aluminium, such as bars, sections or apparatus components for forming electrical contacts capable of withstanding mechanical and thermal stressing. The method by which these elements are produced consists in depositing a firmly adhering layer of nickel to the aluminium substrate at least in the contact zone. The quality of the contact is further improved when the nickel-plated element is in contact with a silver-plated element. The elements according to the invention may be used for the production of pin-type contacts and any other devices for making or breaking electrical circuits, such as isolators, circuit breakers, and contactors.
Inventors
- 👤 Michel Ladet
- 👤 Jacques Lefevre
- 👤 Jos Patrie
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 19:28
CPC Classifications
H; H01; H01H; H01H1/00; H01H1/02; H01H1/021; Y; Y10; Y10S; Y10S205/00; Y10S205/917
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
90 words
A method of producing electrical contacts comprising electrolytically coating conductive elements of aluminum with nickel and wherein an initial thin layer of nickel is deposited by chemical displacement in an acidic aqueous bath comprising: HF: 5 to 50 g/l H 3 BO 3 : 10 to 60 g/l NiCl 2 .6H 2 O: 50 to 500 g/l and then said initial layer of nickel is dissolved in an acid solution to produce an oxide-free surface before the definitive layer of nickel is electrolytically deposited directly onto the aluminum conductive elements.
Claim 2
Independent Claim
90 words
A method of producing electrical contacts comprising electrolytically coating conductive elements of aluminum with nickel and wherein an initial thin layer of nickel is deposited by chemical displacement in an acidic aqueous bath comprising: HF: 5 to 50 g/l H 3 BO 3 : 10 to 60 g/l NiCl 2 .6H 2 O: 50 to 500 g/l and then said initial layer of nickel is dissolved in an acid solution to produce an oxide-free surface before the definitive layer of nickel is electrolytically deposited directly onto the aluminum conductive elements.
Claim 3
Dependent Claim
21 words
A method as claimed in claim 1 wherein the elements to be coated are pickled before the initial deposit is applied.
Claim 4
Dependent Claim
28 words
A method as claimed in claim 1 wherein the definitive protective layer is formed by electrolytic deposition from a bath containing nickel sulphamate, boric acid and nickel chloride.
Claim 5
Independent Claim
148 words
A method for the production of a nickel plated aluminum substrate electrical contact member by electrodeposition of a nickel electrical contact layer directly on a surface of an aluminum substrate by the sequential manipulative steps of: (a) preparing the surface of the aluminum substrate by; (i) depositing a thin layer of nickel on the surface of the substrate by chemical displacement in an acidic aqueous solution comprising. HF: 5 to 50 g/l H 3 BO 3 : 10 to 60 g/l NiCl 2 .6H 2 O: 50 to 500 g/l (ii) removing the thin layer of nickel by dissolution wherein the surface of the substrate contiguous with the removed nickel is physically modified and oxide-free; and (b) electrodepositioning a nickel electrical contact layer on the prepared surface of the aluminum substrate whereby resistance to mechanical and or thermal stressing of the nickel contact layer-aluminum substrate bond is increased.
Claim 6
Independent Claim
148 words
A method for the production of a nickel plated aluminum substrate electrical contact member by electrodeposition of a nickel electrical contact layer directly on a surface of an aluminum substrate by the sequential manipulative steps of: (a) preparing the surface of the aluminum substrate by; (i) depositing a thin layer of nickel on the surface of the substrate by chemical displacement in an acidic aqueous solution comprising. HF: 5 to 50 g/l H 3 BO 3 : 10 to 60 g/l NiCl 2 .6H 2 O: 50 to 500 g/l (ii) removing the thin layer of nickel by dissolution wherein the surface of the substrate contiguous with the removed nickel is physically modified and oxide-free; and (b) electrodepositioning a nickel electrical contact layer on the prepared surface of the aluminum substrate whereby resistance to mechanical and or thermal stressing of the nickel contact layer-aluminum substrate bond is increased.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-22 | 1986-05-24 | 1986-11-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-22 | 1990-05-24 | 1990-11-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-22 | 1994-05-24 | 1994-11-23 | $7700.00 | Window Closed / Lapsed |