US4359504A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Dual-layer coating containing aluminum-flake pigment and coated article
Assignee: EIDP Inc
•
Filing: 1979-09-28
•
Granted: 1982-11-16
•
Expires: 1999-09-28
Abstract
Abstract A high-solids enamel coating on a substrate can give metallic glamor comparable to that imparted by conventional lacquer coatings containing metallic-flakes when the amount of metallic flake pigment in the enamel is increased over conventional amounts with a proportional increase in the amount of chromatic pigments.
Inventors
- 👤 Daniel J. Troy
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 03:56
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/53; B05D7/536; B05D5/00; B05D5/06; B05D5/067; B05D5/068; C; C09; C09D; C09D133/00; C09D133/04; C09D133/06; C09D5/00; C09D5/38; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31688; Y10T428/31692; Y10T428/31699; Y10T428/31786; Y10T428/31794; Y10T428/31797; Y10T428/31855; Y10T428/31859; Y10T428/31862; Y10T428/31909; Y10T428/31928
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
241 words
A substrate coated with an improved dual-layer high-solids enamel coating of the kind wherein the coating comprises (A) a cured base layer produced from a composition having (1) binder constituents consisting essentially of a first film-forming material and a crosslinker for the film-forming material wherein the film-forming material is selected from the group consisting of acrylic resins, polyester resins, and alkyd resins having a weight-average molecular weight of 500-10,000; (2) an organic solvent for the binder constituents in an amount of no more than 100% by weight of the binder; and (3) chromatic and metallic-flake pigments; and (B) a cured transparent top layer, deposited on said base layer, produced from a composition having (1) binder constituents consisting essentially of a second film-forming material and crosslinker for the film-forming material wherein the film-forming material is selected from the group consisting of acrylic resins, alkyd resins, and polyester resins having a weight-average molecular weight of 500-10,000; and (2) an organic solvent for the binder constituents in an amount of no more than 100% by weight of the binder, wherein the improvement is characterized in that the metallic-flake pigment is present in the base layer in an amount of 10-24% by weight, based on the weight of the binder constituents of the base layer, and the chromatic pigment is present in an amount sufficient with the amount of the metallic-flake pigment to give the dual-layer coating a flake orientation index of at least 40.
Claim 2
Dependent Claim
241 words
A substrate coated with an improved dual-layer high-solids enamel coating of the kind wherein the coating comprises (A) a cured base layer produced from a composition having (1) binder constituents consisting essentially of a first film-forming material and a crosslinker for the film-forming material wherein the film-forming material is selected from the group consisting of acrylic resins, polyester resins, and alkyd resins having a weight-average molecular weight of 500-10,000; (2) an organic solvent for the binder constituents in an amount of no more than 100% by weight of the binder; and (3) chromatic and metallic-flake pigments; and (B) a cured transparent top layer, deposited on said base layer, produced from a composition having (1) binder constituents consisting essentially of a second film-forming material and crosslinker for the film-forming material wherein the film-forming material is selected from the group consisting of acrylic resins, alkyd resins, and polyester resins having a weight-average molecular weight of 500-10,000; and (2) an organic solvent for the binder constituents in an amount of no more than 100% by weight of the binder, wherein the improvement is characterized in that the metallic-flake pigment is present in the base layer in an amount of 10-24% by weight, based on the weight of the binder constituents of the base layer, and the chromatic pigment is present in an amount sufficient with the amount of the metallic-flake pigment to give the dual-layer coating a flake orientation index of at least 40.
Claim 3
Dependent Claim
23 words
The substrate of claim 1 wherein at least one of the first film-forming material and the second film-forming material is a polyester resin.
Claim 4
Dependent Claim
52 words
The substrate of claim 2 wherein the first and second film-forming materials are polyester resins that are a mixture of the condensation products of (1) aliphatic diols and aliphatic dibasic acids, and (2) aliphatic diols and aromatic dibasic acids, and wherein the crosslinker for each of the film-forming materials is an aminoplast.
Claim 5
Dependent Claim
34 words
The substrate of claims 1, 2 or 3 wherein the amount of metallic-flake pigment in the base layer is 10-20% by weight, based on the weight of the binder constituents of the base layer.
Claim 6
Dependent Claim
25 words
The substrate of claim 4 wherein at least one, of the base layer and the top layer, contains an ultraviolet light stabilizer and an antioxidant.
Claim 7
Dependent Claim
23 words
The substrate of claim 1 wherein at least one of the first film-forming material and the second film-forming material is an acrylic resin.
Claim 8
Dependent Claim
46 words
The substrate of claim 6 wherein the first and second film-forming materials are copolymers of an alkyl acrylate, alkyl methacrylate, and at least one of a hydroxy alkyl acrylate and hydroxy alkyl methacrylate, and wherein the crosslinker for each of the film-forming materials is an aminoplast.
Claim 9
Dependent Claim
33 words
The substrate of claim 6 or 7 wherein the amount of metallic-flake pigment in the base layer is 10-20% by weight, based on the weight of the binder constituents of the base layer.
Claim 10
Dependent Claim
24 words
The substrate of claim 8 wherein at least one, of the base layer and top layer, contains an ultraviolet light stabilizer and an antioxidant.
Claim 11
Dependent Claim
24 words
The substrate of claim 1 in which at least one, of the first film-forming material and the second film-forming material, is an alkyd resin.
Claim 12
Dependent Claim
33 words
The substrate of claim 10 wherein the first and second film-forming materials are alkyd resins that are the reaction product of a glyceride of a fatty acid, a diol, and a dicarboxylic acid.
Claim 13
Dependent Claim
33 words
The substrate of claim 10 or 11 wherein the amount of metallic-flake pigment in the base layer is 10-20% by weight, based on the weight of the binder constituents of the base layer.
Claim 14
Dependent Claim
24 words
The substrate of claim 12 wherein at least one, of the base layer and top layer, contains an ultraviolet light stabilizer and an antioxidant.
References Cited (Backward Citations)
US2662027A
Cited
US3708318A
Cited
US3953644A
Cited
US4139672A
Cited
US4220679A
Cited
US4280465A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-15 | 1986-05-17 | 1986-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-15 | 1990-05-17 | 1990-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-15 | 1994-05-17 | 1994-11-16 | $7700.00 | Window Closed / Lapsed |