Process for granulating molten material
Assignee: VENSKT STAL AB
•
Filing: 1978-09-05
•
Granted: 1982-11-16
•
Expires: 1998-09-05
Abstract
Abstract A process for granulating slag melts, glass melts, ceramic melts, metal melts and melts of metal alloys, particularly blast furnace slag melts, the melt being shaped into at least one thin, liquid melt stream moving freely in a predetermined direction and which, by meeting at a predetermined incidence angle with a stream of fine-grained, solid particles and/or gas, particularly inert gas, flowing substantially freely in a substantially uniform direction at a high rate of flow in relation to the melt stream or melt streams, being converted at least partly into a substantially fine-grained granulate having a fan-shaped distribution over at least part of the opposite angle to the incidence angle.
Inventors
- 👤 Nils Tiberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 07:22
CPC Classifications
B; B22; B22F; B22F9/00; B22F9/02; B22F9/06; B22F9/08; B22F9/082; C; C03; C03B; C03B19/00; C03B19/10; C03B19/1005; C03B19/102; C21; C21B; C21B3/00; C21B3/04; C21B3/06; B22F2999/00; C21B2400/00; C21B2400/02; C21B2400/022; C21B2400/028; C21B2400/05; C21B2400/062; Y; Y02; Y02W; Y02W30/00; Y02W30/50; Y10; Y10S; Y10S264/00; Y10S264/51
Claims Analysis
Total Claims: 38
Claim 1
Independent Claim
141 words
A process for granulating slag melts, glass melts, ceramic melts and melts of metal alloys, comprising the steps of: (A) creating a flowing stream of molten material; (B) widening said stream of molten material to form a melt film as it flows; (C) creating a substantially freely flowing stream of fine-grained, said particles; (D) imparting a rate of flow to the stream of solid particles that is greater than that of the melt film and directing the stream of solid particles in a substantially uniform direction against a widened side of said stream of molten material at an incidence angle which will atomize said stream of molten material into a fan-shaped distribution of droplets over at least part of an opposite angle to the incidence angle; (E) cooling said droplets into a substantially fine-grained granulate; and (F) collecting the fine-grained granulate.
Claim 2
Dependent Claim
141 words
A process for granulating slag melts, glass melts, ceramic melts and melts of metal alloys, comprising the steps of: (A) creating a flowing stream of molten material; (B) widening said stream of molten material to form a melt film as it flows; (C) creating a substantially freely flowing stream of fine-grained, said particles; (D) imparting a rate of flow to the stream of solid particles that is greater than that of the melt film and directing the stream of solid particles in a substantially uniform direction against a widened side of said stream of molten material at an incidence angle which will atomize said stream of molten material into a fan-shaped distribution of droplets over at least part of an opposite angle to the incidence angle; (E) cooling said droplets into a substantially fine-grained granulate; and (F) collecting the fine-grained granulate.
Claim 3
Dependent Claim
18 words
The process of claim 1, wherein step (F) is performed at least partly by a air fluidized bed.
Claim 4
Dependent Claim
43 words
The process of claim 1 or 2, wherein step (F) includes the step of dividing the granulate into fractions in dependence upon the distance between a point of collection and a point at which the stream of solid particles intersects the melt film.
Claim 5
Dependent Claim
15 words
The process of claim 3, wherein the incidence angle is between about 5° and 90°.
Claim 6
Dependent Claim
15 words
The process of claim 4, wherein the incidence angle is between about 50° and 90°.
Claim 7
Dependent Claim
23 words
The process of claim 1 or 2, wherein the melt film formed in step (B) has a thickness of less than 10 mm.
Claim 8
Dependent Claim
26 words
The process of claim 1 or 2, wherein the speed imparted to the stream of solid particles in step (D) is from 5 to 100 m/sec.
Claim 9
Dependent Claim
24 words
The process of claim 6, wherein the speed imparted to the stream of solid particles in step (D) is from 5 to 100 m/sec.
Claim 10
Dependent Claim
14 words
The process of claim 4, wherein said incidence angle is between 20° and 90°.
Claim 11
Dependent Claim
11 words
The process of claim 5, wherein said incidence angle is 60°.
Claim 12
Dependent Claim
18 words
The process of claim 6, wherein the melt film is formed with a thickness less than 3 mm.
Claim 13
Dependent Claim
18 words
The process of claim 6, wherein said melt film is formed with a thickness less than 1 mm.
Claim 14
Dependent Claim
24 words
The process of claim 3, wherein the speed imparted to the stream of solid particles in step (D) is from 5 to 100 m/sec.
Claim 15
Dependent Claim
24 words
The process of claim 5, wherein the speed imparted to the stream of solid particles in step (D) is from 5 to 100 m/sec.
Claim 16
Dependent Claim
15 words
The process of claim 4, wherein said incidence angle is between about 20° and 40°.
Claim 17
Dependent Claim
25 words
The process of claim 15, wherein the speed imparted to the stream of solid particles in step (D) is from about 5 to 50 m/sec.
Claim 18
Dependent Claim
42 words
The process of claim 1, wherein the quantity by weight of solid particles delivered per unit of time and the weight of the melt delivered per unit of time are in a ratio to one another of from about 2:1 to 1:1.
Claim 19
Dependent Claim
36 words
The process of claim 1 or 2, wherein the stream of solid fine-grained particles is formed of particles that are not all the same with respect to at least one of their particle size and composition.
Claim 20
Dependent Claim
34 words
The process of claim 17, wherein the stream of solid fine-grained particles is formed of particles that are not all the same with respect to at least one of their particle size and composition.
Claim 21
Dependent Claim
28 words
The process of claim 1, wherein the molten material consists essentially of steel slag and said stream of solid particles is comprised at least in part of limestone.
Claim 22
Dependent Claim
25 words
The process of claim 17, wherein during step (F) at least one fraction of the granulate is collected by means of a air fluidized bed.
Claim 23
Dependent Claim
22 words
The process of claim 1, wherein the speed imparted to the stream of solid particles is from about 10 to 20 m/sec.
Claim 24
Dependent Claim
14 words
The process of claim 18, wherein said solid particles comprise two or more materials.
Claim 25
Dependent Claim
15 words
The process of claim 18, wherein said solid particles comprise two or more grain fractions.
Claim 26
Dependent Claim
15 words
The process of claim 23, wherein said solid particles comprise two or more grain fractions.
Claim 27
Dependent Claim
13 words
The process of claim 18, wherein said solid particles comprise different grain forms.
Claim 28
Dependent Claim
13 words
The process of claim 25, wherein said solid particles comprise different grain forms.
Claim 29
Dependent Claim
32 words
The process of claim 1 or 20, wherein said molten material consists essentially of steel slag and the stream of fine-grained solid particles is comprised at least in part of quick lime.
Claim 30
Dependent Claim
39 words
The process of claim 1 or 2, wherein step (B) is performed by impinging the melt upon a baffle plate so as to cause the melt to spread out into the melt film immediately upon leaving the baffle plate.
Claim 31
Dependent Claim
36 words
The process of claim 29, wherein step (D) is performed before the melt flow, upon leaving said baffle plate, can shrink into a substantially circular cross-section under the effect of surface tension of the molten material.
Claim 32
Dependent Claim
34 words
The process of claim 1, wherein the molten material is a blast furnace slag and the stream of solid particles is formed of sand particles having a grain size of up to 2 mm.
Claim 33
Dependent Claim
34 words
The process of claim 1, wherein the molten material is a blast furnace slag and the stream of solid particles is formed of sand particles having a grain size of up to 1 mm.
Claim 34
Dependent Claim
50 words
The process of claim 1 or 19, wherein the stream of solid fine-grained particles comprises at least one material which is added to and mixed with the molten material during step (D) in a fixed mixing ratio between the proportion of molten material and the proportion of fine-grained solid particles.
Claim 35
Dependent Claim
23 words
The process of claim 33, wherein said fine-grained particles are comprised of powdered granite for use in producing mineral wool from said granulate.
Claim 36
Dependent Claim
23 words
The process of claim 33, wherein said fine-grained particles are comprised of a phosphate mixture for use in producing fertilizer from said granulate.
Claim 37
Dependent Claim
31 words
The process of claim 2 or 21, comprising the step of extracting heat from the granulate and free fine-grained solid particles which are not bound to the granulate during step (F).
Claim 38
Dependent Claim
23 words
The process of claim 36, wherein the heat extracted during the heat extracting step is transferred to the air of the fluidized bed.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-15 | 1986-05-17 | 1986-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-15 | 1990-05-17 | 1990-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-15 | 1994-05-17 | 1994-11-16 | $7700.00 | Window Closed / Lapsed |