US4359372A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for making a carbide thin film thermistor
Assignee: Panasonic Holdings Corp
•
Filing: 1980-10-10
•
Granted: 1982-11-16
•
Expires: 2000-10-10
Abstract
Abstract A method for making a carbide thin film thermistor which comprises providing an insulating substrate, forming at least one pair of electroconductive electrodes on the substrate in a desired pattern, and forming a carbide resistor film on the insulating substrate and the electroconductive electrodes by sputtering process while leaving part of the electrodes exposed for external connections. A carbide target material is sputtered in an inert gas atmosphere containing a small amount of an impurity gas. The thermistor element is arbitrarily controlled to have a desired level of resistance by choice of the impurity gas, the amount of such gas and the mode of sputtering. Optionally, the element is trimmed to adjust its resistance accurately and is also hermetically sealed within a glass tube to prevent the element from being contaminated with harmful substances.
Inventors
- 👤 Takeshi Nagai
- 👤 Kazushi Yamamoto
- 👤 Ikuo Kobayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 16:04
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/04; H01C7/041; H10; H10W; H10W72/00; H10W72/01; H10W72/015; H10W72/01515; H10W72/071; H10W72/075; H10W72/50; H10W72/531; H10W72/5363; H10W72/551; H10W72/552; H10W72/5522; H10W90/00; H10W90/701; H10W90/751; H10W90/756; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49082; Y10T29/49085; Y10T29/49087; Y10T29/49099; Y10T29/49101
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
120 words
A method for making a carbide thin film thermistor comprising: providing an insulating substrate; forming at least one pair of electroconductive electrodes on said insulating substrate in a desired pattern, the electrodes being electrically insulated from each other; and forming a resistive carbide film on said insulating substrate and said at least one pair of electroconductive electrodes, while leaving part of the electrodes exposed for external connections, by a sputtering technique in which a carbide target material selected from the group consisting of SiC and B 4 C is sputtered in an inert gas atmosphere containing an impurity gas selected from the group consisting of O 2 , N 2 , CO, CO 2 , air and a mixture thereof.
Claim 2
Independent Claim
120 words
A method for making a carbide thin film thermistor comprising: providing an insulating substrate; forming at least one pair of electroconductive electrodes on said insulating substrate in a desired pattern, the electrodes being electrically insulated from each other; and forming a resistive carbide film on said insulating substrate and said at least one pair of electroconductive electrodes, while leaving part of the electrodes exposed for external connections, by a sputtering technique in which a carbide target material selected from the group consisting of SiC and B 4 C is sputtered in an inert gas atmosphere containing an impurity gas selected from the group consisting of O 2 , N 2 , CO, CO 2 , air and a mixture thereof.
Claim 3
Dependent Claim
13 words
A method according to claim 1, wherein said carbide target material is SiC.
Claim 4
Dependent Claim
15 words
A method according to claim 1, wherein said carbide target material is B 4 C.
Claim 5
Dependent Claim
30 words
A method according to claim 1, wherein said impurity gas is N 2 gas and is used in an amount of below 2.5 vol% based on the total gas composition.
Claim 6
Dependent Claim
31 words
A method according to claim 1, wherein said impurity gas is CO or CO 2 and is used in an amount of below 1.5 vol% based on the total gas composition.
Claim 7
Dependent Claim
29 words
A method according to claim 1, wherein said impurity gas is O 2 and is used in an amount of below 0.6 vol% based on the total gas composition.
Claim 8
Dependent Claim
28 words
A method according to claim 1, wherein said impurity gas is air and is used in an amount of below 2.0 vol% based on the total gas composition.
Claim 9
Dependent Claim
51 words
A method according to claim 1, wherein said impurity gas is a mixed gas composed of 78.5 vol% of N 2 gas, 21.45 vol% of O 2 gas and 0.05 vol% of CO 2 gas and is used in an amount of below 2 vol% based on the total gas composition.
Claim 10
Dependent Claim
70 words
A method according to claim 1, wherein said carbide target material is SiC and said impurity gas which reacts with said target material on the sputtering is used in such an amount that the specific resistance of the resistor film is below 10 5 Ω-cm and said impurity gas is selected from the group consisting of N 2 , CO, CO 2 , O 2 air and a mixture thereof.
Claim 11
Dependent Claim
31 words
A method according to claim 9, wherein said impurity gas is N 2 and is used in an amount of 2.5 vol% to 10.0 vol% based on the total gas composition.
Claim 12
Dependent Claim
31 words
A method according to claim 9, wherein said impurity gas is CO gas and is used in an amount of 1.5 vol% to 7.0 vol% based on the total gas composition.
Claim 13
Dependent Claim
32 words
A method according to claim 9, wherein said impurity gas is CO 2 gas and is used in an amount of 1.5 vol% to 5.0 vol% based on the total gas composition.
Claim 14
Dependent Claim
32 words
A method according to claim 9, wherein said impurity gas is O 2 gas and is used in an amount of 0.6 vol% to 7.0 vol% based on the total gas composition.
Claim 15
Dependent Claim
30 words
A method according to claim 9, wherein said impurity gas is air and is used in an amount of 2.0 vol% to 9.0 vol% based on the total gas composition.
Claim 16
Dependent Claim
53 words
A method according to claim 9, wherein said impurity gas is a mixed gas composed of 78.5 vol% of N 2 gas, 21.45 vol% of O 2 gas and 0.05 vol% of CO 2 gas and is used in an amount of 2.0 vol% to 9.0 vol% based on the total gas composition.
Claim 17
Dependent Claim
44 words
A method according to claim 1, further comprising removing said electrode film and/or said carbide film in a desired pattern by means of a diamond edge of a cylindrical or wedge form to adjust the resistance of said thermistor element to a desired level.
Claim 18
Dependent Claim
22 words
A method according to claim 16, wherein said diamond edge of cylindrical form has a diameter of 0.1-1.0 mm and is rotated.
Claim 19
Dependent Claim
32 words
A method according to claim 16, wherein said diamond edge of the wedge form has a terminal angle of 30°-150° and a length of 0.1-1 mm and is vibrated by ultrasonic frequency.
Claim 20
Dependent Claim
22 words
A method according to claim 1, further comprising connecting lead wires to said thermistor element at exposed portions of the electrodes, respectively.
Claim 21
Dependent Claim
43 words
A method according to claim 19, wherein said lead wires each consists of a fine metal wire and a Kovar alloy wire welded to each other at one end, and said metal wire is welded to the exposed portion at the other end.
Claim 22
Dependent Claim
19 words
A method according to claim 20, wherein said metal wire is a Pt wire of 0.1-0.2 mm in diameter.
Claim 23
Dependent Claim
33 words
A method according to claim 19, wherein the welded portion between each metal wire and each exposed portion of said electrode film is covered with a sintered mass of a low melting glass.
Claim 24
Dependent Claim
47 words
A method according to claim 19, further comprising placing the connected thermistor element in a glass tube so that the Kovar wires are each extending outwardly from the opening of said glass tube, and sealing up said thermistor element hermetically within said tube through said Kovar wires.
Claim 25
Dependent Claim
16 words
A method according to claim 23, wherein said glass tube is made of a borosilicate glass.
Claim 26
Dependent Claim
42 words
A method according to claim 24, wherein the thermal expansion coefficients of said Kovar wire and said glass tube are each in the range of from 50×10 -7 to 60×10 -7 /°C. in the temperature range of from 30° to 300° C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-15 | 1986-05-17 | 1986-11-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-15 | 1990-05-17 | 1990-11-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-15 | 1994-05-17 | 1994-11-16 | $7700.00 | Window Closed / Lapsed |