Agent for de-icing and protecting against icing-up
Assignee: Clariant Produkte Deutschland GmbH
•
Filing: 1981-03-18
•
Granted: 1982-11-09
•
Expires: 2001-03-18
Abstract
Abstract A liquid agent for de-icing and protecting against icing-up is described, by means of which it is possible, in particular, to free the metal surface of aircraft rapidly and completely from ice, hoar-frost, snow and the like, and to protect the surface against further build-up for a relatively long period. The agent is essentially composed of several components, namely of (a) glycols, (b) water, (c) thickeners, (d) substances insoluble in water, (e) surface-active agents, (f) corrosion inhibitors and (g) alkaline compounds, in very specific quantities in each case, the quantity of the components (a) and (b) being at least 94%, relative to the total weight of the agent. Its pH value is 7.5 to 10.
Inventors
- 👤 Inge Konig-Lumer
- 👤 Ulrich Schwenk
- 👤 Rene Salvador
- 👤 Josef Kapfinger
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:55
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/18; C09K3/185
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
240 words
Agent for de-icing and protecting against icing-up, consisting essentially of (a) 40 to 65% by weight of a glycol selected from the group consisting of alkylene glycols having 2 to 3 carbon atoms and oxalkylene glycols having 4 to 6 carbon atoms; (b) 35 to 60% by weight of water; (c) 0.05 to 1.5% by weight of a thickener comprising cross-linked polyacrylates having a viscosity of 1,000 to 50,000 mPa.s in a 0.5% strength by weight aqueous solution at 20° C. and a pH value of 7.5 to 10, and having a laminar flow behavior in a 0.1 to 1.5% strength by weight aqueous solution at +20° C., 0° C. and -10° C. and a pH value of 7.5 tp 10, at a shear rate of up to at least 20,000 seconds -1 ; (d) 0.05 to 1% by weight of a water-insoluble component comprising a mixed-base mineral oil comprising paraffin hydrocarbons and naphthenes; (e) 0.05 to 1% by weight of a surface-active agent comprising alkali metal alkylarylsulfonates; (f) 0.01 to 1% by weight of at least one corrosion inhibitor; and (g) a quantity of at least one alkaline compound selected from the group consisting of alkali metal carbonates, bicarbonates or hydroxides and amines, such that the agent has a pH value of 7.5 to 10, the quantity of the components (a) and (b) in the agent being at least 94% by weight, relative to the weight of the agent.
Claim 2
Dependent Claim
240 words
Agent for de-icing and protecting against icing-up, consisting essentially of (a) 40 to 65% by weight of a glycol selected from the group consisting of alkylene glycols having 2 to 3 carbon atoms and oxalkylene glycols having 4 to 6 carbon atoms; (b) 35 to 60% by weight of water; (c) 0.05 to 1.5% by weight of a thickener comprising cross-linked polyacrylates having a viscosity of 1,000 to 50,000 mPa.s in a 0.5% strength by weight aqueous solution at 20° C. and a pH value of 7.5 to 10, and having a laminar flow behavior in a 0.1 to 1.5% strength by weight aqueous solution at +20° C., 0° C. and -10° C. and a pH value of 7.5 tp 10, at a shear rate of up to at least 20,000 seconds -1 ; (d) 0.05 to 1% by weight of a water-insoluble component comprising a mixed-base mineral oil comprising paraffin hydrocarbons and naphthenes; (e) 0.05 to 1% by weight of a surface-active agent comprising alkali metal alkylarylsulfonates; (f) 0.01 to 1% by weight of at least one corrosion inhibitor; and (g) a quantity of at least one alkaline compound selected from the group consisting of alkali metal carbonates, bicarbonates or hydroxides and amines, such that the agent has a pH value of 7.5 to 10, the quantity of the components (a) and (b) in the agent being at least 94% by weight, relative to the weight of the agent.
Claim 3
Dependent Claim
89 words
Agent as claimed in claim 1, wherein the component (c) is a crosslinked polyacrylate which has a viscosity of 1,000 to 50,000 mPa.s in a 0.5% strength by weight aqueous solution at 20° C. and a pH value of 8 to 9.5, and which has a laminar flow behavior in a 0.1 to 1.5% strength by weight aqueous solution at +20° C., 0° C. and -10° C. and at a pH value of 8 to 9.5, at a shear rate of up to at least 20,000 seconds -1 .
Claim 4
Dependent Claim
184 words
Agent as claimed in claim 2, wherein the component (a) is a glycol selected from the group consisting of ethylene glycol, propylene glycol and diethylene glycol; the component (c) is a polyacrylate having a viscosity of 5,000 to 30,000 mPa.s, the component (d) is a mixed base mineral oil composed essentially of 60 to 70% by weight of paraffin hydrocarbons having 12 to 18 carbon atoms and of 30 to 40% by weight of naphthenes having 10 to 20 carbon atoms; the component (e) is an alkali metal alkylarylsulfonate selected from the group consisting of potassium alkylarylsulfonates and sodium alkylarylsulfonates having one or two sulfonate groups, one or two alkyl groups of 12 to 18 carbon atoms and one or two benzene rings; the component (f) is a corrosion inhibitor selected from the group consisting of potassium salts and sodium salts of carbonic acid, phosphorous acid, phosphoric acid, and silicic acid, mono-, di- and tri-ethanolamines, mono-, di- and tri- propanolamines and benztriazole; and the component (g) is potassium hydroxide, in a quantity such that the agent has a pH value of 8 to 9.5.
Claim 5
Dependent Claim
69 words
Agent as claimed in claim 3, wherein the component (c) is a polyacrylate having a viscosity of 10,000 to 20,000 mPa.s, the component (e) is an alkylbenzenesulfonate selected from the group consisting of potassium alkylbenzenesulfonates and sodium alkylbenzenesulfonates having 12 to 18 C atoms in the alkyl group; and the component (f) is a corrosion inhibitor selected from the group consisting of potassium silicate, sodium silicate, triethanolamine and benztriazole.
Claim 6
Dependent Claim
30 words
Agent as claimed in claim 1 or 3, wherein the component (c) is a polyacrylate selected from the group consisting of homopolymers and copolymers of acrylic acid or methacrylic acid.
Claim 7
Dependent Claim
21 words
Agent as claimed in claim 1 or 3, wherein the component (c) is a homopolymer of acrylic acid or methacrylic acid.
Claim 8
Dependent Claim
18 words
Agent as claimed in claim 1 or 3, wherein the component (c) is a homopolymer of acrylic acid.
Claim 9
Dependent Claim
82 words
Agent as claimed in claim 1, wherein the components are present in the following quantities: (a) 45 to 60% by weight (b) 40 to 55% by weight (c) 0.1 to 1% by weight (d) 0.1 to 0.5% by weight (e) 0.1 to 0.7% by weight (f) 0.05 to 0.5% by weight and (g) 0.1 to 0.5% by weight, the quantity of the components (a) and (b) in the agent being 96 to 99% by weight, relative to the weight of the agent.
Claim 10
Dependent Claim
52 words
Agent as claimed in claim 1, which additionally contains: (h) 0.01 to 0.5% by weight of at least one anti-oxidant and, in the case of a crosslinked polyacrylate having a viscosity of about 1,000 to 5,000 mPa.s, (i) 0.01 to 0.5% by weight of a high-molecular xanthan gum as a further thickener.
Claim 11
Dependent Claim
24 words
Agent as claimed in claim 9, which contains each of the components (h) and (i) in a quantity of 0.03 to 0.1% by weight.
References Cited (Backward Citations)
CA772557A
Cited
US2373727A
Cited
US3412030A
Cited
GB1285862A
Cited
US3630913A
Cited
US3624243A
Cited
DE2423893A1
Cited
US3940356A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-08 | 1986-05-10 | 1986-11-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-08 | 1990-05-10 | 1990-11-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-08 | 1994-05-10 | 1994-11-09 | $7700.00 | Window Closed / Lapsed |