Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1981-10-05
•
Granted: 1982-11-09
•
Expires: 2001-10-05
Abstract
Abstract The invention provides a method for molding a block of a fused quartz glass by the plastic deformation of a starting block with smaller dimensions at a high temperature. The molding procedure is carried out in a graphite mold under compression at a temperature of 1700° C. or higher in an atmosphere of helium at a pressure in the range, preferably, from 50 to 500 Torr. The cooling schedule as specified is also of importance in order that the molded quartz glass block is freed from any strain or cracks.
Inventors
- 👤 Haruo Okamoto
- 👤 Motoyuki Yamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 13:02
CPC Classifications
C; C03; C03B; C03B11/00; C03B11/06; C03B11/08; C03B11/084; C03B2215/00; C03B2215/02; C03B2215/05; C03B2215/07; C03B2215/40
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
122 words
A method for shaping a block of a fused quartz glass from a starting quartz glass block which comprises the steps of (a) placing the starting block in a mold made of graphite, (b) causing plastic deformation of the starting block to fill the mold by compression under an atmosphere of helium at a temperature of 1700° C. or higher, (c) rapidly cooling the thus molded block in the graphite mold down to a temperature in the range from 1300° C. to 1100° C., (d) slowly cooling the molded block at a temperature of 1300° to 1100° C. in the graphite mold down to a temperature of 900° C. or below, and (e) taking the molded block out of the graphite mold.
Claim 2
Independent Claim
122 words
A method for shaping a block of a fused quartz glass from a starting quartz glass block which comprises the steps of (a) placing the starting block in a mold made of graphite, (b) causing plastic deformation of the starting block to fill the mold by compression under an atmosphere of helium at a temperature of 1700° C. or higher, (c) rapidly cooling the thus molded block in the graphite mold down to a temperature in the range from 1300° C. to 1100° C., (d) slowly cooling the molded block at a temperature of 1300° to 1100° C. in the graphite mold down to a temperature of 900° C. or below, and (e) taking the molded block out of the graphite mold.
Claim 3
Dependent Claim
17 words
The method as claimed in claim 1 wherein the mold made of graphite is a split mold.
Claim 4
Dependent Claim
27 words
The method as claimed in claim 1 wherein the pressure for compression in the step (b) is in the range from 1 to 100 g/cm 2 .
Claim 5
Dependent Claim
29 words
The method as claimed in claim 1 wherein the pressure of helium in the atmosphere in the step (b) is in the range from 50 Torr to 5000 Torr.
Claim 6
Dependent Claim
31 words
The method as claimed in claim 1 wherein the temperature at which the plastic deformation of the starting block is caused is in the range from 1730° C. to 1800° C.
Claim 7
Dependent Claim
25 words
The method as claimed in claim 1 wherein the plastic deformation of the starting block is caused over a period of 10 to 180 minutes.
Claim 8
Dependent Claim
24 words
The method as claimed in claim 1 wherein the time taken for the rapid cooling in the step (c) is 60 minutes or shorter.
Claim 9
Dependent Claim
21 words
The method as claimed in claim 1 wherein the rate of cooling in the step (d) is 100° C./hour or smaller.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-08 | 1986-05-10 | 1986-11-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-08 | 1990-05-10 | 1990-11-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-08 | 1994-05-10 | 1994-11-09 | $7700.00 | Window Closed / Lapsed |