Economic preparation of alumina suitable for isostatic pressing and sintering
Assignee: Philips North America LLC
•
Filing: 1981-10-19
•
Granted: 1982-11-02
•
Expires: 2001-10-19
Abstract
Abstract Method for preparing finely divided high purity alumina doped with a small predetermined percentage of magnesia. In the preparation, there is first formed a mixed clear solution of aluminum alkoxide and a small amount of magnesium in the form of alkoxide or water soluble magnesium salt. There is then included with the clear solution a substantial excess of water over that required to completely hydrolyze the alkoxide and there is added thereto a small amount of selected acid which is effective to peptize the resulting slurry. The formed milky slurry is then allowed to become fully peptized to form a clear sol. The clear sol is converted to a finely divided and dried powder either by forming the sol into a gel, which is then dried, and mechanically reduced to a powder status or by spray drying the sol at elevated temperatures which produces the dried powder. Thereafter, the finely divided and dried powder is calcined at a temperature of from about 700° C. to about 900° C., with the crystalline structure of the powder predominately being that of a delta alumina. The preparation of this alumina is very economic and the resulting material is suitable for being isostatically pressed into a tubular form and then sintered to translucent tubular form to a density which closely approaches theoretical.
Inventors
- 👤 Shih-Ming Ho
- 👤 Bulent E. Yoldas
- 👤 Douglas M. Mattox
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 11:42
CPC Classifications
C; C01; C01F; C01F7/00; B; B82; B82Y; B82Y30/00; C01F7/02; C01F7/34; C01F7/36; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B35/115; C01P; C01P2004/00; C01P2004/51; C01P2004/52; C01P2004/60; C01P2004/62; C01P2004/64; C01P2006/00; C01P2006/80
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
243 words
The method of preparing finely divided alumina doped with a small predetermined percentage of magnesia and which is suitable for being isostatically pressed into tubular form and then sintered to translucent light-transmitting tubular form to a density which closely approximates theoretical, which method comprises: forming a mixed clear solution substantially comprising a predetermined amount of aluminum alkoxide of the formula Al(OR) 3 where R contains from one to six carbon atoms and a small predetermined amount of water soluble magnesium salt which will decompose on heating to magnesia or magnesium alkoxide of the formula Mg(OR) 2 where R contains from one to six carbon atoms, and wherein the atom ratio of Al to Mg in said mixed solution is that atom ratio which is desired in the prepared finely divided magnesia-doped alumina; including with the mixed clear solution a substantial excess of water over that amount required to completely hydrolyze the alkoxide present to form a milky slurry and adding thereto a small predetermined amount of selected acid which is effective to peptize said slurry, and allowing the formed milky slurry to become fully peptized and form a clear sol; converting the formed clear sol to a finely divided and dried powder; and calcining the finely divided and dried powder for a predetermined time at a temperature in the range of from about 700° C. to about 900° C., with the crystalline structure of the calcined powder predominately being that of delta alumina.
Claim 2
Independent Claim
243 words
The method of preparing finely divided alumina doped with a small predetermined percentage of magnesia and which is suitable for being isostatically pressed into tubular form and then sintered to translucent light-transmitting tubular form to a density which closely approximates theoretical, which method comprises: forming a mixed clear solution substantially comprising a predetermined amount of aluminum alkoxide of the formula Al(OR) 3 where R contains from one to six carbon atoms and a small predetermined amount of water soluble magnesium salt which will decompose on heating to magnesia or magnesium alkoxide of the formula Mg(OR) 2 where R contains from one to six carbon atoms, and wherein the atom ratio of Al to Mg in said mixed solution is that atom ratio which is desired in the prepared finely divided magnesia-doped alumina; including with the mixed clear solution a substantial excess of water over that amount required to completely hydrolyze the alkoxide present to form a milky slurry and adding thereto a small predetermined amount of selected acid which is effective to peptize said slurry, and allowing the formed milky slurry to become fully peptized and form a clear sol; converting the formed clear sol to a finely divided and dried powder; and calcining the finely divided and dried powder for a predetermined time at a temperature in the range of from about 700° C. to about 900° C., with the crystalline structure of the calcined powder predominately being that of delta alumina.
Claim 3
Dependent Claim
49 words
The method as specified in claim 1, wherein said formed clear sol is converted to a finely divided and dried powder by evaporating sufficient water from said sol to convert same to a gel, drying the gel, and physically reducing the resulting dried material to finely divided powder form.
Claim 4
Dependent Claim
35 words
The method as specified in claim 1, wherein said formed clear sol is converted to a finely divided and dried powder by spray drying said sol at a temperature above the boiling temperature of water.
Claim 5
Independent Claim
60 words
The method as specified in claims 2 or 3, wherein a small predetermined amount of yttrium in the form of water soluble yttrium salt which will decompose to yttria on heating or yttrium alkoxide of the formula Y(OR) 3 where R contains from one to six carbon atoms is also included as a part of said initial mixed clear solution.
Claim 6
Dependent Claim
27 words
The method as specified in claim 1, wherein said aluminum alkoxide is aluminum butoxide, said magnesium alkoxide is magnesium ethoxide, and said selected acid is nitric acid.
Claim 7
Dependent Claim
20 words
The method as specified in claim 1, wherein said selected acid is one of nitric, hydrochloric, perchloric, acetic and trichloroacetic.
Claim 8
Dependent Claim
23 words
The method as specified in claim 1, wherein said magnesium salt is at least one of magnesium acetate, magnesium chloride and magnesium nitrate.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-11-01 | 1986-05-03 | 1986-11-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-11-01 | 1990-05-03 | 1990-11-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-11-01 | 1994-05-03 | 1994-11-02 | $7700.00 | Window Closed / Lapsed |