Thermoplastic synthetic filaments and process for producing the same
Assignee: Teijin Ltd
•
Filing: 1981-03-05
•
Granted: 1982-10-26
•
Expires: 2001-03-05
Abstract
Abstract Thermoplastic synthetic filaments having a properly delustered appearance and an adequate frictional property, comprise 85 to 99% by weight of a thermoplastic matrix polymer and 1 to 15% by weight of a dispersed polymer which is incompatible with the matrix polymer and uniformly dispersed in the form of fine particles in the matrix polymer, and are characterized by numerous fine protuberances consisting of the dispersed polymer and formed in the number of at least 5 per 10 μ 2 on the peripheral surface of each individual filament, the protuberances preferably being each in the form of a hemisphere, hemispheroid or hemiellipsoid extending along the longitudinal axis of each individual filament.
Inventors
- 👤 Shiro Kumakawa
- 👤 Toshimasa Kuroda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 07:55
CPC Classifications
D; D01; D01F; D01F1/00; D01F1/02; D01F1/08; D01F1/10; D01F6/00; D01F6/88; D01F6/92; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2927; Y10T428/2973; Y10T428/2978
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
82 words
Thermoplastic synthetic filaments comprising 85 to 99% by weight of a thermoplastic matrix polymer and 1 to 15% by weight of a dispersed polymer comprising at least one polysulfone which is incompatible with said matrix polymer and dispersed in the form of fine particles in said matrix polymer, which filaments are characterized by numerous fine protuberances consisting of said dispersed polymer and formed in the number of at least 5 per 10 square microns on the peripheral surface of each individual filament.
Claim 2
Dependent Claim
82 words
Thermoplastic synthetic filaments comprising 85 to 99% by weight of a thermoplastic matrix polymer and 1 to 15% by weight of a dispersed polymer comprising at least one polysulfone which is incompatible with said matrix polymer and dispersed in the form of fine particles in said matrix polymer, which filaments are characterized by numerous fine protuberances consisting of said dispersed polymer and formed in the number of at least 5 per 10 square microns on the peripheral surface of each individual filament.
Claim 3
Dependent Claim
30 words
The filaments as claimed in claim 1, wherein said protuberances are each in the form of a hemisphere, hemispheroid or hemiellipsoid extending along the longitudinal axis of the individual filament.
Claim 4
Dependent Claim
21 words
The filaments as claimed in claim 1, wherein the area of bottoms of said protuberances is 0.5 square microns or more.
Claim 5
Dependent Claim
14 words
The filaments as claimed in claim 1, wherein said matrix polymer is thermoplastic polyester.
Claim 6
Dependent Claim
17 words
The filaments as claimed in claim 1, wherein said polyester consists essentially of recurring ethylene terephthalate units.
Claim 7
Dependent Claim
24 words
The filaments as claimed in claim 1, wherein said dispersed polymer is non-crystalline and has a glass transition temperature of at least 150° C.
Claim 8
Dependent Claim
25 words
The filaments as claimed in claim 1, wherein the amount of said dispersed polymer is in the range of from 3 to 9% by weight.
Claim 9
Dependent Claim
97 words
The filaments as claimed in claim 1, wherein the individual filaments exhibit a snap back value of 4% or less, said snap back value being defined by the equation (1): SB=(eb-esb)-eb×rb/100 (1) wherein SB represents a snap back value in % of the filaments, eb represents a breaking elongation in % of the filaments, rb represents a tensile recovery in % of the filaments at its break and esb represents an elongation in % of the filament determined from the difference between the length of the filament at its break and the original length of the filament.
Claim 10
Dependent Claim
85 words
A fiber as claimed in claim 1, wherein the individual fiber exhibits a breaking modulus of 4 g/d or less, said breaking modulus being defined by the equation (2): ##EQU4## wherein Mb represents a breaking modulus in g/d of the filament, sb represents a gradient in g/% of a tangential line drawn through a breaking point of the filament on the stress-strain curve of the filament, eb represents a breaking elongation in % of the filament and D o represents a denier of the filament.
Claim 11
Dependent Claim
20 words
The filaments as claimed in claim 1,2,3,4,5,6,7,8 or 9, wherein said polysulfone comprises the recurring unit of the formula ##STR3##
Claim 12
Dependent Claim
82 words
The filament as claimed in claim 1, wherein said protuberances are removed to cause formation of neumerous concaves on the peripheral surface of the individual filament, each concave being composed of a center portion thereof in the form of a hemisphere, hemispheroid or hemiellipsoid and a pair of wing portions thereof each in the form of a hemicone or hemielliptic cone and each extending from the ceter portion in opposit direction to the other along the longitudinal axis of the individual filament.
Claim 13
Dependent Claim
21 words
The filaments as claimed in claim 1, wherein said concaves each have an opening area of at least 5 square microns.
Claim 14
Dependent Claim
29 words
The filaments as claimed in claim 1, wherein the number of said concaves is at least one per 300 square microns of the peripheral surface of the individual filament.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-25 | 1986-04-26 | 1986-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-25 | 1990-04-26 | 1990-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-25 | 1994-04-26 | 1994-10-26 | $7700.00 | Window Closed / Lapsed |