Injection blow molding pet products
Assignee: Wheaton Inc
•
Filing: 1980-08-27
•
Granted: 1982-10-26
•
Expires: 2000-08-27
Abstract
Abstract Method for injection blow molding transparent hollow objects from a polyethylene terephthalate melt comprises molding from a melt at 530°-575° F. into a parison, quickly and relatively uniformly cooled by parison mold elements, at 75°-150° F., to a temperature above the glass transition temperature of the melt. The parison is then immediately blown and cooled to temperature below the softening point of the melt, all in a manner to avoid crystallization and to produce a hollow PET object, typically a clear bottle.
Inventors
- 👤 Louis Germanio
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:15
CPC Classifications
B; B29; B29C; B29C49/00; B29C49/0005; B29C49/0006; B29C49/42; B29C49/64; B29C43/00; B29C43/32; B29C43/52; B29C2043/527; B29C49/78; B29C2049/7879; B29C2949/00; B29C2949/07; B29C2949/0715; B29C2949/081; B29C2949/0811; B29C2949/082; B29C2949/0861; B29C2949/0872; B29C2949/20; B29C2949/22; B29C2949/24; B29C2949/26; B29C2949/28; B29C2949/30; B29C2949/3024; B29C2949/3032; B29C49/02; B29C49/06; B29C49/08; B29C49/087; B29C49/42394; B29K; B29K2067/00; B29K2105/00; B29K2105/25; B29K2105/253
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
191 words
A method for injection blow molding transparent hollow objects from a polyethylene terephthalate melt comprising: (a) cooling a parison mold and a core rod each to a preselected temperature in the range of 75°-150° F., injection molding from said melt at 530°-575° F. a parison in a mold shape formed by said core rod disposed centrally in a cavity of said parison mold, said parison having a wall thickness of 0.075-0.200 inches; (b) quickly and uniformly cooling said parison in a manner to avoid crystallization by holding said parison in said parison mold for 1-4 seconds while continuing to cool said injection mold to said preselected mold temperature, then removing said core rod and said parison from said parison mold with the outer surface of said parison at 185°-245° F.; (c) immediately transferring said core rod and parison to a blow mold at 40°-60° F. and introducing blow air at 100-200 psi through said core into the interior of said parison for a time period sufficient to blow said parison into the shape of said blow mold and quickly cool the blown shape also in a manner to avoid crystallization thereof.
Claim 2
Independent Claim
191 words
A method for injection blow molding transparent hollow objects from a polyethylene terephthalate melt comprising: (a) cooling a parison mold and a core rod each to a preselected temperature in the range of 75°-150° F., injection molding from said melt at 530°-575° F. a parison in a mold shape formed by said core rod disposed centrally in a cavity of said parison mold, said parison having a wall thickness of 0.075-0.200 inches; (b) quickly and uniformly cooling said parison in a manner to avoid crystallization by holding said parison in said parison mold for 1-4 seconds while continuing to cool said injection mold to said preselected mold temperature, then removing said core rod and said parison from said parison mold with the outer surface of said parison at 185°-245° F.; (c) immediately transferring said core rod and parison to a blow mold at 40°-60° F. and introducing blow air at 100-200 psi through said core into the interior of said parison for a time period sufficient to blow said parison into the shape of said blow mold and quickly cool the blown shape also in a manner to avoid crystallization thereof.
Claim 3
Dependent Claim
91 words
A method as recited in claim 1, wherein just prior to said molding, said core rod outer surface is at a temperature of 90°-120° F. and said parison mold is cooled by an internal coolant at a temperature of 80°-110° F., said molded parison wall thickness is 0.090 0.120 inches, said holding time is 1.5-3 seconds, said parison outer surface temperature just prior to transfer is 200°-220° F., said blow mold pressure is 150-200 psi and said blow mold is cooled by an internal coolant at a temperature of 35°-50° F.
Claim 4
Independent Claim
156 words
A method for injection blow molding transparent hollow objects from a polyethylene terephthalate melt comprising: (a) cooling a core rod and parison mold each to a preselected temperature below 150° F., and then injecting a portion of said melt into said parison mold while continuing to cool said mold to said preselected mold temperature to produce a parison at relatively uniform pressure and temperature; (b) said cooled core rod and parison mold quickly and uniformly cooling said parison to an intermediate temperature in a manner to avoid crystallization thereof such that the surface temperature of said parison is reduced within four seconds following completion of molding to a temperature in the range of 185°-245° F.; (c) then immediately blowing said parison into a final shape in a mold at sufficiently low temperature to quickly cool said blown shape to a temperature below the softening temperature of said melt, also in a manner to avoid crystallization thereof.
Claim 5
Independent Claim
156 words
A method for injection blow molding transparent hollow objects from a polyethylene terephthalate melt comprising: (a) cooling a core rod and parison mold each to a preselected temperature below 150° F., and then injecting a portion of said melt into said parison mold while continuing to cool said mold to said preselected mold temperature to produce a parison at relatively uniform pressure and temperature; (b) said cooled core rod and parison mold quickly and uniformly cooling said parison to an intermediate temperature in a manner to avoid crystallization thereof such that the surface temperature of said parison is reduced within four seconds following completion of molding to a temperature in the range of 185°-245° F.; (c) then immediately blowing said parison into a final shape in a mold at sufficiently low temperature to quickly cool said blown shape to a temperature below the softening temperature of said melt, also in a manner to avoid crystallization thereof.
References Cited (Backward Citations)
US3822332A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-25 | 1986-04-26 | 1986-10-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-25 | 1990-04-26 | 1990-10-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-25 | 1994-04-26 | 1994-10-26 | $7700.00 | Window Closed / Lapsed |