Wholly aromatic polyester capable of forming an anisotropic melt phase at an advantageously reduced temperature
Assignee: Celanese Corp
•
Filing: 1981-06-04
•
Granted: 1982-10-19
•
Expires: 2001-06-04
Abstract
Abstract An improved wholly aromatic polyester is provided which exhibits an anisotropic melt phase and which is capable of readily undergoing melt processing. The wholly aromatic polyester consists essentially of the recurring units (a) p-oxybenzoyl moiety, (b) 2,6-dioxynaphthalene moiety, (c) 2,6-dioxyanthraquinone moiety, and (d) terephthaloyl moiety in the concentrations indicated. The resulting polymer is substantially free of aromatic rings possessing ring substitution and meta disposed linkages in the polymer chain. The present invention represents an improvement over the polyester of U.S. Pat. No. 4,184,996 since the melt phase may be formed at an advantageously reduced temperature thereby better facilitating the use of standard melt processing equipment when forming fibers, films, three-dimensional shaped articles, etc. The reduction in possible melt processing temperature is accomplished without any significant diminution in melt anisotropy such as that which would result if non-symmetrical meta disposed linkages were present in the polymer chain. Also, the present polyester does not rely upon the presence of ring substitution as a means for producing the desired melt anisotropy.
Inventors
- 👤 Larry F. Charbonneau
- 👤 Gordon W. Calundann
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 07:19
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/60; C08G63/605
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
142 words
A melt processable wholly aromatic polyester capable of forming an anisotropic melt phase consisting essentially of the recurring moieties I, II, III, and IV having the structural formulas wherein: ##STR9## wherein said wholly aromatic polyester is substantially free of aromatic rings possessing ring substitution and meta disposed linkages in the polymer chain, wherein said wholly aromatic polyester comprises approximately 20 to 80 mole percent of moiety I, approximately 5 to 20 mole percent of moiety II, approximately 5 to 20 mole percent of moiety III, and approximately 10 to 40 mole percent of moiety IV, and wherein said wholly aromatic polyester can be melt processed at a lower minimum temperature when compared to a similarly formed wholly aromatic polyester wherein moiety III is omitted and is replaced by an additional concentration of moiety II which corresponds to the concentration of moiety III.
Claim 2
Dependent Claim
142 words
A melt processable wholly aromatic polyester capable of forming an anisotropic melt phase consisting essentially of the recurring moieties I, II, III, and IV having the structural formulas wherein: ##STR9## wherein said wholly aromatic polyester is substantially free of aromatic rings possessing ring substitution and meta disposed linkages in the polymer chain, wherein said wholly aromatic polyester comprises approximately 20 to 80 mole percent of moiety I, approximately 5 to 20 mole percent of moiety II, approximately 5 to 20 mole percent of moiety III, and approximately 10 to 40 mole percent of moiety IV, and wherein said wholly aromatic polyester can be melt processed at a lower minimum temperature when compared to a similarly formed wholly aromatic polyester wherein moiety III is omitted and is replaced by an additional concentration of moiety II which corresponds to the concentration of moiety III.
Claim 3
Dependent Claim
23 words
A melt processable wholly aromatic polyester according to claim 1 which is capable of forming an anisotropic melt phase below approximately 300° C.
Claim 4
Dependent Claim
23 words
A melt processable wholly aromatic polyester according to claim 1 which is capable of forming an anisotropic melt phase below approximately 290° C.
Claim 5
Dependent Claim
36 words
A melt processable wholly aromatic polyester according to claim 1 which exhibits an inherent viscosity of approximately 2 to 8 dl./gram when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 60° C.
Claim 6
Dependent Claim
25 words
A melt processable wholly aromatic polyester according to claim 1 wherein the molar quantities of moieties II and III are substantially equal to each other.
Claim 7
Dependent Claim
28 words
A melt processable wholly aromatic polyester according to claim 1 wherein the total molar quantity of moieties II and III is substantially equal to that of moiety IV.
Claim 8
Dependent Claim
43 words
A melt processable wholly aromatic polyester according to claim 1 wherein the molar quantities of moieties II and III are substantially equal to each other and the total molar quantity of moieties II and III is substantially equal to that of moiety IV.
Claim 9
Dependent Claim
13 words
A molded article comprising the melt processable wholly aromatic polyester of claim 1.
Claim 10
Dependent Claim
29 words
A molding compound comprising the melt processable wholly aromatic polyester of claim 1 which incorporates approximately 1 to 60 percent by weight of a solid filler and/or reinforcing agent.
Claim 11
Dependent Claim
15 words
A fiber which has been melt spun from the wholly aromatic polyester of claim 1.
Claim 12
Dependent Claim
142 words
A melt processable wholly aromatic polyester capable of forming an anisotropic melt phase consisting essentially of the recurring moieties I, II, III, and IV having the structural formulas wherein: ##STR10## wherein said wholly aromatic polyester is substantially free of aromatic rings possessing ring substitution and meta disposed linkages in the polymer chain, wherein said wholly aromatic polyester comprises approximately 40 to 60 mole percent of moiety I, approximately 10 to 15 mole percent of moiety II, approximately 10 to 15 mole percent of moiety III, and approximately 20 to 30 mole percent of moiety IV, and wherein said wholly aromatic polyester can be melt processed at a lower minimum temperature when compared to a similarly formed wholly aromatic polyester wherein moiety III is omitted and is replaced by an additional concentration of moiety II which corresponds to the concentration of moiety III.
Claim 13
Dependent Claim
142 words
A melt processable wholly aromatic polyester capable of forming an anisotropic melt phase consisting essentially of the recurring moieties I, II, III, and IV having the structural formulas wherein: ##STR10## wherein said wholly aromatic polyester is substantially free of aromatic rings possessing ring substitution and meta disposed linkages in the polymer chain, wherein said wholly aromatic polyester comprises approximately 40 to 60 mole percent of moiety I, approximately 10 to 15 mole percent of moiety II, approximately 10 to 15 mole percent of moiety III, and approximately 20 to 30 mole percent of moiety IV, and wherein said wholly aromatic polyester can be melt processed at a lower minimum temperature when compared to a similarly formed wholly aromatic polyester wherein moiety III is omitted and is replaced by an additional concentration of moiety II which corresponds to the concentration of moiety III.
Claim 14
Dependent Claim
23 words
A melt processable wholly aromatic polyester according to claim 11 which is capable of forming an anisotropic melt phase below approximately 300° C.
Claim 15
Dependent Claim
23 words
A melt processable wholly aromatic polyester according to claim 11 which is capable of forming an anisotropic melt phase below approximately 290° C.
Claim 16
Dependent Claim
25 words
A melt processable wholly aromatic polyester according to claim 11 wherein the molar quantities of moieties II and III are substantially equal to each other.
Claim 17
Dependent Claim
28 words
A melt processable wholly aromatic polyester according to claim 11 wherein the total molar quantity of moieties II and III is substantially equal to that of moiety IV.
Claim 18
Dependent Claim
43 words
A melt processable wholly aromatic polyester according to claim 11 wherein the molar quantities of moieties II and III are substantially equal to each other and the total molar quantity of moieties II and III is substantially equal to that of moiety IV.
Claim 19
Dependent Claim
41 words
A melt processable wholly aromatic polyester according to claim 11 which comprises approximately 40 mole percent of moiety I, approximately 15 mole percent of moiety II, approximately 15 mole percent of moiety III, and approximately 30 mole percent of moiety IV.
Claim 20
Dependent Claim
41 words
A melt processable wholly aromatic polyester according to claim 11 which comprises approximately 60 mole percent of moiety I, approximately 10 mole percent of moiety II, approximately 10 mole percent of moiety III, and approximately 20 mole percent of moiety IV.
Claim 21
Dependent Claim
36 words
A melt processable wholly aromatic polyester according to claim 11 which exhibits an inherent viscosity of approximately 2 to 8 dl./gram when dissolved in a concentration of 0.1 percent by weight of pentafluorophenol at 60° C.
Claim 22
Dependent Claim
13 words
A molded article comprising the melt processable wholly aromatic polyester of claim 11.
Claim 23
Dependent Claim
29 words
A molding compound comprising the melt processable wholly aromatic polyester of claim 11 which incorporates approximately 1 to 60 percent by weight of a solid filler and/or reinforcing agent.
Claim 24
Dependent Claim
15 words
A fiber which has been melt spun from the wholly aromatic polyester of claim 11.
References Cited (Backward Citations)
US4224433A
Cited
US4188476A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-18 | 1986-04-19 | 1986-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-18 | 1990-04-19 | 1990-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-18 | 1994-04-19 | 1994-10-19 | $7700.00 | Window Closed / Lapsed |