Method for superplastic forming
Assignee: Boeing North American Inc
•
Filing: 1980-05-16
•
Granted: 1982-10-19
•
Expires: 2000-05-16
Abstract
Abstract A method is provided for eliminating internal voids in superplastically forming parts. A blank of material which is capable of being formed superplastically is held opposite a forming surface of a die. The blank is heated to the superplastic forming temperature and pressure is applied to both sides of the blank. This pressure is sufficient to prevent the formation of voids. The pressure on the side of the blank farthest from the die surface is then increased to superplastically form the material against the die surface. In a second embodiment, the pressure is applied after the blank has been formed either by maintaining the forming pressure to compreses the material between the forming pressure and the reaction of the die, or by applying a fluid pressure to both sides of the part, thereby removing voids by plastic deformation and diffusion.
Inventors
- 👤 C. Howard Hamilton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:27
CPC Classifications
B; B21; B21D; B21D26/00; B21D26/02; B21D26/053; B21D26/055
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
145 words
A method of reducing cavitation during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying positive pressure concurrently to both sides of said blank sufficient to prevent the formation of voids in said material; and increasing said positive pressure on the side of said blank farthest from said forming surface to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity, whereby said blank stretches by said tensile strain toward said forming surface and forms against said forming surface without cavitation.
Claim 2
Independent Claim
145 words
A method of reducing cavitation during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying positive pressure concurrently to both sides of said blank sufficient to prevent the formation of voids in said material; and increasing said positive pressure on the side of said blank farthest from said forming surface to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity, whereby said blank stretches by said tensile strain toward said forming surface and forms against said forming surface without cavitation.
Claim 3
Dependent Claim
78 words
The method as claimed in claim 1 wherein said positive pressure applied to both sides of said blank is at least equal to σ-2γ/r, where σ is the hydrostatic tensile stress component imposed during said positive step of increasing said pressure on the side of said blank furthest from said forming surface, γ is the surface energy of the void, and r is the void radius which is selected to be larger than intergranular particles in the material.
Claim 4
Independent Claim
157 words
A method of reducing cavitation which occurs during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying positive pressure on the side of said blank farthest from said forming surface sufficient to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity so that said material stretches by said tensile strain toward said forming surface and forms against said forming surface; and applying positive pressure on said farthest said of said blank after said blank has formed against said forming surface whereby voids in said material are removed by plastic deformation and diffusion.
Claim 5
Independent Claim
157 words
A method of reducing cavitation which occurs during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying positive pressure on the side of said blank farthest from said forming surface sufficient to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity so that said material stretches by said tensile strain toward said forming surface and forms against said forming surface; and applying positive pressure on said farthest said of said blank after said blank has formed against said forming surface whereby voids in said material are removed by plastic deformation and diffusion.
Claim 6
Independent Claim
183 words
A method of reducing cavitation during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying positive pressure concurrently to both sides of said blank sufficient to retard the formation of voids in said material; increasing said positive pressure on the side of said blank farthest from said forming surface to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity so that said material stretches by said tensile strain toward said forming surface and forms against said forming surface; and maintaining positive pressure on said farthest side of said blank after said blank has formed against said forming surface to compress said material between said pressure and the reaction of said die, whereby voids in said material are removed.
Claim 7
Independent Claim
183 words
A method of reducing cavitation during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying positive pressure concurrently to both sides of said blank sufficient to retard the formation of voids in said material; increasing said positive pressure on the side of said blank farthest from said forming surface to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity so that said material stretches by said tensile strain toward said forming surface and forms against said forming surface; and maintaining positive pressure on said farthest side of said blank after said blank has formed against said forming surface to compress said material between said pressure and the reaction of said die, whereby voids in said material are removed.
Claim 8
Independent Claim
180 words
A method of reducing cavitation during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying a positive forward pressure on the side of said blank farthest from said forming surface sufficient to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity so that said material stretches by said tensile strain toward said forming surface; after said material begins stretching and while still applying said forward pressure applying a positive back pressure which is equal to or less than said forming pressure to the side of said blank opposite said farthest side to remove voids in said materials; and reducing said back pressure while continuing said forward pressure until said material forms against said forming surface.
Claim 9
Independent Claim
180 words
A method of reducing cavitation during superplastically forming a blank of material, comprising the steps of: providing a blank of material which exhibits an effective value of strain rate sensitivity at a forming temperature; providing a die having a forming surface; positioning said blank in said die opposite said forming surface; holding said blank at said forming temperature so that said material exhibits said effective value of strain rate sensitivity; applying a positive forward pressure on the side of said blank farthest from said forming surface sufficient to develop tensile strain in said material at a rate which provides said effective value of strain rate sensitivity so that said material stretches by said tensile strain toward said forming surface; after said material begins stretching and while still applying said forward pressure applying a positive back pressure which is equal to or less than said forming pressure to the side of said blank opposite said farthest side to remove voids in said materials; and reducing said back pressure while continuing said forward pressure until said material forms against said forming surface.
Claim 10
Dependent Claim
42 words
The method as claimed in claim 5, wherein said step of applying a positive forward pressure includes raising said forward pressure during said step of applying a positive back pressure, and then reducing said forward pressure as said back pressure is reduced.
Claim 11
Dependent Claim
24 words
The method as claimed in claim 5, wherein said steps of applying and reducing back pressure are done periodically during stretching of said material.
References Cited (Backward Citations)
US3340101A
Cited
US3516274A
Cited
US3920175A
Cited
US3927817A
Cited
US3974673A
Cited
US4197777A
Cited
US4087037A
Cited
US4233831A
Cited
US4266416A
Cited
US4233829A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-18 | 1986-04-19 | 1986-10-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-18 | 1990-04-19 | 1990-10-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-18 | 1994-04-19 | 1994-10-19 | $7700.00 | Window Closed / Lapsed |