Tungsten recovery from tungsten ore concentrates by caustic digestion
Assignee: Osram Sylvania Inc
•
Filing: 1981-05-07
•
Granted: 1982-10-12
•
Expires: 2001-05-07
Abstract
Abstract Tungsten is recovered from tungsten ore concentrates in the form of sodium tungstate by a basic process in which ground ore is first digested in a sodium hydroxide solution followed by diluting the solution to dissolve sodium tungstate separating the solution from the caustic insoluble sludge and crystallizing soluble sodium tungstate, wherein the present invention permits improved recovery of tungsten from difficult to process ores by the process steps of comminuting said tungsten ore concentrate to a particle size less than 325 mesh, adding said comminuted ore to aqueous sodium hydroxide at a concentration of at least 10 molar and digesting at a temperature of from about 75° C. to 150° C. for a sufficient period of time to convert substantially all of the tungsten values to soluble sodium tungstate, and diluting the mixture to reduce the sodium hydroxide concentration to between about 4.5 and 5.5 molar at a temperature below about 90° C. to substantially dissolve all of the sodium tungstate.
Inventors
- 👤 Lucretia R. Quatrini
- 👤 Marie B. Terlizzi
- 👤 Brice E. Martin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 02:50
CPC Classifications
C; C22; C22B; C22B34/00; C22B34/30; C22B34/36; C01; C01G; C01G41/00
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
195 words
A method for increasing the recovery of dissolved sodium tungstate from tungsten ore concentrate of the type which produce a sludge containing tungsten values when processed according to the steps of digesting said tungsten ore concentrate in concentrated sodium hydroxide to produce a mixture comprising soluble sodium tungstate and an insoluble sludge, diluting the mixture with water to form an aqueous portion containing dissolved sodium tungstate, separating the aqueous portion from the insoluble sludge portion and crystallizing sodium tungstate from the aqueous portion, the improvement comprising: comminuting said tungsten ore concentrate to a particle size less than 325 mesh, adding said comminuted ore to aqueous sodium hydroxide at a concentration of at least 10 molar and digesting in the presence of about 6 to 17 moles of sodium hydroxide per mole of tungsten at a temperature of from about 75° C. to 150° C. for a sufficient period of time to convert substantially all of the tungsten values to dissolvable sodium tungstate, and diluting the digested mixture to reduce the sodium hydroxide concentration to between about 4.5 and 5.5 molar at a temperature below about 90° C. to substantially dissolve all the dissolvable sodium tungstate.
Claim 2
Independent Claim
195 words
A method for increasing the recovery of dissolved sodium tungstate from tungsten ore concentrate of the type which produce a sludge containing tungsten values when processed according to the steps of digesting said tungsten ore concentrate in concentrated sodium hydroxide to produce a mixture comprising soluble sodium tungstate and an insoluble sludge, diluting the mixture with water to form an aqueous portion containing dissolved sodium tungstate, separating the aqueous portion from the insoluble sludge portion and crystallizing sodium tungstate from the aqueous portion, the improvement comprising: comminuting said tungsten ore concentrate to a particle size less than 325 mesh, adding said comminuted ore to aqueous sodium hydroxide at a concentration of at least 10 molar and digesting in the presence of about 6 to 17 moles of sodium hydroxide per mole of tungsten at a temperature of from about 75° C. to 150° C. for a sufficient period of time to convert substantially all of the tungsten values to dissolvable sodium tungstate, and diluting the digested mixture to reduce the sodium hydroxide concentration to between about 4.5 and 5.5 molar at a temperature below about 90° C. to substantially dissolve all the dissolvable sodium tungstate.
Claim 3
Dependent Claim
22 words
A method according to claim 1 wherein digestion is carried out at temperature of from about 75° C. to about 145° C.
Claim 4
Dependent Claim
48 words
A method according to claim 2 wherein after crystallizing said sodium tungstate from the aqueous portion, said sodium tungstate crystals are separated from a remaining aqueous portion containing excess sodium hydroxide, said remaining portion is treated to concentrate said excess sodium hydroxide for digesting additional tungsten ore concentrate.
Claim 5
Dependent Claim
27 words
A method according to claim 3 wherein said tungsten ore concentrate is digested for a period of time less than about 2 hours at a sufficient temperature.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-11 | 1986-04-12 | 1986-10-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-11 | 1990-04-12 | 1990-10-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-11 | 1994-04-12 | 1994-10-12 | $7700.00 | Window Closed / Lapsed |