Assignee: Phillips Petroleum Co
•
Filing: 1981-02-20
•
Granted: 1982-10-05
•
Expires: 2001-02-20
Abstract
Abstract A molded object having a sponge-like interior surrounded by a skin, molding composition from which it is produced, and the method for producing the article. Copolymers of vinyl-substituted aromatic compounds containing from 8-18 carbon atoms copolymerized with conjugated diene having from 4-12 carbon atoms and polymer chosen from among solid resinous polymers of vinyl-substituted aromatic compounds present in amounts ranging from about 10 to about 75 parts by weight per 100 parts by weight of the copolymer and solid resinous copolymers of ethylene present in an amount of about 5 to about 50 parts by weight per 100 parts by weight of the copolymer are blended with a sufficient amount of polarizing agent to achieve rapid heating through response to microwave treatment, blowing agent in an amount sufficient to provide a sponge-like, rubbery porosity to an article molded therefrom, and, optionally, cellular control agent. Composition is melted at a temperature that activates the blowing agent, molded, and removed from the mold as an article having a sponge-like interior surrounded by polymeric skin.
Inventors
- 👤 Roy W. Siedenstrang
- 👤 Agmund K. Thorsrud
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 19:54
CPC Classifications
B; B29; B29C; B29C44/00; C; C08; C08J; C08J9/00; C08J9/0061; C08J9/04; C08J9/06; C08J9/10; C08J9/34; B29K; B29K2105/00; B29K2105/04; B29K2105/043; C08J2353/00; C08J2353/02; C08J2425/00; Y; Y10; Y10S; Y10S264/00; Y10S264/05; Y10T; Y10T428/00; Y10T428/249921; Y10T428/249953; Y10T428/249987; Y10T428/249988; Y10T428/249989
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
144 words
A method for producing molded sponge like articles comprising: (a) introducing into a mold an expandable thermoplastic elastomer composition comprising: (1) vinyl-substituted aromatic compounds containing from 8-18 carbon atoms copolymerized with conjugated diene having from 4-12 carbon atoms, (2) resinous solid polymer of vinyl-substituted aromatic compound in the range of about 10 to about 60 parts resinous polymer per 100 parts said copolymer, (3) polarizing agent, and (4) blowing agent in an amount sufficient to produce upon activation and molding an article of rubbery, sponge-like porosity surrounded by a thin, dense skin, (b) melting said composition with microwave energy at temperatures sufficient to activate said blowing agent and cause expansion of said melted composition, (c) shaping said expanding melted composition at low pressures to form said sponge like molded article having a thin, dense skin; and (d) removing said molded article from the mold.
Claim 2
Independent Claim
144 words
A method for producing molded sponge like articles comprising: (a) introducing into a mold an expandable thermoplastic elastomer composition comprising: (1) vinyl-substituted aromatic compounds containing from 8-18 carbon atoms copolymerized with conjugated diene having from 4-12 carbon atoms, (2) resinous solid polymer of vinyl-substituted aromatic compound in the range of about 10 to about 60 parts resinous polymer per 100 parts said copolymer, (3) polarizing agent, and (4) blowing agent in an amount sufficient to produce upon activation and molding an article of rubbery, sponge-like porosity surrounded by a thin, dense skin, (b) melting said composition with microwave energy at temperatures sufficient to activate said blowing agent and cause expansion of said melted composition, (c) shaping said expanding melted composition at low pressures to form said sponge like molded article having a thin, dense skin; and (d) removing said molded article from the mold.
Claim 3
Dependent Claim
32 words
A method of claim 1 wherein the total amount of blowing agent is in the range of about 6 to about 10 parts by weight per 100 parts by weight thermoplastic polymer.
Claim 4
Dependent Claim
31 words
A method of claim 3 wherein the blowing agent is a mixture of azobisformamide (ABFA) and 4,4'-oxabis(benzenesulfonylhydrazide) (OBSH) in a weight ratio range of about 1:2 to about 4:1 of ABFA/OBSH.
Claim 5
Dependent Claim
16 words
A method of claim 1 wherein the composition further comprises at least one cellular control agent.
Claim 6
Dependent Claim
17 words
A method of claim 4 wherein the composition further comprises a silicone-glycol copolymer as cellular control agent.
Claim 7
Independent Claim
154 words
A method for producing molded sponge like articles comprising (a) blending the followiang components to form an expandable thermoplastic elastomer molding composition: (1) vinyl-substituted aromatic compounds containing from 8-18 carbon atoms copolymerized with conjugated diene having from 4-12 carbon atoms, (2) resinous, solid polymer of vinyl-substituted aromatic compound in the range of about 10 to about 60 parts resinous polymer per 100 parts said copolymer, (3) polarizing agent, and (4) blowing agent in an amount sufficient to produce upon activation and molding an article of rubbery sponge-like porosity surrounded by a thin, dense skin; (b) introducing said molding composition into a mold; (c) melting said composition with microwave energy at temperatures sufficient to activate said blowing agent and cause expansion of said melted composition. (d) shaping said expanding melted composition at low pressures to form said sponge like molded article having a thin, dense skin; and (e) removing said molded article from the mold.
Claim 8
Independent Claim
154 words
A method for producing molded sponge like articles comprising (a) blending the followiang components to form an expandable thermoplastic elastomer molding composition: (1) vinyl-substituted aromatic compounds containing from 8-18 carbon atoms copolymerized with conjugated diene having from 4-12 carbon atoms, (2) resinous, solid polymer of vinyl-substituted aromatic compound in the range of about 10 to about 60 parts resinous polymer per 100 parts said copolymer, (3) polarizing agent, and (4) blowing agent in an amount sufficient to produce upon activation and molding an article of rubbery sponge-like porosity surrounded by a thin, dense skin; (b) introducing said molding composition into a mold; (c) melting said composition with microwave energy at temperatures sufficient to activate said blowing agent and cause expansion of said melted composition. (d) shaping said expanding melted composition at low pressures to form said sponge like molded article having a thin, dense skin; and (e) removing said molded article from the mold.
Claim 9
Dependent Claim
9 words
An article molded by the method of claim 1.
Claim 10
Dependent Claim
13 words
An article molded by the method of claim 2, 3, 4, or 5.
References Cited (Backward Citations)
US2459225A
Cited
US2465307A
Cited
US2476308A
Cited
US3242238A
Cited
US3281383A
Cited
US3414528A
Cited
US3803274A
Cited
US3705071A
Cited
US3826776A
Cited
US3823109A
Cited
US3959545A
Cited
US4022856A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-04 | 1986-04-05 | 1986-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-04 | 1990-04-05 | 1990-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-04 | 1994-04-05 | 1994-10-05 | $7700.00 | Window Closed / Lapsed |