Surface pre-treatment prior to underwater bonding
Assignee: UK Secretary of State for Energy
•
Filing: 1981-07-17
•
Granted: 1982-10-05
•
Expires: 2001-07-17
Abstract
Abstract The invention relates to a method of forming a metal-resin bond in the presence of environmental contamination of the metal surface by, for example, adsorbed water. The method consists of cleaning the metal surface and then coating it with a pre-treatment material adapted to displace the adsorbed contaminant and to be displaced in turn by the applied resin. The method is particularly relevant to the formation of steel/epoxy resin bonds underwater for the repair of submerged structures. The pre-treatment material may consist of a hydrocarbon solvent containing in solution a surfactant such as an ionic surfactant together with a viscous hydrocarbon such as petroleum jelly.
Inventors
- 👤 Malcolm R. Bowditch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 01:04
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/14; B05D7/16; B05D3/00; B05D3/10; B05D3/102; B05D3/12
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
138 words
A method of bonding an adherent resin to a metal surface having an adsorbed water contaminant including the steps of a. cleaning the metal surface b. removing the contaminant from said surface by coating the cleaned metal surface with a pretreatment material comprising an organic solvent and a surfactant, which pretreatment material is i. adapted to displace the absorbed contaminant from the metal surface ii. substantially chemically inert with respect to the metal iii. soluble in the resin, and iv. displaceable from the metal surface by the resin, and c. with said surface still coated with said pretreatment material, applying the adherent resin to the coated metal surface to cause the resin to remove said pretreatment material from said metal surface by solution of the pretreatment material into the resin while said resin bonds to said metal surface.
Claim 2
Independent Claim
138 words
A method of bonding an adherent resin to a metal surface having an adsorbed water contaminant including the steps of a. cleaning the metal surface b. removing the contaminant from said surface by coating the cleaned metal surface with a pretreatment material comprising an organic solvent and a surfactant, which pretreatment material is i. adapted to displace the absorbed contaminant from the metal surface ii. substantially chemically inert with respect to the metal iii. soluble in the resin, and iv. displaceable from the metal surface by the resin, and c. with said surface still coated with said pretreatment material, applying the adherent resin to the coated metal surface to cause the resin to remove said pretreatment material from said metal surface by solution of the pretreatment material into the resin while said resin bonds to said metal surface.
Claim 3
Dependent Claim
14 words
A method according to claim 1 wherein the resin is an epoxy resin adhesive.
Claim 4
Dependent Claim
23 words
A method according to claim 1 wherein the metal is selected from the group comprising steel, stainless steel, aluminum alloy and aluminum bronze.
Claim 5
Dependent Claim
27 words
A method according to claim 3 wherein the pretreatment material consists at least partially of a surfactant and a viscous hydrocarbon material dissolved in a hydrocarbon solvent.
Claim 6
Dependent Claim
29 words
A method according to claim 4 wherein the solvent is either white spirit or a mixture of white spirit and solvent naptha containing between 50% an d80% white spirit.
Claim 7
Dependent Claim
15 words
A method according to claim 4 or 5 wherein the surfactant is an ionic surfactant.
Claim 8
Dependent Claim
22 words
A method according to claim 6 wherein the surfactant comprises a quarternary ammonium salt cation and a fatty acid carboxylate group anion.
Claim 9
Dependent Claim
14 words
A method according to claim 7 wherein the surfactant is N-tallow 1, 3-diaminopropane dioleate.
Claim 10
Dependent Claim
42 words
A method according to claim 8 wherein the pretreatment material consists substantially of: a. 1 to 2 parts by weight of the surfactant b. 0.25 to 2 parts by weight of petroleum jelly, and c. 100 parts by weight of hydrocarbon solvent.
Claim 11
Dependent Claim
42 words
A method according to claim 1 wherein the metal is cleaned by grit blasting and coated with pretreatment material with the aid of a pressurized air supply connected to an outlet having a grit-dispensing forward compartment and a pretreatment material-dispensing rear compartment.
References Cited (Backward Citations)
US2669546A
Cited
US2636257A
Cited
FR1055872A
Cited
GB835072A
Cited
DE1209402B
Cited
FR1327755A
Cited
DE1546098A1
Cited
NL7512036A
Cited
US4170579A
Cited
US4273598A
Cited
GB2040732A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-10-04 | 1986-04-05 | 1986-10-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-10-04 | 1990-04-05 | 1990-10-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-10-04 | 1994-04-05 | 1994-10-05 | $7700.00 | Window Closed / Lapsed |