Quick-setting bituminous emulsion compositions
Assignee: Chevron USA Inc
•
Filing: 1980-07-28
•
Granted: 1982-09-28
•
Expires: 2000-07-28
Abstract
Abstract Quick setting, anionic bitumen emulsion compositions, suitable for road paving, recreational surfaces, etc., are formulated by emulsifying the bitumen in water with an ammonium or alkali metal salt of a hydrocarbon-substituted sulfuric, sulfonic, phosphoric or phosphonic acid emulsifier, mixing the emulsion with a fine aggregate and, prior to spreading the aggregate emulsion mixture, introducing an alkaline earth metal set initiator. The resulting composition rapidly breaks to a hard cohesive structure, so as to permit early use by traffic.
Inventors
- 👤 Richard L. Ferm
- 👤 Chester C. Latif
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:21
CPC Classifications
C; C08; C08L; C08L95/00; C08L95/005
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
153 words
A surfacing composition which rapidly sets to a tough cohesive surface with early development of tensile strength and rain resistance and is prepared by intimately mixing a solid particulate matter, a bituminous emulsion having a pH greater than about 7, and a set initiator in the following proportions: which comprises 100 parts by weight of a solid particulate matter, 0.1 to less than 5 parts by weight of a set initiator which is Portland cement, hydrated lime, or mixtures thereof; and from about 3 to 150 parts of a bituminous emulsion comprising from about 50 to 70 weight percent of a bituminous binder and from about 0.1 to about 3 weight percent of the anionic ammonium or alkali metal emulsifying salt of a compound selected from the group consisting of a hydrocarbyl phosphoric acid, a hydrocarbyl phosphonic acid and mixtures thereof, wherein the hydrocarbyl moiety is from about 8 to 22 carbon atoms.
Claim 2
Dependent Claim
153 words
A surfacing composition which rapidly sets to a tough cohesive surface with early development of tensile strength and rain resistance and is prepared by intimately mixing a solid particulate matter, a bituminous emulsion having a pH greater than about 7, and a set initiator in the following proportions: which comprises 100 parts by weight of a solid particulate matter, 0.1 to less than 5 parts by weight of a set initiator which is Portland cement, hydrated lime, or mixtures thereof; and from about 3 to 150 parts of a bituminous emulsion comprising from about 50 to 70 weight percent of a bituminous binder and from about 0.1 to about 3 weight percent of the anionic ammonium or alkali metal emulsifying salt of a compound selected from the group consisting of a hydrocarbyl phosphoric acid, a hydrocarbyl phosphonic acid and mixtures thereof, wherein the hydrocarbyl moiety is from about 8 to 22 carbon atoms.
Claim 3
Dependent Claim
36 words
A composition according to claim 1, wherein said emulsifying salt has the following formula: ##STR3## wherein R 2 is alkyl, alkenyl or alkylphenyl of from 8 to 24 carbon atoms and m is 0 or 1.
Claim 4
Dependent Claim
42 words
The composition according to claim 2 wherein the ammonium salt is a lower alkyl substituted amine wherein the alkyl groups are from 1 to 3 carbon atoms and the alkali metals are selected from the group consisting of lithium, sodium, and potassium.
Claim 5
Dependent Claim
22 words
The composition according to claim 3 wherein the pH of the bituminous emulsion is from about pH 7 to about pH 12.
Claim 6
Dependent Claim
18 words
The composition according to claim 2 wherein said bituminous emulsion concentration is from about 5 to 100 parts.
Claim 7
Dependent Claim
24 words
The composition according to claim 5 wherein the set initiator is present in an amount of from about 0.1 to about 3 weight percent.
Claim 8
Dependent Claim
27 words
The composition according to claim 1 further comprising water in an amount equal to or less than about 25 parts per 100 parts of solid particulate matter.
Claim 9
Dependent Claim
32 words
The composition according to claim 7 wherein the solid particulate matter is selected from the group consisting of rubber buffings, bagasse, hemp, organic polymeric fibers, inorganic aggregates, mineral aggregates, and mixtures thereof.
Claim 10
Dependent Claim
142 words
A process of forming a surfacing composition comprising: mixing a solid particulate matter; introducing a composition to said solid particulate matter which comprises about 0.1 to less than 5 parts by weight of a set initiator which is Portland cement, hydrated lime, or mixtures thereof; and about 3 to 150 parts of a bituminous emulsion per 100 parts by weight of solid particulate matter wherein said bituminous emulsion has a pH greater than about 7 and comprises 50 to 70 weight percent of a bituminous binder and from about 0.1 to about 3 weight percent of the anionic ammonium or alkali metal emulsifying salt of a compound selected from the group consisting of a hydrocarbyl phosphonic acid, a hydrocarbyl phosphoric acid, and mixtures thereof; and, mixing said solid particulate matter and said composition for a sufficient time to form a homogenous mixture.
Claim 11
Dependent Claim
142 words
A process of forming a surfacing composition comprising: mixing a solid particulate matter; introducing a composition to said solid particulate matter which comprises about 0.1 to less than 5 parts by weight of a set initiator which is Portland cement, hydrated lime, or mixtures thereof; and about 3 to 150 parts of a bituminous emulsion per 100 parts by weight of solid particulate matter wherein said bituminous emulsion has a pH greater than about 7 and comprises 50 to 70 weight percent of a bituminous binder and from about 0.1 to about 3 weight percent of the anionic ammonium or alkali metal emulsifying salt of a compound selected from the group consisting of a hydrocarbyl phosphonic acid, a hydrocarbyl phosphoric acid, and mixtures thereof; and, mixing said solid particulate matter and said composition for a sufficient time to form a homogenous mixture.
Claim 12
Dependent Claim
22 words
The process according to claim 9 wherein said composition and said solid particulate matter are mixed for about 0.5 to 5 minutes.
Claim 13
Dependent Claim
25 words
The process according to claim 9 wherein the set initiator is introduced to and mixed with the solid particulate matter prior to introducing said composition.
Claim 14
Dependent Claim
37 words
The process according to claim 11 wherein water in an amount less than about 25 parts per 100 parts of solid particulate matter is added during the mixing of said set initiator and said solid particulate matter.
Claim 15
Dependent Claim
13 words
The surfacing compositions produced according to the process of claims 10 or 12.
References Cited (Backward Citations)
USRE26204E
Cited
US2488252A
Cited
US2492994A
Cited
US2862830A
Cited
US2773777A
Cited
US3126292A
Cited
US3206319A
Cited
US3206174A
Cited
US3364046A
Cited
US3513005A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-09-27 | 1986-03-29 | 1986-09-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-09-27 | 1990-03-29 | 1990-09-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-09-27 | 1994-03-29 | 1994-09-28 | $7700.00 | Window Closed / Lapsed |