Process for coating glass
Assignee: BFG Glassgroup GIE
•
Filing: 1981-01-26
•
Granted: 1982-09-14
•
Expires: 2001-01-26
Abstract
Abstract In the formation of a metal or metal compound coating on a face of a heated glass substrate during its forward displacement by contacting such face at a coating station with at least one stream of droplets comprising one or more substances from which the coating is formed, problems are encountered in controlling the thickness of the coating. To facilitate such control, the or each droplet stream (21) is downwardly inclined towards the substrate (4) in the forward (6) direction or in a rearward direction, and at least one current (25) of preheated gas is discharged into the environment above the substrate (4) to flow in the same forward or rearward direction as the droplet stream(s) (21) and into contact therewith, the preheated gas current temperature being such as to influence the temperature of the droplets on their way to the substrate. The invention includes apparatus for performing the method.
Inventors
- 👤 Robert Van Laethem
- 👤 Albert Van Cauter
- 👤 Robert Terneu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:39
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C17/001; C03C17/002; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/229; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/112
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
155 words
In a process of forming a metal or metal compound coating on a face of a heated glass substrate during its displacement in a given direction, constituting a forward direction of displacement, by contacting such face, at a coating station through which the substrate passes, with at least one stream of droplets composed of at least one substance from which said coating metal or metal compound is formed on said face, the improvement comprising causing said stream of droplets to travel downwardly at an inclination to a direction parallel to the forward direction, discharging at least one current of pre-heated gas into the environment above the substrate so that such gas flows in said direction parallel to the forward direction above the substrate and into contact with said stream, and regulating the temperature of such gas current such that said current influences the temperature of droplets of said stream on their way to the substrate.
Claim 2
Dependent Claim
155 words
In a process of forming a metal or metal compound coating on a face of a heated glass substrate during its displacement in a given direction, constituting a forward direction of displacement, by contacting such face, at a coating station through which the substrate passes, with at least one stream of droplets composed of at least one substance from which said coating metal or metal compound is formed on said face, the improvement comprising causing said stream of droplets to travel downwardly at an inclination to a direction parallel to the forward direction, discharging at least one current of pre-heated gas into the environment above the substrate so that such gas flows in said direction parallel to the forward direction above the substrate and into contact with said stream, and regulating the temperature of such gas current such that said current influences the temperature of droplets of said stream on their way to the substrate.
Claim 3
Dependent Claim
25 words
A process according to claim 1, characterised in that the gas constituting said current is pre-heated to an extent such that it heats said droplets.
Claim 4
Dependent Claim
58 words
A process according to claim 1 or 2, characterised in that said gas current is caused to influence the temperature of the droplets selectively or differentially at at least one region across the path of the substrate so as at least partially to compensate for a tendency for the coating to vary in thickness because of other factors.
Claim 5
Dependent Claim
67 words
A process according to claim 3, characterised in that the substrate is a continuous ribbon of flat glass travelling from a flat glass forming plant and said gas current differentially affects the temperature of the droplets travelling towards different regions across the ribbon path so as to promote the formation of a coating which is of substantially uniform thickness over the full coated width of the ribbon.
Claim 6
Dependent Claim
33 words
A process according to claim 1 or 2, characterised in that the droplets comprise a solution of a metal compound and said gas current accelerates or retards evaporation of solvent from the droplets.
Claim 7
Dependent Claim
44 words
A process according to claim 1 or 2, characterised in that at least one said stream of droplets impinges on a zone within the substrate width to be coated and further comprising repeatedly displacing such stream to and fro transversely across the substrate path.
Claim 8
Dependent Claim
39 words
A process according to claim 1 or 2, characterised in that said at least one current of pre-heated gas is discharged continuously and the droplet stream is continuously intersected over its full width by said at least one current.
Claim 9
Dependent Claim
42 words
A process according to claim 1 or 2, characterised in that said at least one current of pre-heated gas is constituted by a plurality of currents continuously discharged from a series of stationary orifices distributed transversely over the path of the substrate.
Claim 10
Dependent Claim
33 words
A process according to claim 8, characterised in that quanta of gas supplied to different orifices are pre-heated to temperatures which are independently regulated for controlling the coating thickness profile across the substrate.
Claim 11
Dependent Claim
63 words
A process according to claim 1 or 2, characterised in that said step of regulating the gas temperature comprises pre-heating the gas forming said gas current in an automatically controlled manner in dependence on signals emitted by a device which detects thickness values of the coating on the moving substrate at a detecting station located in the forward direction from the coating station.
Claim 12
Dependent Claim
33 words
A process according to claim 1 or 2, characterised in that the gas current is directed towards the droplet stream so as to encounter that stream at a zone spaced above the substrate.
Claim 13
Dependent Claim
24 words
A process according to claim 1 or 2, characterised in that said coating station is located within a lehr through which the substrate travels.
Claim 14
Dependent Claim
24 words
A process according to claim 1 or 2, characterised in that said droplet stream travels downwardly and in the forward direction towards the substrate.
Claim 15
Dependent Claim
35 words
A process according to claim 1 or 2, characterised in that the included angle between the axis of the droplet stream and the substrate face being coated is in the range of 20° to 60°.
Claim 16
Dependent Claim
20 words
A process according to claim 14, characterised in that said included angle is in the range of 25° to 35°.
Claim 17
Dependent Claim
39 words
A process according to claim 1 or 2, characterised in that there is at least one said stream of droplets which is a parallel stream or which diverges from its source at an angle of not more than 30°.
Claim 18
Dependent Claim
38 words
A process according to claim 1 or 2, characterised in that there is at least one said droplet stream whose source is at a perpendicular distance of from 15 to 35 cm above the substrate face being coated.
Claim 19
Dependent Claim
22 words
A process according to claim 1 or 2, characterised in that the droplets are droplets of a solution of a metal salt.
Claim 20
Dependent Claim
30 words
A process according to claim 18, characterised in that the droplets are droplets of a solution of a metal chloride from which a metal oxide coating forms on the substrate.
Claim 21
Dependent Claim
16 words
A process according to claim 19, characterised in that said solution is a tin chloride solution.
Claim 22
Dependent Claim
49 words
A process according to claim 1 or 2, further comprising creating suction forces in exhaust ducting to draw gases environmental to the droplet stream away from said stream in the same direction parallel to the forward direction over the substrate as that in which said gas current is discharged.
Claim 23
Dependent Claim
26 words
A process according to claim 1 or 2, characterised in that said at least one current of pre-heated gas is continuously discharged from a stationary orifice.
Claim 24
Dependent Claim
25 words
A process according to claim 1, characterised in that the substrate is a continuous ribbon of flat glass travelling from a flat glass forming plant.
Claim 25
Dependent Claim
22 words
A process according to claim 23, characterised in that the substrate is a ribbon of float glass travelling from a float tank.
Claim 26
Dependent Claim
43 words
A process according to claim 23 or 24, characterised in that at least one said droplet stream impinges on the top face of the ribbon at a position where the temperature of the glass is within the range of 650° to 100° C.
References Cited (Backward Citations)
GB1516032A
Cited
GB1523991A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-09-13 | 1986-03-15 | 1986-09-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-09-13 | 1990-03-15 | 1990-09-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-09-13 | 1994-03-15 | 1994-09-14 | $7700.00 | Window Closed / Lapsed |