Assignee: Penn Specialty Chemicals Inc
•
Filing: 1980-10-06
•
Granted: 1982-09-07
•
Expires: 2000-10-06
Abstract
Abstract A method and composition for forming a dry free-flowing particulate solid is disclosed which utilizes a novel binder system for bonding particles of carbon, sand and/or other solid particulate materials. The solid, non-sticky binder system comprises furfural, solid resin, (such as a phenolic resin), which is not sticky at room temperature and is soluble in furfural, and a liquid amine having free hydrogens on the amine nitrogen which amine is capable of reacting with furfural. This system is capable of adhering to such particles while retaining the free-flowing characteristics of the particles. The free-flowing particulate solid thus formed may be shaped, extruded or compression molded as necessary to form the desired article. A shaped mass of this particulate material is converted to an integral mass by warming or compressing. While the binder is curable at room temperature over a long period of time, the cure rate may be accelerated by increases in temperature. Carbonization of the resin system yields a high carbon residue.
Inventors
- 👤 Denis W. Akerberg
- 👤 George W. Huffman
- 👤 Carl A. Rude
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 00:56
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/528; C04B35/532; B; B22; B22C; B22C1/00; B22C1/16; B22C1/20; B22C1/22; B22C1/2233; B22C1/224; C04B35/01; C04B35/013; C04B35/56; C04B35/565; C08; C08G; C08G8/00; C08G8/04; C08G8/06; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
93 words
A method for forming shapes comprising the steps of a. mixing particles of a solid particulate material and a liquid amine capable of reacting with furfural into a substantially uniform blend; b. mixing at room temperature said blend from step (a) with a resin system comprising a phenolic novolak resin dissolved in furfural; c. continuing mixing until a free-flowing dry particulate solid results, and d. forming said particulate solid into a desired shape whereby shapes of refractory material with satisfactory green strength are formed, said shapes being capable of being baked and carbonized.
Claim 2
Independent Claim
93 words
A method for forming shapes comprising the steps of a. mixing particles of a solid particulate material and a liquid amine capable of reacting with furfural into a substantially uniform blend; b. mixing at room temperature said blend from step (a) with a resin system comprising a phenolic novolak resin dissolved in furfural; c. continuing mixing until a free-flowing dry particulate solid results, and d. forming said particulate solid into a desired shape whereby shapes of refractory material with satisfactory green strength are formed, said shapes being capable of being baked and carbonized.
Claim 3
Dependent Claim
28 words
The method of claim 1 wherein said liquid amine is a liquid aliphatic amine having free hydrogens on the amine nitrogen and a boiling point of 150° C.
Claim 4
Dependent Claim
11 words
The method of claim 1 wherein said liquid amine is triethylenetetramine.
Claim 5
Dependent Claim
12 words
The method of claim 1 wherein said solid particulate material is carbon.
Claim 6
Dependent Claim
16 words
The method of claim 4 wherein said free-flowing particulate solid is extruded into a carbon rod.
Claim 7
Dependent Claim
22 words
The method of claim 4 wherein said free-flowing particulate solid is compression molded into blocks for use as a cupola melt ingredient.
Claim 8
Dependent Claim
13 words
The method of claim 1 wherein said solid particulate material is silicon carbide.
Claim 9
Dependent Claim
25 words
The method of claim 7 wherein said free-flowing particulate solid is formed into a crucible shape in a shaping mold and thereafter baked and carbonized.
Claim 10
Dependent Claim
16 words
The method of claim 1 wherein said solid particulate material includes calcined dead-burned basic refractory material.
Claim 11
Dependent Claim
20 words
The method of claim 9 wherein said solid particulate material is compression molded under heat to form a refractory brick.
Claim 12
Dependent Claim
12 words
The method of claim 1 wherein said solid particulate material includes sand.
Claim 13
Dependent Claim
33 words
The method of claim 11 wherein a surplus quantity of said free-flowing particulate solid is placed against a heated mold pattern for a sufficient time to produce a shell mold of desired thickness.
Claim 14
Independent Claim
86 words
A method for forming carbon rods by extrusion, comprising the steps of a. mixing carbon particles and a liquid amine capable of reacting with furfural into a substantially uniform blend; b. mixing a phenolic novolak dissolved in furfural with said blend until a free-flowing dry solid results; c. placing said dry solid into an extruder; d. extruding said dry solid to form carbon rods of good green strength; e. cutting said green carbon rods, and f. baking and carbonizing said carbon rods under a reducing atmosphere.
Claim 15
Independent Claim
86 words
A method for forming carbon rods by extrusion, comprising the steps of a. mixing carbon particles and a liquid amine capable of reacting with furfural into a substantially uniform blend; b. mixing a phenolic novolak dissolved in furfural with said blend until a free-flowing dry solid results; c. placing said dry solid into an extruder; d. extruding said dry solid to form carbon rods of good green strength; e. cutting said green carbon rods, and f. baking and carbonizing said carbon rods under a reducing atmosphere.
Claim 16
Dependent Claim
10 words
The method of claim 13 wherein said amine is triethylenetetramine.
Claim 17
Dependent Claim
45 words
The method of claim 13 wherein said baking and carbonizing includes the steps of placing said green carbon rods into a furnace and raising the temperature of said furnace in a programmed manner to 650° C. under a reducing atmosphere and holding at that temperature.
Claim 18
Independent Claim
138 words
A method of manufacturing a composition consisting of free-flowing non-sticky particulate solids capable of being shaped and integrated into a unitary mass, said method comprising steps of a. preparing a furfural solution of a phenolic novolak said furfural being present in an amount sufficient to provide a viscosity of the resulting solution sufficiently low to uniformly distribute the solution on particulate solid material; and b. admixing the resulting solution with a mixture of particulate solid material and an amine, said amine being capable of reacting with furfural to produce a solid, said amine having free hydrogens on the amine nitrogen; said amine being used in an amount sufficient to convert the furfural resin solution into an uncured solid, said mixing taking place at temperatures not exceeding 50° C., continuing the mixing until a free-flowing dry particulate solid results.
Claim 19
Independent Claim
138 words
A method of manufacturing a composition consisting of free-flowing non-sticky particulate solids capable of being shaped and integrated into a unitary mass, said method comprising steps of a. preparing a furfural solution of a phenolic novolak said furfural being present in an amount sufficient to provide a viscosity of the resulting solution sufficiently low to uniformly distribute the solution on particulate solid material; and b. admixing the resulting solution with a mixture of particulate solid material and an amine, said amine being capable of reacting with furfural to produce a solid, said amine having free hydrogens on the amine nitrogen; said amine being used in an amount sufficient to convert the furfural resin solution into an uncured solid, said mixing taking place at temperatures not exceeding 50° C., continuing the mixing until a free-flowing dry particulate solid results.
Claim 20
Dependent Claim
10 words
The method of claim 16 wherein the amine is triethylenetetramine.
Claim 21
Dependent Claim
12 words
The method of claim 16 wherein the particulate solid material comprises carbon.
Claim 22
Dependent Claim
11 words
The method of claim 16 wherein the particulate material includes sand.
Claim 23
Dependent Claim
16 words
The method of claim 16 in which the particulate material includes calcined dead-burned basic refractory material.
References Cited (Backward Citations)
US3377189A
Cited
US3947420A
Cited
US4064331A
Cited
US4051301A
Cited
US4108826A
Cited
US4182696A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-09-06 | 1986-03-08 | 1986-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-09-06 | 1990-03-08 | 1990-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-09-06 | 1994-03-08 | 1994-09-07 | $7700.00 | Window Closed / Lapsed |