Welded structure having improved mechanical strength and process for making same
Assignee: Hitachi Ltd
•
Filing: 1980-05-06
•
Granted: 1982-09-07
•
Expires: 2000-05-06
Abstract
Abstract A welded structure and a method for making same wherein a plurality of weld metals, such as martensitic steel and austenitic steel, differing in coefficient of thermal expansion from each other are deposited in a plurality of layers thicknesswise of the welded structure in a gap defined by structural members to be welded in such a manner that a layer of the weld metal of higher coefficient of thermal expansion is covered by a layer of the weld metal of lower coefficient of thermal expansion in a weld formed, to improve brittle fracture strength, fatigue strength and stress corrosion cracking resistance of the weld. By subjecting the welded structure to stress relief annealing treatment, it is possible to produce compressive stress on the surface of the layer of the weld metal of lower coefficient of thermal expansion.
Inventors
- 👤 Shizuka Shimanuki
- 👤 Toshimi Matsumoto
- 👤 Hiroshi Sato
- 👤 Tsutomu Onuma
- 👤 Seishin Kirihara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 19:55
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/50; B; B23; B23K; B23K9/00; B23K9/23; C21D2251/00; Y; Y10; Y10T; Y10T403/00; Y10T403/21
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
231 words
A welded structure with compressive stress on the surface of its weld produced by stress relief annealing treatment, comprising: structural members welded by at least one weld joint into said welded structure and thereafter annealed; a plurality of weld metals deposited on said structural members in a zone defining said weld joint of said welded structure in such a manner that the weld metals are restrained by the structural members; said plurality of weld metals comprising a first weld metal having a first coefficient of thermal expansion forming at least one layer and a second weld metal having a second coefficient of thermal expansion higher than said first coefficient of thermal expansion forming at least a second layer, said first weld metal and said second weld metal being contiguous to each other and fused into the welded portion of said welded structure to provide a metallurgical bond, the layer of said first weld metal having an exposed surface; said coefficient of thermal expansion of said first weld metal layer being lower than that of said second weld metal layer by over 1×10 -6 /°C.; and the ratio of the thickness, as measured perpendicular to said surface, of said second weld metal to the thickness of said weld joint and the difference between said first and second coefficient of thermal expansion being sufficient that said exposed surface has compressive stress after annealing.
Claim 2
Dependent Claim
231 words
A welded structure with compressive stress on the surface of its weld produced by stress relief annealing treatment, comprising: structural members welded by at least one weld joint into said welded structure and thereafter annealed; a plurality of weld metals deposited on said structural members in a zone defining said weld joint of said welded structure in such a manner that the weld metals are restrained by the structural members; said plurality of weld metals comprising a first weld metal having a first coefficient of thermal expansion forming at least one layer and a second weld metal having a second coefficient of thermal expansion higher than said first coefficient of thermal expansion forming at least a second layer, said first weld metal and said second weld metal being contiguous to each other and fused into the welded portion of said welded structure to provide a metallurgical bond, the layer of said first weld metal having an exposed surface; said coefficient of thermal expansion of said first weld metal layer being lower than that of said second weld metal layer by over 1×10 -6 /°C.; and the ratio of the thickness, as measured perpendicular to said surface, of said second weld metal to the thickness of said weld joint and the difference between said first and second coefficient of thermal expansion being sufficient that said exposed surface has compressive stress after annealing.
Claim 3
Dependent Claim
16 words
A welded structure as claimed in claim 1, wherein said welded portion comprises a butt weld.
Claim 4
Dependent Claim
27 words
A welded structure as claimed in claim 2, wherein said butt weld is one of the group of types including I-, U-, V-, K-, X- and Y-types.
Claim 5
Dependent Claim
32 words
A welded structure as claimed in claim 1, wherein said welded portion comprises at least one of the group of materials consisting of low alloy steel, carbon steel and high alloy steel.
Claim 6
Dependent Claim
22 words
A welded structure as claimed in claim 1, wherein said first weld metal is substantially the same material as said welded portion.
Claim 7
Dependent Claim
151 words
A welded structure comprising: structural members welded by at least one weld joint into said welded structure; and a plurality of weld metals deposited in a gap defining said weld joint of said welded structure for butt welding comprising a first weld metal forming at least one layer, and a second weld metal of higher coefficient of thermal expansion than said first weld metal forming at least a second layer, said first and second weld metal layers being metallurgically bonded together and fused into said structural members in said gap defined therebetween to provide a metallurgical bond in such a manner that the weld metals are restrained in said gap, said first weld metal layer having an exposed surface having compressive stress present thereof, and said coefficient of thermal expansion of said first weld metal layer being lower than that of said second weld metal layer by over 1×10 -6 /°C.
Claim 8
Dependent Claim
151 words
A welded structure comprising: structural members welded by at least one weld joint into said welded structure; and a plurality of weld metals deposited in a gap defining said weld joint of said welded structure for butt welding comprising a first weld metal forming at least one layer, and a second weld metal of higher coefficient of thermal expansion than said first weld metal forming at least a second layer, said first and second weld metal layers being metallurgically bonded together and fused into said structural members in said gap defined therebetween to provide a metallurgical bond in such a manner that the weld metals are restrained in said gap, said first weld metal layer having an exposed surface having compressive stress present thereof, and said coefficient of thermal expansion of said first weld metal layer being lower than that of said second weld metal layer by over 1×10 -6 /°C.
Claim 9
Dependent Claim
22 words
A welded structure as claimed in claim 6 wherein said first weld metal is substantially the same material as said structural members.
Claim 10
Dependent Claim
151 words
A welded structure comprising: structural members of alloy steel welded by at least one weld joint into said weld structure; and a plurality of weld metals deposited in a gap defining said weld joint of said welded structure to form a butt weld of symmetrical configuration comprising a first weld metal forming at least one layer, and a second weld metal higher in coefficient of thermal expansion than said first weld metal by over 1×10 -6 /°C. forming at least a second layer, said first and second weld metal layers being metallurgically bonded together and fused into said structural members in said gap defined therebetween to provide a metallurgical bond in the form of said butt weld in such a manner that said first weld metal and said second weld metal are restrained by said welded portion, said first weld metal layer including an exposed surface having compressive stress present thereon.
Claim 11
Dependent Claim
151 words
A welded structure comprising: structural members of alloy steel welded by at least one weld joint into said weld structure; and a plurality of weld metals deposited in a gap defining said weld joint of said welded structure to form a butt weld of symmetrical configuration comprising a first weld metal forming at least one layer, and a second weld metal higher in coefficient of thermal expansion than said first weld metal by over 1×10 -6 /°C. forming at least a second layer, said first and second weld metal layers being metallurgically bonded together and fused into said structural members in said gap defined therebetween to provide a metallurgical bond in the form of said butt weld in such a manner that said first weld metal and said second weld metal are restrained by said welded portion, said first weld metal layer including an exposed surface having compressive stress present thereon.
Claim 12
Dependent Claim
37 words
A welded structure as claimed in claim 6 or 8, wherein the coefficient of thermal expansion of said first weld metal layer is lower than that of said second weld metal layer by over 2×10 -6 /°C.
Claim 13
Independent Claim
101 words
A method for making a welded structure comprising the steps of: depositing a first weld metal and a second weld metal in contiguous layers in a gap defined by structural members to be welded into said welded structure in such a manner that a layer of said first weld metal has an exposed surface in said welded structure, said first weld metal having a lower coefficient of thermal expansion than said second weld metal by over 1×10 -6 /°C.; and subjecting said welded structure to stress relief annealing treatment to produce compressive stress on the exposed surface of said weld metal.
Claim 14
Independent Claim
101 words
A method for making a welded structure comprising the steps of: depositing a first weld metal and a second weld metal in contiguous layers in a gap defined by structural members to be welded into said welded structure in such a manner that a layer of said first weld metal has an exposed surface in said welded structure, said first weld metal having a lower coefficient of thermal expansion than said second weld metal by over 1×10 -6 /°C.; and subjecting said welded structure to stress relief annealing treatment to produce compressive stress on the exposed surface of said weld metal.
Claim 15
Independent Claim
110 words
A method for making a welded structure comprising the steps of: depositing a first weld metal and a second weld metal in contiguous layers in a gap defined by structural members to be welded into said welded structure in such a manner that a layer of said first weld metal has an exposed surface in said welded structure, said first weld metal having a lower coefficient of thermal expansion than said second weld metal by over 1×10 -6 /°C.; and subjecting said welded structure to stress relief annealing treatment by means of keeping it at the transformation point of the material forming the welded portion and thereafter slowly cooling it.
Claim 16
Independent Claim
110 words
A method for making a welded structure comprising the steps of: depositing a first weld metal and a second weld metal in contiguous layers in a gap defined by structural members to be welded into said welded structure in such a manner that a layer of said first weld metal has an exposed surface in said welded structure, said first weld metal having a lower coefficient of thermal expansion than said second weld metal by over 1×10 -6 /°C.; and subjecting said welded structure to stress relief annealing treatment by means of keeping it at the transformation point of the material forming the welded portion and thereafter slowly cooling it.
Claim 17
Independent Claim
183 words
A method for forming a welded structure suitable for producing compressive stress on the surface of its weld by stress release annealing treatment comprising: providing structural members to be welded into said welded structure; and depositing a plurality of weld metals on said structural members in a zone defined by a welded portion of said welded structure in such a manner that the weld metals are restrained by the welded portion; characterized in that: said depositing provides said plurality of weld metals to comprise a first weld metal of lower coefficient of thermal expansion forming at least one layer and a second weld metal of higher coefficient of thermal expansion forming at least one layer, with said first weld metal and said second weld metal being contiguous to each other and fused into the welded portion of said welded structure to provide a metallurgical bond, the layer of said first weld metal having an exposed surface, and said coefficient of thermal expansion of said first weld metal layer being lower than that of said second weld metal layer by over 1×10 -6 /°C.
Claim 18
Independent Claim
183 words
A method for forming a welded structure suitable for producing compressive stress on the surface of its weld by stress release annealing treatment comprising: providing structural members to be welded into said welded structure; and depositing a plurality of weld metals on said structural members in a zone defined by a welded portion of said welded structure in such a manner that the weld metals are restrained by the welded portion; characterized in that: said depositing provides said plurality of weld metals to comprise a first weld metal of lower coefficient of thermal expansion forming at least one layer and a second weld metal of higher coefficient of thermal expansion forming at least one layer, with said first weld metal and said second weld metal being contiguous to each other and fused into the welded portion of said welded structure to provide a metallurgical bond, the layer of said first weld metal having an exposed surface, and said coefficient of thermal expansion of said first weld metal layer being lower than that of said second weld metal layer by over 1×10 -6 /°C.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-09-06 | 1986-03-08 | 1986-09-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-09-06 | 1990-03-08 | 1990-09-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-09-06 | 1994-03-08 | 1994-09-07 | $7700.00 | Window Closed / Lapsed |