Electrodes of vacuum circuit breaker
Assignee: Hitachi Ltd
•
Filing: 1979-07-30
•
Granted: 1982-08-31
•
Expires: 1999-07-30
Abstract
Abstract An electrode of a vacuum circuit breaker, having a high dielectric strength, large breaking current and superior non-welding characteristic. The electrode is made of a cast alloy comprising copper, 20 wt% or less of rare earth metal such as lanthanum, cerium or an alloy of either one of these rare earth metal with another rare earth metal, 10 wt% or less of a metal such as lead and bismuth having a lower melting point and a higher vapor pressure than copper, and 0.1 to 30 wt% of a metal of iron group. A part of the rare earth metal and a part of the metal having the lower melting point and higher vapor pressure than copper are crystallized in the grain boundary and in the grains of copper.
Inventors
- 👤 Ryuji Watanabe
- 👤 Keiichi Kuniya
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 23:44
CPC Classifications
C; C22; C22C; C22C9/00; H; H01; H01H; H01H1/00; H01H1/02; H01H1/0203
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
85 words
An electrode for a vacuum circuit breaker made of a cast alloy consisting essentially of copper, about 0.1 to 20 wt % of a rare earth metal and about 0.01 to 10 wt % of a metal having a lower melting point and a higher vapor pressure than copper, wherein a part of said rare earth metal and a part of said metal having lower melting point and higher vapor pressure than copper are crystallized in the grain boundary or in the grains of copper.
Claim 2
Dependent Claim
85 words
An electrode for a vacuum circuit breaker made of a cast alloy consisting essentially of copper, about 0.1 to 20 wt % of a rare earth metal and about 0.01 to 10 wt % of a metal having a lower melting point and a higher vapor pressure than copper, wherein a part of said rare earth metal and a part of said metal having lower melting point and higher vapor pressure than copper are crystallized in the grain boundary or in the grains of copper.
Claim 3
Dependent Claim
47 words
An electrode of a vacuum circuit breaker as claimed in claim 1, wherein said rare earth metal is one or more of metals selected from a group consisting of lanthanum, cerium and a mixture alloy of at least one of these metals and another rare earth metal.
Claim 4
Dependent Claim
38 words
An electrode of a vacuum circuit breaker as claimed in claim 1, wherein said metal having lower melting point and higher vapor pressure than Cu is constituted by at least one selected from lead, bismuth and their alloy.
Claim 5
Dependent Claim
26 words
An electrode of a vacuum circuit breaker as claimed in claim 2, wherein the content of said rare earth metal is 1 to 5 wt %.
Claim 6
Dependent Claim
32 words
An electrode of a vacuum circuit breaker as claimed in claim 3, wherein the content of at least one of said lead, bismuth and their alloys is 0.1 to 7 wt %.
Claim 7
Dependent Claim
46 words
An electrode of a vacuum circuit breaker as claimed in claim 1, wherein a part of said rare earth metal and a part of said metal having a lower melting point and a higher vapor pressure than copper are crystallized in a granular or spheroidized form.
Claim 8
Dependent Claim
27 words
An electrode of a vacuum circuit breaker as claimed in claim 1, wherein said cast alloy has been casted by water-cooled casting method or pressure casting method.
Claim 9
Dependent Claim
97 words
An electrode of a vacuum circuit breaker made of a cast alloy consisting essentially of copper, about 0.1 to 20 wt % of a rare earth metal, about 0.01 to 10 wt % of a metal having a lower melting point and a higher vapor pressure than copper, and 0.1 to 30 wt % of a metal of iron group, wherein a part of said rare earth metal and a part of said metal having a lower melting point and higher vapor pressure than copper are crystallized in the grain boundary and in the grains of copper.
Claim 10
Dependent Claim
97 words
An electrode of a vacuum circuit breaker made of a cast alloy consisting essentially of copper, about 0.1 to 20 wt % of a rare earth metal, about 0.01 to 10 wt % of a metal having a lower melting point and a higher vapor pressure than copper, and 0.1 to 30 wt % of a metal of iron group, wherein a part of said rare earth metal and a part of said metal having a lower melting point and higher vapor pressure than copper are crystallized in the grain boundary and in the grains of copper.
Claim 11
Dependent Claim
26 words
An electrode of a vacuum circuit breaker as claimed in claim 8, wherein said metal of iron group is at least one of iron and cobalt.
Claim 12
Dependent Claim
34 words
An electrode of a vacuum circuit breaker as claimed in claim 9, wherein said cast alloy contains at least one of iron and cobalt by an amount in excess of its solid solubility limit.
Claim 13
Dependent Claim
41 words
An electrode of a vacuum circuit breaker as claimed in claim 8, wherein said rare earth metal is constituted by at least one of lanthanum, cerium and mixture alloys of at least one of these metals with another rare earth metal.
Claim 14
Dependent Claim
39 words
An electrode of a vacuum circuit breaker as claimed in claim 8, wherein said metal having a lower melting point and a higher vapor pressure than copper is constituted by at least one of lead, bismuth and their alloys.
Claim 15
Dependent Claim
47 words
An electrode of a vacuum circuit breaker as in claim 1 or 8, wherein said metal having a lower melting point and a higher vapor pressure than copper is at least one metal selected from the group consisting of lead, bismuth, thallium, indium, selenium, cadmium and tellurium.
Claim 16
Dependent Claim
37 words
An electrode of a vacuum circuit breaker as in claim 1, wherein said cast alloy consists of copper, a rare earth metal, and a metal having a lower melting point and a higher vapor pressure than copper.
Claim 17
Dependent Claim
42 words
An electrode of a vacuum circuit breaker as in claim 8, wherein said cast alloy consists of copper, a rare earth metal, a metal having a lower melting point and a higher vapor pressure than copper, and a metal of iron group.
References Cited (Backward Citations)
DE1074120B
Cited
US3014110A
Cited
US3551622A
Cited
GB1194674A
Cited
US3502465A
Cited
US3783213A
Cited
US4091248A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |