Process for the production of ethylene graft copolymers containing anhydride or carboxyl groups
Assignee: Bayer AG
•
Filing: 1981-08-24
•
Granted: 1982-08-31
•
Expires: 2001-08-24
Abstract
Abstract A process for the production of ethylene graft copolymers containing anhydride or carboxyl groups in homogeneous or heterogeneous phase in tert.-butanol or methylene chloride wherein (A) from 5 to 70% by weight of a monomer mixture of: (a) from 10 to 80% by weight of a vinyl ester of an aliphatic C 1 -C 18 -monocarboxylic acid; and (b) from 90 to 30% by weight of maleic acid anhydride and/or its C 1 -C 20 -alkyl semiesters; are radically polymerized in the presence of (B) from 95 to 30% by weight of an ethylene homopolymer or an ethylene/vinyl ester copolymer as the graft substrate.
Inventors
- 👤 Herbert Bartl
- 👤 Klaus Schuster
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 15:46
CPC Classifications
C; C08; C08F; C08F263/00; C08F263/02; C08F255/00; C08F255/02
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
155 words
A process for the production of ethylene graft copolymers containing anhydride or carboxyl groups in homogeneous or heterogeneous phase in an organic solvent, wherein (A) from 5 to 70% by weight of a monomer mixture of: (a) from 10 to 70% by weight of a vinyl ester of an aliphatic C 1 -C 18 -monocarboxylic acid; and (b) from 90 to 30% by weight of maleic acid anhydride, its C 1 -C 20 -alkyl semiesters or mixtures thereof; are radically polymerised in the presence of (B) from 95 to 30% by weight of an ethylene homopolymer or an ethylene/vinyl ester copolymer containing from 5 to 70% by weight of copolymerised units of a vinyl ester of an aliphatic C 1 -C 18 -monocarboxylic acid as the graft substrate in tert.-butanol or methylene chloride, the sum total of (A) and (B) and the sum total of (a) and (b) each a mounting to 100% by weight.
Claim 2
Dependent Claim
155 words
A process for the production of ethylene graft copolymers containing anhydride or carboxyl groups in homogeneous or heterogeneous phase in an organic solvent, wherein (A) from 5 to 70% by weight of a monomer mixture of: (a) from 10 to 70% by weight of a vinyl ester of an aliphatic C 1 -C 18 -monocarboxylic acid; and (b) from 90 to 30% by weight of maleic acid anhydride, its C 1 -C 20 -alkyl semiesters or mixtures thereof; are radically polymerised in the presence of (B) from 95 to 30% by weight of an ethylene homopolymer or an ethylene/vinyl ester copolymer containing from 5 to 70% by weight of copolymerised units of a vinyl ester of an aliphatic C 1 -C 18 -monocarboxylic acid as the graft substrate in tert.-butanol or methylene chloride, the sum total of (A) and (B) and the sum total of (a) and (b) each a mounting to 100% by weight.
Claim 3
Dependent Claim
27 words
A process as claimed in claim 1, wherein the vinyl ester in the monomer mixture A, in the graft substrate B or in both is vinyl acetate.
Claim 4
Dependent Claim
59 words
A process as claimed in claim 1 or 2, wherein, in a first step, the ethylene homopolymer or copolymer used as the graft substrate B is produced in known manner and, in a second step, the monomer mixture A to be grafted on is added to the resulting reaction mixture without isolation of the graft substrate, and radically polymerised.
Claim 5
Dependent Claim
50 words
A process as claimed in claim 3, wherein the graft substrate is produced under pressures above 1000 bars, after which the ethylene pressure is reduced to below 400 bars and the graft polymerisation reaction is carried out after the addition of methylene chloride and monomer mixture to be grafted on.
Claim 6
Dependent Claim
79 words
A process as claimed in claim 3, wherein, in the first step for preparing the graft substrate, ethylene and vinyl ester are copolymerised in tert.-butanol, residual ethylene is largely removed by reducing the pressure after a conversion of at least 20% of the monomers has been reached and, in the second step, maleic acid anhydride, its semiesters or a mixture thereof is added to the reaction mixture obtained which is then radically polymerised together with the remaining vinyl ester.
Claim 7
Dependent Claim
54 words
A process as claimed in claim 1 or 2, wherein vinyl esters and maleic acid anhydride are used as the graft monomer and the anhydride groups in the graft copolymer are subsequently reacted with C 1 -C 20 -alkyl alcohols, ammonia or C 1 -C 20 -alkyl amines to form semiester or semiamide groups.
Claim 8
Dependent Claim
35 words
A process as claimed in claim 3, wherein the monomer mixture (a) to be grafted on is added to the resulting reaction mixture without isolation of the graft substrate and after reduction of unreacted ethylene.
References Cited (Backward Citations)
US3949019A
Cited
US4157362A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |