US4347332A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Polyamide/polyethylene copolymer film and method for producing
Assignee: Pechiney Plastic Packaging Inc
•
Filing: 1981-04-01
•
Granted: 1982-08-31
•
Expires: 2001-04-01
Abstract
Abstract A blend of nylon and ethylene vinyl alcohol copolymer is provided which is suitable for conversion into films having desirable levels of strength and toughness, and good oxygen barrier properties. In addition, the blend exhibits enhanced adhesive qualities, as compared to films of EVOH copolymer per se, thus better adapting it for use in multilayer films. Methods for fabricating the resin blend into bare and composite films are also provided.
Inventors
- 👤 Thomas W. Odorzynski
- 👤 II Jack E. Knott
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 18:38
CPC Classifications
B; B32; B32B; B32B27/00; B32B27/34; B32B27/06; B32B27/08; B32B27/18; B32B27/22; B32B27/30; B32B27/306; B32B7/00; B32B7/04; B32B7/12; C; C08; C08J; C08J5/00; C08J5/18; C08L; C08L29/00; C08L29/02; C08L29/04; C08L77/00; B32B2270/00; B32B2307/00; B32B2307/70; B32B2307/724; B32B2307/7242; B32B2307/7244; C08J2377/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31725
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
198 words
In a method for the production of a film having relatively high levels of strength and toughness and good oxygen barrier properties, the steps comprising: a. forming a blend of about 90 to 20 weight percent of a film-forming polyamide resin having a molecular weight of about 20,000 to 30,000 and a melting point temperature of about 415 degrees to 440 degrees Fahrenheit, conversely about 10 to 80 weight percent of an ethylene vinyl alcohol copolymer having a molecular weight of about 15,000 to 30,000 and a melting point temperature of about 325 degrees to 375 degrees Fahrenheit, and about 2 to 25 percent, based upon the weight of said polyamide resin, of a plasticizer therefor, said plasticizer being effective to lower the processing temperature of said polyamide resin to a value approximately that of said copolymer and below the temperature at which any sustantial amount of degradation would occur therein under appropriate conditions for extrusion; b. heating said blend to said processing temperature; c. forcing said blend through an extrusion die to produce a film of said blend; and d. cooling said film to obtain a product having such desirable levels of toughness and oxygen barrier capability.
Claim 2
Dependent Claim
198 words
In a method for the production of a film having relatively high levels of strength and toughness and good oxygen barrier properties, the steps comprising: a. forming a blend of about 90 to 20 weight percent of a film-forming polyamide resin having a molecular weight of about 20,000 to 30,000 and a melting point temperature of about 415 degrees to 440 degrees Fahrenheit, conversely about 10 to 80 weight percent of an ethylene vinyl alcohol copolymer having a molecular weight of about 15,000 to 30,000 and a melting point temperature of about 325 degrees to 375 degrees Fahrenheit, and about 2 to 25 percent, based upon the weight of said polyamide resin, of a plasticizer therefor, said plasticizer being effective to lower the processing temperature of said polyamide resin to a value approximately that of said copolymer and below the temperature at which any sustantial amount of degradation would occur therein under appropriate conditions for extrusion; b. heating said blend to said processing temperature; c. forcing said blend through an extrusion die to produce a film of said blend; and d. cooling said film to obtain a product having such desirable levels of toughness and oxygen barrier capability.
Claim 3
Dependent Claim
17 words
The method of claim 1 wherein said processing temperature is in excess of about 400 degrees Fahrenheit.
Claim 4
Dependent Claim
17 words
The method of claim 2 wherein said processing temperature is about 430 degrees to 480 degrees Fahrenheit.
Claim 5
Dependent Claim
41 words
The method of claim 2 wherein said plasticizer is selected from the group consisting of fatty acid amides, aromatic sulfonamides and polyamides having a molecular weight of about 5,000 to 25,000 and a melting point temperature below about 400 degrees Fahrenheit.
Claim 6
Dependent Claim
26 words
The method of claim 4 wherein said plasticizer is selected from the class consisting of lauramide, o,p-toluenesulfonamide, N-ethyl-o,p-toluenesulfonamide and polyamides of 7,000 to 10,000 molecular weight.
Claim 7
Dependent Claim
26 words
The method of claim 1 including the additional step of compounding said film-forming polyamide resin and said plasticizer prior to said step of forming said blend.
Claim 8
Dependent Claim
72 words
The method of claim 1 including the additional step of introducing into said extruder a second resin having a composition different from that of said blend, said second resin being combined with said blend in said die to produce a laminar structure of plural layers, and said structure being extruded from said die as a multilayer film including one layer comprised of said blend and a second layer comprised of said resin.
Claim 9
Dependent Claim
35 words
The method of claim 7 wherein said resin is selected from the group consisting of ionomer resins, partially hydrolyzed ethylene vinyl acetate copolymer adhesive, anhydride modified polyolefin adhesives, and ethylene organic acid ester copolymer compositions.
Claim 10
Dependent Claim
15 words
The film produced in accordance with any one of claims 1, 3, 5 or 8.
References Cited (Backward Citations)
US3882259A
Cited
US4064296A
Cited
US4243074A
Cited
US4243724A
Cited
US4261482A
Cited
US4240993A
Cited
US4239826A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |