Corrosion resistant coated articles which include an intermediate coating layer of a thermosetting polymer and non-siliceous filler
Assignee: Sandoz AG
•
Filing: 1980-08-14
•
Granted: 1982-08-31
•
Expires: 2000-08-14
Abstract
Abstract A concrete or metal substrate which is normally subject to deterioration in the presence of corrosive substances such as strong acids, particularly sulfuric acid, is rendered corrosion resistant when covered with the improved multilayered coating of this invention. In particular, a coated article, such as a coated chimney liner or flue duct, which includes a substrate, a primer coating layer of a thermosetting polymer, one or more inner coating layers of a thermosetting polymer which includes a siliceous filler, an intermediate coating layer of a thermosetting polymer which includes a non-siliceous filler, and a fluoroelastomeric top coating layer which includes a non-siliceous filler, has improved resistance to the corrosive effects of strong acids. Chimney liners, flue ducts, scrubbers, and the like which have been coated in accordance with this invention are useful in power plants, smelters, and other industrial settings where corrosive environments are present.
Inventors
- 👤 William R. Slama
- 👤 Robert B. Washburn
- 👤 Dale J. Semanisin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:47
CPC Classifications
F; F16; F16L; F16L58/00; F16L58/02; F16L58/04; F16L58/10; B; B05; B05D; B05D7/00; B05D7/14; B05D7/50; B05D7/56; B05D7/58; B05D2202/00; B05D5/00; B05D5/08; B05D5/083; B05D7/22; B05D7/222; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/31504; Y10T428/3154; Y10T428/31544; Y10T428/31551; Y10T428/31565; Y10T428/31605; Y10T428/31678; Y10T428/31681; Y10T428/31692; Y10T428/31786; Y10T428/31797; Y10T428/31855
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
164 words
A coated article resistant to corrosion or deterioration which comprises: a substrate; a primer coating layer in contact with the surface of said substrate, said primer coating layer being a thermosetting polymeric material and having a thickness from about 1 to about 5 mils; an inner coating layer in bonded contact with said primer coating layer, said inner coating layer being an admixture of a thermosetting polymeric material and a siliceous filler material and having a thickness from about 20 to about 80 mils; an intermediate coating layer in bonded contact with said inner coating layer, said intermediate coating layer being an admixture of a thermosetting polymeric material and a non-siliceous filler material and having a thickness from about 10 to about 15 mils; and an outer coating layer in chemically bonded contact with said intermediate coating layer, said outer coating layer being an admixture of a fluoroelastomer and a non-siliceous filler material and having a thickness from about 10 to about 50 mils.
Claim 2
Dependent Claim
164 words
A coated article resistant to corrosion or deterioration which comprises: a substrate; a primer coating layer in contact with the surface of said substrate, said primer coating layer being a thermosetting polymeric material and having a thickness from about 1 to about 5 mils; an inner coating layer in bonded contact with said primer coating layer, said inner coating layer being an admixture of a thermosetting polymeric material and a siliceous filler material and having a thickness from about 20 to about 80 mils; an intermediate coating layer in bonded contact with said inner coating layer, said intermediate coating layer being an admixture of a thermosetting polymeric material and a non-siliceous filler material and having a thickness from about 10 to about 15 mils; and an outer coating layer in chemically bonded contact with said intermediate coating layer, said outer coating layer being an admixture of a fluoroelastomer and a non-siliceous filler material and having a thickness from about 10 to about 50 mils.
Claim 3
Dependent Claim
19 words
A coated article in accordance with claim 1 wherein said substrate is a chimney liner, flue duct or scrubber.
Claim 4
Dependent Claim
22 words
A coated article in accordance with claim 1 wherein said thermosetting polymeric material is polyester, vinyl ester, epoxy, furan, phenolic or urethane.
Claim 5
Dependent Claim
21 words
A coated article in accordance with claim 1 wherein said siliceous filler is silica, glass wool, glass flakes, or mica flakes.
Claim 6
Dependent Claim
18 words
A coated article in accordance with claim 1 wherein said non-siliceous filler is carbon or an inorganic oxide.
Claim 7
Dependent Claim
21 words
A coated article in accordance with claim 1 wherein said fluoroelastomer has a molecular weight less than about 2×10 5 .
Claim 8
Dependent Claim
23 words
A coated article in accordance with claim 1 wherein said fluoroelastomer is a substantially fully saturated fluorinated copolymer of vinylidene fluoride and hexafluoropropylene.
Claim 9
Dependent Claim
23 words
A coated article in accordance with claim 1 wherein said thermosetting polymeric material of said primer coating layer is polyester or vinyl ester.
Claim 10
Dependent Claim
158 words
A coated article resistant to corrosion or deterioration which comprises: a substrate; a primer coating layer in contact with the surface of said substrate, said primer coating layer being a polyester and having a thickness from about 1 to about 5 mils; an inner coating layer in bonded contact with said primer coating layer, said inner coating layer being a polymer formed from vinyl ester and styrene in admixture with glass flakes and having a thickness from about 20 to about 80 mils; an intermediate coating layer in bonded contact with said inner coating layer, said intermediate coating layer being a polymer formed from vinyl ester and styrene in admixture with carbon and having a thickness from about 10 to about 15 mils; and an outer coating layer in chemically bonded contact with said intermediate layer, said outer coating layer being a fluoroelastomer in admixture with carbon and having a thickness from about 10 to about 50 mils.
Claim 11
Dependent Claim
158 words
A coated article resistant to corrosion or deterioration which comprises: a substrate; a primer coating layer in contact with the surface of said substrate, said primer coating layer being a polyester and having a thickness from about 1 to about 5 mils; an inner coating layer in bonded contact with said primer coating layer, said inner coating layer being a polymer formed from vinyl ester and styrene in admixture with glass flakes and having a thickness from about 20 to about 80 mils; an intermediate coating layer in bonded contact with said inner coating layer, said intermediate coating layer being a polymer formed from vinyl ester and styrene in admixture with carbon and having a thickness from about 10 to about 15 mils; and an outer coating layer in chemically bonded contact with said intermediate layer, said outer coating layer being a fluoroelastomer in admixture with carbon and having a thickness from about 10 to about 50 mils.
Claim 12
Dependent Claim
188 words
A method of preparing a coated article in accordance with claim 1 which comprises: cleaning and roughening the surface of a substrate to be coated; covering said cleaned and roughened surface of said substrate with a primer coating layer, said primer coating layer being a thermosetting polymeric material, to a thickness from about 1 to about 5 mils; covering said primer coating layer with an inner coating layer, said inner coating layer being an admixture of a thermosetting polymeric material and a siliceous filler material to a thickness from about 20 to about 80 mils; covering said inner coating layer with an intermediate coating layer, said intermediate coating layer being an admixture of a thermosetting polymeric material and a non-siliceous filler material to a thickness from about 10 to about 15 mils; applying an outer coating layer over said intermediate coating layer, said outer coating layer being an admixture of a non-siliceous filler material and a fluoroelastomer capable of chemically bonding to said intermediate coating layer, to a thickness from about 10 to about 50 mils; and curing the resulting multiple coating layers to produce said coated article.
Claim 13
Dependent Claim
171 words
A method of preparing a coated article in accordance with claim 9 which comprises: cleaning and roughening the surface of a substrate to be coated; covering said cleaned and roughened surface of said substrate with a primer coating layer of a polyester to a thickness from about 1 to about 5 mils; covering said primer coating layer with an inner coating layer of a polymer formed from vinyl ester and styrene in admixture with glass flakes to a thickness from about 20 to about 80 mils; covering said inner coating layer with an intermediate coating layer of a polymer formed from vinyl ester and styrene in admixture with carbon to a thickness from about 10 to about 15 mils; applying an outer coating layer over said intermediate coating layer, said outer coating layer being an admixture of carbon and a fluoroelastomer capable of chemically bonding to said intermediate layer, to a thickness from about 10 to about 50 mils; and curing the resulting multiple coating layers to produce said coated article.
References Cited (Backward Citations)
US2777783A
Cited
US3093264A
Cited
US2809130A
Cited
US3111426A
Cited
GB1228853A
Cited
US3526532A
Cited
BE763759A
Cited
US3799832A
Cited
US3874903A
Cited
US4154876A
Cited
US4237177A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |