Selective magnetization of rare-earth transition metal alloys
Assignee: Motors Liquidation Co
•
Filing: 1980-04-07
•
Granted: 1982-08-31
•
Expires: 2000-04-07
Abstract
Abstract An amorphous rare-earth transition metal body is provided that has integral, predetermined regions of hard and soft magnetism. A method is provided for heating portions of an amorphous rare-earth transition metal alloy body, in situ, to transform predetermined portions from a state of low magnetic coercivity to a highly magnetically coercive state.
Inventors
- 👤 Andrew R. Chraplyvy
- 👤 Jan F. Herbst
- 👤 John J. Croat
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 21:07
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/0302; H01F1/0306; H01F1/032; H01F1/04; H01F1/047; H01F1/053; H01F1/055
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
72 words
A method of forming an integral region of hard magnetism in a portion of a magnetically soft rare-earth transition metal alloy body comprising forming said alloy body to place it entirely in an amorphous, magnetically soft condition and thereafter selectively tempering the portion of said body in said region to convert the structure of the alloy thereat from an amorphous to a crystalline state such that said region has high magnetic coercivity.
Claim 2
Independent Claim
72 words
A method of forming an integral region of hard magnetism in a portion of a magnetically soft rare-earth transition metal alloy body comprising forming said alloy body to place it entirely in an amorphous, magnetically soft condition and thereafter selectively tempering the portion of said body in said region to convert the structure of the alloy thereat from an amorphous to a crystalline state such that said region has high magnetic coercivity.
Claim 3
Independent Claim
99 words
A method of making a body of rare-earth transition metal alloy having a first amorphous portion that has soft magnet characteristics and an integral second crystalline portion that has hard magnet characteristics comprising: sputtering a mixture of rare-earth and transition metals to form said alloy in an amorphous, soft magnetic state; forming said body from said alloy; and selectively treating the said second portion of the body by heating it to a temperature whereat the alloy thereat is converted to a crystalline form that has high intrinsic magnetic coercivity, the balance of said body remaining in an amorphous state.
Claim 4
Independent Claim
99 words
A method of making a body of rare-earth transition metal alloy having a first amorphous portion that has soft magnet characteristics and an integral second crystalline portion that has hard magnet characteristics comprising: sputtering a mixture of rare-earth and transition metals to form said alloy in an amorphous, soft magnetic state; forming said body from said alloy; and selectively treating the said second portion of the body by heating it to a temperature whereat the alloy thereat is converted to a crystalline form that has high intrinsic magnetic coercivity, the balance of said body remaining in an amorphous state.
Claim 5
Independent Claim
104 words
A method of making a body of PrCo 3 having a first amorphous portion that has soft magnet characteristics and an integral second crystalline portion that has hard magnet characteristics comprising: sputtering praseodymium and cobalt onto a cooled substrate in an atomic ratio of 1:3 to form a PrCo 3 alloy that is amorphous and has soft magnet characteristics; forming said body from said alloy; selectively heating said second portion of said body to a temperature in the range of from about 350°-450° C. such that the amorphous alloy of the portion is is substantially transformed to a crystalline state of high magnetic coercivity.
Claim 6
Independent Claim
104 words
A method of making a body of PrCo 3 having a first amorphous portion that has soft magnet characteristics and an integral second crystalline portion that has hard magnet characteristics comprising: sputtering praseodymium and cobalt onto a cooled substrate in an atomic ratio of 1:3 to form a PrCo 3 alloy that is amorphous and has soft magnet characteristics; forming said body from said alloy; selectively heating said second portion of said body to a temperature in the range of from about 350°-450° C. such that the amorphous alloy of the portion is is substantially transformed to a crystalline state of high magnetic coercivity.
References Cited (Backward Citations)
US3116181A
Cited
US3276922A
Cited
US3661567A
Cited
US3676867A
Cited
US4126494A
Cited
US4265684A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-30 | 1986-03-01 | 1986-08-31 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-30 | 1990-03-01 | 1990-08-31 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-30 | 1994-03-01 | 1994-08-31 | $7700.00 | Window Closed / Lapsed |