US4346206A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Imide prepolymer from reaction of epoxy compound with bis-imide/diamine reaction mixture
Assignee: Resonac Corp
•
Filing: 1980-08-11
•
Granted: 1982-08-24
•
Expires: 2000-08-11
Abstract
Abstract A process for preparing a thermosetting imide type prepolymer which comprises heating a bis-imide (A) and a diamine (B) in the presence of an organic solvent with a boiling point of 70° to 170° C. and heating the reaction mixture together with an epoxy compound (C). The imide type prepolymer prepared according to the process of the present invention has rapid curability and excellent solubility in low boiling point solvents such as acetone, methyl ethyl ketone and methyl cellosolve, which are available at low cost. Accordingly, the prepolymer is advantageously used especially for the production of laminated boards having good heat resisting properties, low moisture absorption and good adhesion to various substrates such as a copper foil.
Inventors
- 👤 Akio Takahashi
- 👤 Yutaka Itoh
- 👤 Takeshi Shimazaki
- 👤 Motoyo Wajima
- 👤 Hirosada Morishita
- 👤 Yutaka Mizuno
- 👤 Shunya Yokozawa
- 👤 Kenji Tsukanishi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 05:44
CPC Classifications
C; C08; C08G; C08G79/00; C08G79/08; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4014; C08G59/4042; C08G73/00; C08G73/06; C08G73/10; C08G73/12; C08G73/121; C08L; C08L63/00; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0313; H05K1/032; H05K1/0346
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
287 words
A process for preparing an imide prepolymer, which comprises the steps of: (1) heating, at 70° to 170° C. for 5 to 120 minutes, at least one bis-imide (A) represented by the formula (a): ##STR6## wherein R 1 stands for a divalent organic radical having a carbon-carbon double bond, and R 2 stands for a divalent organic radical having at least 2 carbon atoms, and at least one diamine (B) represented by the formula (b): H.sub.2 N--R.sub.3 --NH.sub.2 (b) wherein R 3 stands for a divalent organic radical having at least 2 carbon atoms, in an organic solvent having a boiling point of 70° to 170° C. as measured under a pressure of 760 mmHg, said at least one bis-imide (A) and said at least one diamine (B) being employed at a molar ratio of the component (A) to the component (B) of from 1:0.1 to 1:1, to obtain a reaction mixture containing an intermediate reaction product which is insoluble or slightly soluble in a low boiling point organic solvent, said solvent having a boiling point no higher than about that of methyl ethyl ketone; and (2) further heating, at 50° to 140° C. for 5 to 120 minutes, the reaction mixture together with at least one 1,2-epoxy compound (C) having at least two 1,2-epoxy groups, said at least one 1,2-epoxy compound (C) being employed in a weight proportion, relative to the total of said at least one bis-imide (A), said at least one diamine (B) and said at least one 1,2-epoxy compound (C), of from 10 to 80%, to obtain a reaction mixture containing an imide prepolymer having an increased solubility relative to that of said intermediate reaction product in said low boiling point organic solvent.
Claim 2
Dependent Claim
287 words
A process for preparing an imide prepolymer, which comprises the steps of: (1) heating, at 70° to 170° C. for 5 to 120 minutes, at least one bis-imide (A) represented by the formula (a): ##STR6## wherein R 1 stands for a divalent organic radical having a carbon-carbon double bond, and R 2 stands for a divalent organic radical having at least 2 carbon atoms, and at least one diamine (B) represented by the formula (b): H.sub.2 N--R.sub.3 --NH.sub.2 (b) wherein R 3 stands for a divalent organic radical having at least 2 carbon atoms, in an organic solvent having a boiling point of 70° to 170° C. as measured under a pressure of 760 mmHg, said at least one bis-imide (A) and said at least one diamine (B) being employed at a molar ratio of the component (A) to the component (B) of from 1:0.1 to 1:1, to obtain a reaction mixture containing an intermediate reaction product which is insoluble or slightly soluble in a low boiling point organic solvent, said solvent having a boiling point no higher than about that of methyl ethyl ketone; and (2) further heating, at 50° to 140° C. for 5 to 120 minutes, the reaction mixture together with at least one 1,2-epoxy compound (C) having at least two 1,2-epoxy groups, said at least one 1,2-epoxy compound (C) being employed in a weight proportion, relative to the total of said at least one bis-imide (A), said at least one diamine (B) and said at least one 1,2-epoxy compound (C), of from 10 to 80%, to obtain a reaction mixture containing an imide prepolymer having an increased solubility relative to that of said intermediate reaction product in said low boiling point organic solvent.
Claim 3
Dependent Claim
28 words
A process according to claim 1, wherein said solvent having a boiling point of 70° to 170° C. is 2-methoxyethanol, 2-ethoxyethanol, 2-(methoxymethoxy)ethanol, 2-isopropoxyethanol or a mixed solvent thereof.
Claim 4
Dependent Claim
11 words
An imide prepolymer produced by a process according to claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-23 | 1986-02-22 | 1986-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-23 | 1990-02-22 | 1990-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-23 | 1994-02-22 | 1994-08-24 | $7700.00 | Window Closed / Lapsed |