Tank process for plating aluminum substrates including porous aluminum castings
Assignee: Boeing Co
•
Filing: 1981-05-19
•
Granted: 1982-08-24
•
Expires: 2001-05-19
Abstract
Abstract An improved tank process for plating aluminum substrates which is especially advantageous for plating porous aluminum castings and, blister-free plated aluminum substrates produced thereby, characterized in that the aluminum piece parts are: (i) emulsion cleaned in a room temperature alkaline cleaner; (ii) immersed in a room temperature dilute acid, inorganic, fluoride salt solution to dissolve heavy oxides and surface silicon while minimizing etching and intergranular attack of the aluminum substrate such, for example, as a porous cast aluminum substrate; (iii) immersed in a room temperature dilute zincate bath for applying a relatively thin zinc protective coating, preferably utilizing a double zincate immersion process with an intermediate prolonged (1-3 min.) nitric acid soak to reduce the zincate deposition rate and to thereby provide improved zincate adhesion; (iv) plated with a non-porous strike applied directly on the zincate protective coating--e.g., by electroplating or by electroless plating methods such, for example, as by immersion in a bath of nickle-hypophosphite material maintained at a temperature of approximately 190° F.; and (v), immersed in a metal plating bath such, for example, as a tin plating bath--preferably, a low pH, room temperature acid tin bath--so as to apply a blister-free electrically conductive surface on the porous aluminum casting.
Inventors
- 👤 David M. Loch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 14:05
CPC Classifications
C; C25; C25D; C25D5/00; C25D5/34; C25D5/42; C25D5/44; C23; C23C; C23C18/00; C23C18/16; C23C18/1601; C23C18/1633; C23C18/1635; C23C18/1644; C23C18/1646; C23C18/165; C23C18/1653; C23C18/18; C23C18/1803; C23C18/1824; C23C18/1837; C23C18/1844; C23C18/54
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
196 words
The process of plating an aluminum substrate comprising the steps of: (a) cleaning the substrate; (b) immersing the substrate in a room temperature, low pH, dilute acid bath containing an acidic fluoride-containing salt so as to remove surface contaminants from the substrate while subjecting the substrate to only minimal etching; (c) immersing the substrate in a first dilute zincate bath having a zinc concentration on the order of 1.1 oz./gal. to apply a first protective coating of zinc thereon; (d) soaking the substrate in an acid bath for from 1-3 minutes to remove the first protective coating of zinc from the substrate and to apply a uniform oxide coating thereon for reducing subsequent zinc deposition rates; (e) immersing the substrate in a second dilute zincate bath having a zinc concentration on the order of 1.1 oz./gal. to apply a second protective coating of zinc thereon; (f) applying a non-porous barrier layer to the second protective coating of zinc by immersion of the zinc coated substrate in a heated bath containing a metal plating solution; and, (g) applying a conductive metal outer plate to the non-porous barrier layer by immersing the substrate in a metal plating bath.
Claim 2
Dependent Claim
196 words
The process of plating an aluminum substrate comprising the steps of: (a) cleaning the substrate; (b) immersing the substrate in a room temperature, low pH, dilute acid bath containing an acidic fluoride-containing salt so as to remove surface contaminants from the substrate while subjecting the substrate to only minimal etching; (c) immersing the substrate in a first dilute zincate bath having a zinc concentration on the order of 1.1 oz./gal. to apply a first protective coating of zinc thereon; (d) soaking the substrate in an acid bath for from 1-3 minutes to remove the first protective coating of zinc from the substrate and to apply a uniform oxide coating thereon for reducing subsequent zinc deposition rates; (e) immersing the substrate in a second dilute zincate bath having a zinc concentration on the order of 1.1 oz./gal. to apply a second protective coating of zinc thereon; (f) applying a non-porous barrier layer to the second protective coating of zinc by immersion of the zinc coated substrate in a heated bath containing a metal plating solution; and, (g) applying a conductive metal outer plate to the non-porous barrier layer by immersing the substrate in a metal plating bath.
Claim 3
Dependent Claim
26 words
The process as set forth in claim 1 wherein the substrate is emulsion cleaned in step (a) by immersion in a room temperature alkaline cleaning solution.
Claim 4
Dependent Claim
29 words
The process as set forth in claim 2 wherein the substrate is immersed in the alkaline cleaning solution for a period on the order of at least 10 minutes.
Claim 5
Dependent Claim
42 words
The process of claim 1 wherein the room temperature low pH bath comprises a solution of on the order of 25 volume percent water, 25 volume percent nitric acid, 25 volume percent sulfuric acid, and 8-16 oz./gal. of an acidic, fluoride-containing salt.
Claim 6
Dependent Claim
18 words
The process as set forth in claim 4 wherein the acidic fluoride-containing salt comprises at least 98% ammoniumbifluoride.
Claim 7
Dependent Claim
29 words
The process as set forth in claim 4 wherein the substance is immersed in the room temperature, low pH bath for a period on the order of 9-15 minutes.
Claim 8
Dependent Claim
29 words
The process as set forth in claim 4 wherein the substrate etch rate in step (b) is maintained at a relatively low rate on the order of 0.9 mil/surface/hr.
Claim 9
Dependent Claim
26 words
The process as set forth in claims 1, 2, 3, 4, 5, 6 or 7 wherein the acid bath employed in step (d) is nitric acid.
Claim 10
Dependent Claim
48 words
The process as set forth in claims 1, 2, 4 or 5 wherein the substrate is immersed in the first dilute zincate bath for a period on the order of 20-45 seconds and in the second dilute zincate bath for a period on the order of 5-30 seconds.
Claim 11
Dependent Claim
56 words
The process as set forth in claims 1, 2, 4 or 5 wherein the non-porous barrier layer applied in step (f) comprises an electroless nickel strike on the order of 0.0001" thick deposited on the substrate by immersion in a nickel-hypophosphite bath containing on the order of 75 volume percent water and 25 volume percent nickel-hypophosphite.
Claim 12
Dependent Claim
67 words
The process as set forth in claims 1, 2, 4 or 5 wherein the non-porous barrier layer applied in step (f) comprises an electroless nickel strike on the order of 0.0001" thick deposited on the substrate by immersion in a nickel-hypophosphite bath containing on the order of 75 volume percent water and 25 volume percent nickel-hypophosphite and maintained at a temperature on the order of 190° F.
Claim 13
Dependent Claim
70 words
The process as set forth in claims 1, 2, 4 or 5 wherein the non-porous barrier layer applied in step (f) comprises a cyanide copper strike on the order of 0.0001" thick electrolytically deposited on the substrate by immersion in a cyanide copper strike solution for a period of from 7-10 minutes and wherein the cyanide copper strike solution is maintained at a temperature on the order of 130° F.
Claim 14
Dependent Claim
141 words
The process as set forth in claims 1, 2, 4 or 5 wherein the non-porous barrier layer applied in step (f) comprises a cyanide copper strike on the order of 0.0001" thick electrolytically deposited on the substrate by immersion in a cyanide copper strike solution maintained at a temperature on the order of 130° F. for a period of from 7-10 minutes and an acid copper underplate on the order of at least 0.002" thick deposited on the cyanide copper strike, and wherein the conductive metal plate applied to the non-porous barrier layer in step (g) comprises a tin plate on the order of 0.0005" thick deposited on the acid copper underplate by immersion for a period of on the order of 60 minutes in a hot alkaline tin plate bath maintained at a temperature on the order of 160° F.
Claim 15
Dependent Claim
39 words
The process as set forth in claims 1, 2, 4 or 5 wherein the conductive metal plate applied to the non-porous barrier layer in step (g) is applied by immersion in a room temperature, low pH, acid tin bath.
Claim 16
Dependent Claim
22 words
The process as set forth in claims 1, 2, 4, 5 or 7 wherein the aluminum substrate is a porous aluminum substrate.
Claim 17
Dependent Claim
23 words
The process as set forth in claims 1, 2, 4, 5, or 7 wherein the aluminum substrate is a cast porous aluminum substrate.
Claim 18
Dependent Claim
25 words
The plated porous aluminum product formed by the process as set forth in claim 15 and characterized by the absence of plating separations and blisters.
Claim 19
Dependent Claim
26 words
The plated cast porous aluminum product formed by the process as set forth in claim 16 and characterized by the absence of plating separations and blisters.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-23 | 1986-02-22 | 1986-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-23 | 1990-02-22 | 1990-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-23 | 1994-02-22 | 1994-08-24 | $7700.00 | Window Closed / Lapsed |