Adhesive for perfect bound books and method of using same
Assignee: Ingredion Inc
•
Filing: 1981-07-30
•
Granted: 1982-08-24
•
Expires: 2001-07-30
Abstract
Abstract Hot melt adhesives especially suited for use in the perfect binding of books are prepared from (1) 15-30% of a block polymer having the general configuration A-B-A wherein A is a non-elastomeric polymer block derived from the moieties of a monovinyl aromatic hydrocarbon radical and B is an elastomeric polymer block derived from the moieties of a conjugated diene monomer; (2) 5-10% of an ethylene vinyl acetate copolymer containing 17 to 42% vinyl acetate; wherein the ratio of the block polymer to the ethylene vinyl acetate copolymer is within the range of 1.75:1 to 6:1; (3) 25-40% of at least one rosin ester tackifier selected from the group consisting of glycerol and pentaerythritol esters of natural and modified rosins, (4) 25-35% of a wax diluent which is solid at room temperature; and (5) 0.5 to 3% of at least one stabilizer. such composition being characterized by an ability to form a film exhibiting Instron yield strengths of 100-250 psi. and a low temperature flexibility of less than 10 DEG F.; such composition having a melt viscosity of 3,000 to 30,000 cps. at 350 DEG F., and being capable of setting up in less than 30 seconds and, when applied to roughened signature using perfect binding techniques yielding a book having an adhesion page pull on coated stock of at least 10 pounds, preferably at least 15 pounds, per page (73/8 to 71/2'' long). In addition to the adhesive described above, the present invention also discloses a method for binding books containing a plurality of sheets including at least some coated stock by means of the perfect binding method without the use of a primer using the novel adhesive of the present invention.
Inventors
- 👤 Thomas P. Flanagan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 19:16
CPC Classifications
C; C09; C09J; C09J131/00; C09J131/02; C09J131/04; B; B42; B42C; B42C9/00; C09J153/00; C09J153/02; C08; C08L; C08L2666/00; C08L2666/02; C08L53/00; C08L53/02; C08L91/00; C08L91/06; C08L93/00; C08L93/04; C09J2301/00; C09J2301/30; C09J2301/304
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
233 words
A non-pressure sensitive hot melt adhesive composition comprising on a weight basis: (1) 15-30% of at least one block polymer having the general configuration A-B-A wherein A is a non-elastomeric polymer block derived from the moieties of a monovinyl aromatic hydrocarbon radical and B is an elastomeric polymer block derived from the moieties of a conjugated diene monomer; (2) 5-10% of at least one ethylene vinyl acetate copolymer containing 17 to 42% vinyl acetate, where the weight ratio of block polymer to ethylene vinyl acetate copolymer is within the range of 1.75:1 to 6:1; (3) 25-40% of at least one rosin ester tackifier selected from the group consisting of glycerol and pentaerythritol esters of natural and modified rosins; (4) 25-35% of at least one wax diluent which is solid at room temperature; and (5) 0.5 to 3% of at least one stabilizer; said composition being characterized by an ability to form a film exhibiting Instron yield strengths of 100 to 250 psi. and a low temperature flexibility of less than 10° F., said composition having a melt viscosity of 3,000 to 30,000 cps. at 350° F. and being capable of setting up in less than 30 seconds and, when applied to roughened signatures using perfect binding techniques yielding a book having an adhesion page pull on coated stock of at least 10 pounds per page having a length of 73/8 to 71/2 inches.
Claim 2
Dependent Claim
233 words
A non-pressure sensitive hot melt adhesive composition comprising on a weight basis: (1) 15-30% of at least one block polymer having the general configuration A-B-A wherein A is a non-elastomeric polymer block derived from the moieties of a monovinyl aromatic hydrocarbon radical and B is an elastomeric polymer block derived from the moieties of a conjugated diene monomer; (2) 5-10% of at least one ethylene vinyl acetate copolymer containing 17 to 42% vinyl acetate, where the weight ratio of block polymer to ethylene vinyl acetate copolymer is within the range of 1.75:1 to 6:1; (3) 25-40% of at least one rosin ester tackifier selected from the group consisting of glycerol and pentaerythritol esters of natural and modified rosins; (4) 25-35% of at least one wax diluent which is solid at room temperature; and (5) 0.5 to 3% of at least one stabilizer; said composition being characterized by an ability to form a film exhibiting Instron yield strengths of 100 to 250 psi. and a low temperature flexibility of less than 10° F., said composition having a melt viscosity of 3,000 to 30,000 cps. at 350° F. and being capable of setting up in less than 30 seconds and, when applied to roughened signatures using perfect binding techniques yielding a book having an adhesion page pull on coated stock of at least 10 pounds per page having a length of 73/8 to 71/2 inches.
Claim 3
Dependent Claim
32 words
The composition of claim 1 wherein the monovinyl aromatic hydrocarbon monomer moieties in the block polymer are derived from styrene and the conjugated diene monomer moieties are derived from butadiene-1,3 or isoprene.
Claim 4
Dependent Claim
24 words
The composition of claim 1 wherein the ethylene vinyl acetate copolymer contains 17 to 29% vinyl acetate based on the weight of the copolymer.
Claim 5
Dependent Claim
38 words
The composition of claim 1 wherein the tackifier is selected from the group consisting of the glycerol esters of gum, tall or wood rosin; the glycerol ester of hydrogenated rosin and the pentaerythritol esters of the corresponding rosins.
Claim 6
Independent Claim
275 words
A method for binding books containing a plurality of sheets by means of the perfect binding method, the steps for producing a spine for said books comprising: (A) securing the edges of such sheets and applying thereto a molten film of a hot melt non-pressure sensitive adhesive composition comprising on a weight basis: (1) 15-30% of at least the block polymer having the general configuration A-B-A wherein A is a non-elastomeric polymer block derived from the moieties of a monovinyl aromatic hydrocarbon radical and B is an elastomeric polymer block derived from the moieties of a conjugated diene monomer; (2) 5-10% of at least one ethylene vinyl acetate copolymer containing 17% to 42% vinyl acetate; where the weight ratio of the block polymer to the ethylene vinyl acetate copolymer is within the range of 1.75:1 to 6:1; (3) 25-40% of at least one rosin ester tackifier selected from the group consisting of glycerol and pentaerythritol esters of natural and modified rosin, (4) 25-35% of at least one wax diluent which is solid at room temperature; and (5) 0.5 to 3% of at least one stabilizer; said film being characterized by an Instron yield strength of 100 to 250 psi., and a low temperature flexibility of less than 10° F., said composition having a melt viscosity of 3,000 to 30,000 cps. at 350° F. and a set up time of less than 30 seconds and, when applied to roughened signatures using perfect binding techniques yielding a book having an adhesion page pull on coated stock of at least 10 pounds per page having a length of 73/8 to 71/2 inches; (B) allowing said film to solidify.
Claim 7
Independent Claim
275 words
A method for binding books containing a plurality of sheets by means of the perfect binding method, the steps for producing a spine for said books comprising: (A) securing the edges of such sheets and applying thereto a molten film of a hot melt non-pressure sensitive adhesive composition comprising on a weight basis: (1) 15-30% of at least the block polymer having the general configuration A-B-A wherein A is a non-elastomeric polymer block derived from the moieties of a monovinyl aromatic hydrocarbon radical and B is an elastomeric polymer block derived from the moieties of a conjugated diene monomer; (2) 5-10% of at least one ethylene vinyl acetate copolymer containing 17% to 42% vinyl acetate; where the weight ratio of the block polymer to the ethylene vinyl acetate copolymer is within the range of 1.75:1 to 6:1; (3) 25-40% of at least one rosin ester tackifier selected from the group consisting of glycerol and pentaerythritol esters of natural and modified rosin, (4) 25-35% of at least one wax diluent which is solid at room temperature; and (5) 0.5 to 3% of at least one stabilizer; said film being characterized by an Instron yield strength of 100 to 250 psi., and a low temperature flexibility of less than 10° F., said composition having a melt viscosity of 3,000 to 30,000 cps. at 350° F. and a set up time of less than 30 seconds and, when applied to roughened signatures using perfect binding techniques yielding a book having an adhesion page pull on coated stock of at least 10 pounds per page having a length of 73/8 to 71/2 inches; (B) allowing said film to solidify.
Claim 8
Dependent Claim
22 words
The process of claim 5 wherein a cover is applied to the film while the film is still in the molten state.
Claim 9
Dependent Claim
17 words
The process of claim 5 wherein the book block is cased in to form a hardcover book.
References Cited (Backward Citations)
US3837994A
Cited
US3686107A
Cited
US3787531A
Cited
US3644252A
Cited
US3821143A
Cited
US3850858A
Cited
US4105611A
Cited
US4146521A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-23 | 1986-02-22 | 1986-08-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-23 | 1990-02-22 | 1990-08-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-23 | 1994-02-22 | 1994-08-24 | $7700.00 | Window Closed / Lapsed |