Urethane prepolymer repair system
Assignee: THEODORE J AND MARIYLN J DETTLING MARCH 9 1990 FAMILY TRUST
•
Filing: 1981-07-29
•
Granted: 1982-08-17
•
Expires: 2001-07-29
Abstract
Abstract A urethane prepolymer repair system is provided by an isocyanate-terminated polytetramethylene ether glycol prepolymer of about 3,500-10,500 molecular weight that cures to an elastomer upon exposure to atmospheric moisture and is packaged in a container capable of repeatedly dispensing the prepolymer with minimal exposure to ambient air, such as a collapsible tube or caulking gun cartridge. The repair system is used to build up worn down soles and heels of footwear, repair separations of soles and heels from shoe tops, and hundreds of other uses.
Inventors
- 👤 Theodore J. Dettling
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 19:50
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/28; C08G18/40; C08G18/48; C08G18/4854; C08G18/08
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
160 words
A urethane prepolymer repair system which comprises: a urethane prepolymer composition capable of curing to an elastomer upon exposure to atmospheric moisture and having: a total solids of 60-100%, a cured Durometer hardness of 50-90 Shore A, a cured 100% modulus of at least 200 psi, and a shelf life of at least 30 days at 120° F.; said urethane prepolymer composition containing a urethane prepolymer made essentially from a polytetramethylene ether glycol or mixture of glycols having a hydroxyl equivalent weight of about 300 to 2,000, and a stoichiometric excess of an organic polyisocyanate; said polytetramethylene ether glycol urethane prepolymer having: an isocyanate content of about 0.8-2.4%, and an average molecular weight of about 3,500-10,500; said urethane prepolymer composition being packaged in and dispensed from a moisture-impermeable container having a closable dispensing orifice and means to reduce the volume of the container and thereby extrude the urethane prepolymer composition through the orifice without introducing ambient air into the container.
Claim 2
Dependent Claim
160 words
A urethane prepolymer repair system which comprises: a urethane prepolymer composition capable of curing to an elastomer upon exposure to atmospheric moisture and having: a total solids of 60-100%, a cured Durometer hardness of 50-90 Shore A, a cured 100% modulus of at least 200 psi, and a shelf life of at least 30 days at 120° F.; said urethane prepolymer composition containing a urethane prepolymer made essentially from a polytetramethylene ether glycol or mixture of glycols having a hydroxyl equivalent weight of about 300 to 2,000, and a stoichiometric excess of an organic polyisocyanate; said polytetramethylene ether glycol urethane prepolymer having: an isocyanate content of about 0.8-2.4%, and an average molecular weight of about 3,500-10,500; said urethane prepolymer composition being packaged in and dispensed from a moisture-impermeable container having a closable dispensing orifice and means to reduce the volume of the container and thereby extrude the urethane prepolymer composition through the orifice without introducing ambient air into the container.
Claim 3
Dependent Claim
32 words
The repair system of claim 1 wherein the polytetramethylene ether glycol urethane prepolymer has an isocyanate content of about 1.1% to 1.9% and an average molecular weight of about 4,500 to 7,500.
Claim 4
Dependent Claim
17 words
The repair system of claims 1 or 2 wherein the organic polyisocyanate is 4,4 1 -diphenylmethane diisocyanate.
Claim 5
Dependent Claim
20 words
The repair system of claim 1, 2, or 3 wherein the urethane prepolymer composition has a total solids of 70-90%.
Claim 6
Dependent Claim
38 words
The repair system of claim 1 wherein the urethane prepolymer composition contains 0.3 to 1.5%, per 100% of the composition, of a molecular sieve in excess of that required to scavenge any water present in the composition ingredients.
Claim 7
Dependent Claim
18 words
The repair system of claim 1 wherein the urethane prepolymer composition is virtually devoid of free organic polyisocyanate.
Claim 8
Dependent Claim
21 words
The repair system of claim 1 wherein the polytetramethylene ether glycol urethane prepolymer is made essentially only from difunctional prepolymer precusors.
Claim 9
Dependent Claim
30 words
The repair system of claim 1 wherein the polytetramethylene ether glycol urethane prepolymer is incompletely polymerized when loaded into the container and the polymerization is completed in the filled container.
Claim 10
Dependent Claim
37 words
A method of restoring worn-down areas of footwear soles and heels which comprises applying the urethane prepolymer composition of the repair system of claim 1, 2, or 3 to the areas, and allowing the composition to cure.
Claim 11
Dependent Claim
56 words
A method of adhering together two surfaces which comprises applying the urethane prepolymer composition of the repair system of claim 1, 2, or 3 to one or both of the surfaces, then uniting and maintaining in joined relationship the two surfaces till the prepolymer composition cures to a degree sufficient to adhere the two surfaces together.
Claim 12
Dependent Claim
29 words
The method of claim 10 wherein there is an interval of at least 15 minutes between the steps of applying the urethane prepolymer composition and uniting the two surfaces.
Claim 13
Dependent Claim
51 words
A method of repairing holes and tears in an article which comprises applying to a thickness of at least 10 mils the urethane prepolymer composition of the repair system of claim 1, 2, or 3 onto the hole or tear and the contiguous surrounding area and allowing the composition to cure.
Claim 14
Dependent Claim
36 words
A method of making the repair system of claim 1 which comprised filling the container with the polytetramethylene ether glycol urethane prepolymer less than 50% polymerized, then completing the polymerization of the prepolymer in the container.
References Cited (Backward Citations)
US2830037A
Cited
US2998403A
Cited
US2901467A
Cited
US3012987A
Cited
US3705879A
Cited
US3746665A
Cited
US4110317A
Cited
US3919173A
Cited
US4125522A
Cited
US4182898A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |