Assignee: Elmers Products Inc
•
Filing: 1980-11-24
•
Granted: 1982-08-17
•
Expires: 2000-11-24
Abstract
Abstract A barytes-containing wood filler is prepared from essential ingredients including, on weight percent basis, 6-14% acrylic resin, 3-10% platy talc, 3-10% barytes filler, 3-12% clay filler, 40-65% calcium carbonate filler and 13-35% water. A barytes-free wood filler is prepared from the same proportions of acrylic resin, calcium carbonate filler and water, together with 5-18% platy talc and 0-15% clay filler. Desirably the average particle size of the talc is about 9 microns and the average particle size of the clay is about 5 microns.
Inventors
- 👤 Peter S. Columbus
- 👤 John Anderson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 16:15
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C08K3/346
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
112 words
Wood filler composition which provides exceptional performance on soft and hard species of wood, which is easily spreadable, resists shrinking on drying and cracking, stains superbly, is highly water resistant, can be sanded easily and which has excellent adhesion to wood, metal and paint, said composition having a viscosity of 120,000 to 250,000 cps. and comprising on solids basis 6 to 14% acrylic resin comprising polymerized acrylate esters, 3 to 10% platy talc having an average particle size of about 9 microns, 3 to 12% clay filler having an average particle size of about 5 microns, 3 to 10% barytes filler, 40 to 65% calcium carbonate filler and 13 to 35% water.
Claim 2
Dependent Claim
112 words
Wood filler composition which provides exceptional performance on soft and hard species of wood, which is easily spreadable, resists shrinking on drying and cracking, stains superbly, is highly water resistant, can be sanded easily and which has excellent adhesion to wood, metal and paint, said composition having a viscosity of 120,000 to 250,000 cps. and comprising on solids basis 6 to 14% acrylic resin comprising polymerized acrylate esters, 3 to 10% platy talc having an average particle size of about 9 microns, 3 to 12% clay filler having an average particle size of about 5 microns, 3 to 10% barytes filler, 40 to 65% calcium carbonate filler and 13 to 35% water.
Claim 3
Dependent Claim
106 words
Composition of claim 1 wherein the acrylic resin is selected from soft monomers having the formula ##STR3## hard monomers of the formula ##STR4## and mixtures thereof, wherein R 1 is H or an alkyl group of 1 to 4 carbon atoms and R 2 is an alkyl radical of 1 to 14 carbon atoms; and R 3 is H, methyl, alkyl radical of 1 to 5 carbon atoms or alkyl radical of 15 to 20 carbon atoms; the resin being also prepared with an alpha-beta unsaturated monocarboxylic acid in amount of about 0.2 to 5%, based on the weight of the resin, to aid in cross-linking.
Claim 4
Dependent Claim
105 words
Composition of claim 2 wherein the preferred resin is further defined as follows: when R 1 of the soft monomer is H or methyl, R 2 contains about 1 to 14 carbon atoms whereas when R 1 is alkyl of 2 to 4 carbon atoms, then R 2 is alkyl of 6 to 14 carbon atoms; and as to R 3 of the hard monomers, when R 1 is H, R 3 is alkyl of 1 or 13 to 20 carbon atoms whereas when R 1 is methyl, R 3 is alkyl of 1 to 5 carbon atoms or from 15 to 20 carbon atoms.
Claim 5
Dependent Claim
38 words
Composition of claim 3 wherein R 1 is H or methyl and R 2 and R 3 are selected from alkyl group of 1 to 8 carbon atoms; and the acid is selected from acrylic and methacrylic acids.
Claim 6
Dependent Claim
46 words
Composition of claim 4 wherein amounts of the ingredients are 8 to 11% of the acrylic resin, 4 to 6% of platy talc, 4 to 6% of barytes filler, 5 to 9% clay filler, 50 to 56% calcium carbonate filler and 17 to 28% of water.
Claim 7
Dependent Claim
32 words
Composition of claim 4 wherein the resin has a T g of about 0° C., is in emulsion form and is prepared from ethyl acrylate, butyl acrylate, methyl methacrylate and the acid.
Claim 8
Dependent Claim
23 words
Composition of claim 6 wherein amount of ethyl acrylate exceeds 50% of the resin, and amount of the acid is 0.5 to 3%.
Claim 9
Dependent Claim
48 words
Composition of claim 5 wherein the resin has a T g of about 0° to 25° C., is in emulsion form and is prepared from ethyl acrylate in amount exceeding 50%, methyl methacrylate in amount of 25 to 35% and the acid in amount of 0.5 to 3%.
Claim 10
Dependent Claim
60 words
Composition of claim 7 wherein the barytes filler comprises in excess of about 95% barium sulfate with more than 90% thereof having particle size less than 20 microns; the clay filler is aluminum silicate; and the calcium carbonate filler has a mean particle size of about 5 to 15 microns; and viscosity of the composition is 160,000 to 180,000 cps.
Claim 11
Dependent Claim
98 words
Wood filler composition which provides exceptional performance on soft and hard species of wood, which is easily spreadable, resists shrinking on drying and cracking, stains superbly, is highly water resistant, can be sanded easily and which has excellent adhesion to wood, metal and paint, said composition comprising on solids basis 6 to 14% acrylic resin comprising polymerized acrylate esters, 5 to 18% platy talc having an average particle size of about 9 microns, 3 to 15% clay filler having an average particle size of about 5 microns, 40 to 65% calcium carbonate filler and 13 to 35% water.
Claim 12
Dependent Claim
98 words
Wood filler composition which provides exceptional performance on soft and hard species of wood, which is easily spreadable, resists shrinking on drying and cracking, stains superbly, is highly water resistant, can be sanded easily and which has excellent adhesion to wood, metal and paint, said composition comprising on solids basis 6 to 14% acrylic resin comprising polymerized acrylate esters, 5 to 18% platy talc having an average particle size of about 9 microns, 3 to 15% clay filler having an average particle size of about 5 microns, 40 to 65% calcium carbonate filler and 13 to 35% water.
Claim 13
Dependent Claim
106 words
Composition of claim 10 wherein the acrylic resin is selected from soft monomers having the formula ##STR5## hard monomers of the formula ##STR6## and mixtures thereof, wherein R 1 is H or an alkyl group of 1 to 4 carbon atoms and R 2 is an alkyl radical of 1 to 14 carbon atoms; and R 3 is H, methyl, alkyl radical of 1 to 5 carbon atoms or alkyl radical of 15 to 20 carbon atoms; the resin being also prepared with an alpha-beta unsaturated monocarboxylic acid in amount of about 0.2 to 5%, based on the weight of the resin, to aid in cross-linking.
Claim 14
Dependent Claim
104 words
Composition of claim 11 wherein the preferred resin is further defined as follows: when R 1 of the soft monomer is H or methyl, R 2 contains about 1 to 14 carbon atoms whereas R 1 is alkyl of 2 to 4 carbon atoms, then R 2 is alkyl of 6 to 14 carbon atoms; and as to R 3 of the hard monomers, when R 1 is H, R 3 is alkyl of 1 or 13 to 20 carbon atoms whereas when R 1 is methyl, R 3 is alkyl of 1 to 5 carbon atoms or from 15 to 20 carbon atoms.
Claim 15
Dependent Claim
38 words
Composition of claim 12 wherein R 1 is H or methyl and R 2 and R 3 are selected from alkyl group of 1 to 8 carbon atoms; and the acid is selected from acrylic and methacrylic acids.
Claim 16
Dependent Claim
41 words
Composition of claim 13 wherein amounts of the ingredients are 8 to 11% of the acrylic resin, 9 to 13% of platy talc, not more than 8% clay filler, 51 to 57% calcium carbonate filler and 17 to 28% of water.
Claim 17
Dependent Claim
35 words
Composition of claim 13 wherein the resin has a T g of about 0° C. to 25° C., is in emulsion form and is prepared from ethyl acrylate, butyl acrylate, methyl methacrylate and the acid.
Claim 18
Dependent Claim
23 words
Composition of claim 15 wherein amount of ethyl acrylate exceeds 50% of the resin, and amount of the acids is 0.5 to 3%.
Claim 19
Dependent Claim
48 words
Composition of claim 14 wherein the resin has a T g of about 0° to 25° C., is in emulsion form and is prepared from ethyl acrylate in amount exceeding 50%, methyl methacrylate in amount of 25 to 35% and the acid in amount of 0.5 to 3%.
Claim 20
Dependent Claim
37 words
Composition of claim 17 wherein the clay filler is aluminum silicate; the calcium carbonate filler has a mean particle size of about 5 to 15 microns; and the viscosity of the composition is 160,000 to 180,000 cps.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |