Superior ohmic contacts to III-V semiconductor by virtue of double donor impurity
Assignee: United States Department of the Navy
•
Filing: 1981-03-25
•
Granted: 1982-08-17
•
Expires: 2001-03-25
Abstract
Abstract A method for fabricating superior ohmic contacts in a III-V semiconductor wafer by virtue of double donor (or double acceptor) impurity complex formation. A typical III-V, e.g., GaAs, semiconductor device is fabricated by depositing a thin Si 3 N 4 layer and then regions are opened, by photoresist methods, upon which ohmic contacts are to be made. New resist is applied over the wafer and the ohmic contact regions are again opened. Si ions are now implanted to form the active channel and the drain and source regions (in an FET device). The resist layer is removed, a layer of Ge is laid down and a layer of Se over the Ge. The Ge layer is coated with a layer of SiO 2 , Si 3 N 4 or a mixture of both, and annealed, causing the Ge and Se to diffuse rapidly into the Si ion implant region. The SiO 2 , Si 3 N 4 and excess surface Ge and Se is now removed. Metallization of the electrode areas, preferably with reliable refractory metals, is effected, producing ohmic tunneling contacts over the Ge/Se diffused regions and rectifying, non-ohmic, Schottky barrier contacts over the selected remainder of the Si-implanted region.
Inventors
- 👤 Max N. Yoder
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:58
CPC Classifications
H; H10; H10D; H10D30/00; H10D30/01; H10D30/061; H10D30/0612; H10D30/0614; H10D64/00; H10D64/01; H10D64/011; H10D64/0116; H10D64/012; H10D64/0124; H10D64/60; H10D64/62; H10P; H10P32/00; H10P32/10; H10P32/14; H10P32/17; H10P32/174; Y; Y10; Y10S; Y10S148/00; Y10S148/084
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
165 words
A process for fabricating superior ohmic contacts in group III-V compound semiconductor materials comprising the steps of: selecting a substrate wafer composed of a III-V compound, III and V designating groups of elements in the periodic table of elements; implanting the substrate material through one surface with impurity ions from an element from groups II, IV or VI of the periodic table, the element being ionizable to provide charge carriers in the substrate, the impurity element being implanted at a fluence level or under temperature conditions which damage the lattice sites of the substrate material; coating said one surface with a pair of elements which, when diffused into the substrate material, provide ions which become substitutional on opposite sub-lattice sites and act together to provide charge carriers of the same polarity, either donors or acceptors; diffusing said pair of elements into a selected portion of the ion-implanted region; forming an electrode on said surface of said wafer over said selected portion of the ion-implanted region.
Claim 2
Dependent Claim
165 words
A process for fabricating superior ohmic contacts in group III-V compound semiconductor materials comprising the steps of: selecting a substrate wafer composed of a III-V compound, III and V designating groups of elements in the periodic table of elements; implanting the substrate material through one surface with impurity ions from an element from groups II, IV or VI of the periodic table, the element being ionizable to provide charge carriers in the substrate, the impurity element being implanted at a fluence level or under temperature conditions which damage the lattice sites of the substrate material; coating said one surface with a pair of elements which, when diffused into the substrate material, provide ions which become substitutional on opposite sub-lattice sites and act together to provide charge carriers of the same polarity, either donors or acceptors; diffusing said pair of elements into a selected portion of the ion-implanted region; forming an electrode on said surface of said wafer over said selected portion of the ion-implanted region.
Claim 3
Dependent Claim
30 words
A process as in claim 1, wherein: the step of coating comprises first coating said one surface with one element and then coating the other element over the first-element coating.
Claim 4
Dependent Claim
12 words
A process as in claim 2, wherein: said substrate material is GaAs.
Claim 5
Dependent Claim
13 words
A process as in claim 3, wherein: said impurity ions are Si ions.
Claim 6
Dependent Claim
18 words
A process as in claim 4, wherein: said impurity ions are from an element selected from group IV.
Claim 7
Dependent Claim
22 words
A process as in claim 5, wherein: said pair of elements are selected one from group IV and one from group VI.
Claim 8
Dependent Claim
18 words
A process as in claim 4, wherein: said impurity ions are from an element selected from group VI.
Claim 9
Dependent Claim
18 words
A process as in claim 4, wherein: said impurity ions are from an element selected from group II.
Claim 10
Dependent Claim
22 words
A process as in claim 8, wherein: said pair of elements are selected one from group II and one from group IV.
Claim 11
Dependent Claim
20 words
A process as in claim 4, wherein: said pair of elements for coating said one surface are Ge and Se.
Claim 12
Dependent Claim
30 words
A process as in claim 10, wherein: the step of diffusion comprises annealing the coated wafer at a temperature of about 850° C., for a period of about 30 minutes.
Claim 13
Dependent Claim
18 words
A process as in claim 11, wherein: the electrode material is selected from one or more refractory metals.
Claim 14
Dependent Claim
18 words
A process as in claim 12, wherein: the electrode material is selected from one or more refractory metals.
Claim 15
Dependent Claim
21 words
A process as in claim 4, wherein: said impurity ions are Si ions, and said coating elements are Ge and Se.
Claim 16
Dependent Claim
18 words
A process as in claim 14, wherein: the electrode material is selected from one or more refractory metals.
References Cited (Backward Citations)
US4188710A
Cited
US4267014A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |