Welding backup tape and its method of manufacture
Assignee: Individual
•
Filing: 1981-07-06
•
Granted: 1982-08-17
•
Expires: 2001-07-06
Abstract
Abstract In welding metal sheets together from only one side, an improved welding backup tape is self-adhesively applied to insure the consistent formation of a smooth, inclusion free, slightly convex underbead which requires little or no dressing, or grinding, and which does not impede in any way the achievement of 100% radiographic weldment testing. This welding backup tape is made in one embodiment by mixing into solution two parts of a colloidal silica solution with one part of a titanium dioxide refractory coating solution. Applying this resulting solution as a refractory coating to the upper portion of an electrical grade, heat treated, braided, natural finish, finely woven, fiberglass material in a sleeving configuration. Heating this solution soaked fiberglass sleeving at or above seven-hundred and below one-thousand degrees fahrenheit to activate its binding capability, to burn off all the organic matter from both the fiberglass sleeving and the refractory coating, and to remove all mechanical and chemical water. Bringing together from supply sources, this refractory coated fiberglass sleeve, a silicone adhesive coated electrical grade fiberglass carrier tape, and a transfer material such as a thin, three to six mil, polyethylene film. Pressing the fiberglass sleeving, coated side up, down upon the center of the fiberglass carrier tape, adhesive side up. Pressing the transfer material, e.g. the polyethylene film, down on both the coated fiberglass sleeving and the fiberglass carrier tape to affix itself to the exposed adhesive of the carrier tape at either side of the affixed coated sleeving.
Inventors
- 👤 Donald K. Knapp
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:17
CPC Classifications
B; B23; B23K; B23K9/00; B23K9/02; B23K9/035; B23K9/0356; C; C09; C09J; C09J7/00; C09J7/20; C09J7/21; C09J2400/00; C09J2400/20; C09J2400/26; C09J2400/263; Y; Y10; Y10T; Y10T428/00; Y10T428/14; Y10T428/1414; Y10T428/1438; Y10T428/1452; Y10T428/28; Y10T428/2848
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
119 words
A welding backup tape, comprising: (a) a heat treated, braided, substantially finely woven fiberglass material of sleeve like cross section having a high temperature fired on refractory coating on its upper portion, freed of all matter which would otherwise later cause outgasing, which is derived from mixing solutions of two parts of colloidal silica solution and one part of a titanium dioxide refractory coating; (b) a silicone adhesive coated fiberglass carrier tape positioned below and centered against the lower portion of the refractory coated fiberglass material; and (c) a thin polyethylene film release material ranging in thickness from 3 to 6 mils pressed down over the coated fiberglass material and into adhesive contact with the said fiberglass carrier tape.
Claim 2
Dependent Claim
119 words
A welding backup tape, comprising: (a) a heat treated, braided, substantially finely woven fiberglass material of sleeve like cross section having a high temperature fired on refractory coating on its upper portion, freed of all matter which would otherwise later cause outgasing, which is derived from mixing solutions of two parts of colloidal silica solution and one part of a titanium dioxide refractory coating; (b) a silicone adhesive coated fiberglass carrier tape positioned below and centered against the lower portion of the refractory coated fiberglass material; and (c) a thin polyethylene film release material ranging in thickness from 3 to 6 mils pressed down over the coated fiberglass material and into adhesive contact with the said fiberglass carrier tape.
Claim 3
Dependent Claim
146 words
A welding backup tape comprising: (a) a heat treated, braided, substantially finely woven fiberglass material or tubular cross section having a fired on coating, fired at a temperature between 700 and 1000 degrees Fahrenheit, on its upper portion derived from a two part colloidal binding solution and a one part refractory coating solution, wherein compatible materials are selected from among the binding group of silica colloidal solution, alumina colloidal solution, ethyl silicate solution, sodium silicate solution, potassium silicate solution, phosphoric acid solution, chromic acid solution, and from among the refractory group of alumina, zirconia, zircon, magnesia, silica, chromia, titania, boria, or combinations thereof; (b) a silicone adhesive coated fiberglass carrier tape positioned below and centered against the lower portion of the coated fiberglass material; and (c) a release material pressed down over the coated fiberglass material and into adhesive contact with the said fiberglass carrier tape.
Claim 4
Dependent Claim
146 words
A welding backup tape comprising: (a) a heat treated, braided, substantially finely woven fiberglass material or tubular cross section having a fired on coating, fired at a temperature between 700 and 1000 degrees Fahrenheit, on its upper portion derived from a two part colloidal binding solution and a one part refractory coating solution, wherein compatible materials are selected from among the binding group of silica colloidal solution, alumina colloidal solution, ethyl silicate solution, sodium silicate solution, potassium silicate solution, phosphoric acid solution, chromic acid solution, and from among the refractory group of alumina, zirconia, zircon, magnesia, silica, chromia, titania, boria, or combinations thereof; (b) a silicone adhesive coated fiberglass carrier tape positioned below and centered against the lower portion of the coated fiberglass material; and (c) a release material pressed down over the coated fiberglass material and into adhesive contact with the said fiberglass carrier tape.
Claim 5
Independent Claim
157 words
A method of manufacturing a welding backup tape, comprising: (a) mixing into solution a colloidal silica solution with a titanium dioxide refractory coating solution; (b) applying this resulting solution as a coating to the upper portion of a heat treated, braided, finely woven fiberglass material; (c) heating this coated fiberglass material at a sufficiently high temperature to activate its binding capability, to burn off all its organic matter from both the fiberglass material and coating, and to remove all water; (d) bringing together from respective supply sources, this coated fiberglass material, a silicone adhesive coated fiberglass carrier tape, and a release material; (e) pressing the fiberglass material, coated side up, down upon the center of the carrier tape, adhesive side up; and (f) pressing the release material down on both the coated fiberglass material and the carrier tape, to affix itself to the exposed adhesive of the carrier tape at either side of the affixed fiberglass material.
Claim 6
Independent Claim
157 words
A method of manufacturing a welding backup tape, comprising: (a) mixing into solution a colloidal silica solution with a titanium dioxide refractory coating solution; (b) applying this resulting solution as a coating to the upper portion of a heat treated, braided, finely woven fiberglass material; (c) heating this coated fiberglass material at a sufficiently high temperature to activate its binding capability, to burn off all its organic matter from both the fiberglass material and coating, and to remove all water; (d) bringing together from respective supply sources, this coated fiberglass material, a silicone adhesive coated fiberglass carrier tape, and a release material; (e) pressing the fiberglass material, coated side up, down upon the center of the carrier tape, adhesive side up; and (f) pressing the release material down on both the coated fiberglass material and the carrier tape, to affix itself to the exposed adhesive of the carrier tape at either side of the affixed fiberglass material.
Claim 7
Dependent Claim
33 words
A method of manufacturing a welding backup tape, as claimed in claim 3, wherein the heating of the coated fiberglass material is undertaken at or above 700° F. and not over 1000° F.
Claim 8
Independent Claim
25 words
A method of manufacturing a welding backup tape, as claimed in claims 3 or 4, wherein the fiberglass material has a sleeve like cross section.
Claim 9
Independent Claim
35 words
A method of manufacturing a welding backup tape, as claimed in claims 3 or 4 wherein the release material is a thin polyethylene film taken from sources ranging in thickness from three to six mils.
Claim 10
Independent Claim
39 words
A method of manufacturing a welding backup tape as claimed in claims 3 or 4, wherein in mixing the solutions, two parts of the colloidal silica solution are mixed with one part of the titanium dioxide refractory coating solution.
Claim 11
Independent Claim
242 words
A method of manufacturing a welding backup tape; comprising: (a) mixing into solution two parts of compatible binding materials and one part of refractory materials to make a refractory coating solution, the binding materials being selected from among the group of silica colloidal solution, alumina colloidal solution, ethyl silicate solution, sodium silicate solution, potassium silicate solution, phosphoric acid solution, chromic acid solution, and the refractory materials being selected from among the group of alumina, zirconia, zircon, magnesia, silica, chromia, titania. boria, or combinations thereof; (b) applying this resulting solution as a coating to the upper portion of a heat treated, braided, finely woven fiberglass material of tubular cross section; (c) heating this coated fiberglass material at a sufficiently high temperature between 700 and 1000 degrees Fahrenheit to activate its binding capability, to burn off all its organic matter from both the fiberglass material and coating, and to remove all water so there will be no gasing attributed to the welding tape during welding; (d) bringing together from respective supply sources, this coated fiberglass material, a silicone adhesive coated electrical grade fiberglass carrier tape, and a release material; (e) pressing the fiberglass material, coated side up, down upon the center of the carrier tape, adhesive side up; and (f) pressing the release material down on both the coated fiberglass material and the carrier tape, to affix itself to the exposed adhesive of the carrier tape at either side of the affixed fiberglass material.
Claim 12
Independent Claim
242 words
A method of manufacturing a welding backup tape; comprising: (a) mixing into solution two parts of compatible binding materials and one part of refractory materials to make a refractory coating solution, the binding materials being selected from among the group of silica colloidal solution, alumina colloidal solution, ethyl silicate solution, sodium silicate solution, potassium silicate solution, phosphoric acid solution, chromic acid solution, and the refractory materials being selected from among the group of alumina, zirconia, zircon, magnesia, silica, chromia, titania. boria, or combinations thereof; (b) applying this resulting solution as a coating to the upper portion of a heat treated, braided, finely woven fiberglass material of tubular cross section; (c) heating this coated fiberglass material at a sufficiently high temperature between 700 and 1000 degrees Fahrenheit to activate its binding capability, to burn off all its organic matter from both the fiberglass material and coating, and to remove all water so there will be no gasing attributed to the welding tape during welding; (d) bringing together from respective supply sources, this coated fiberglass material, a silicone adhesive coated electrical grade fiberglass carrier tape, and a release material; (e) pressing the fiberglass material, coated side up, down upon the center of the carrier tape, adhesive side up; and (f) pressing the release material down on both the coated fiberglass material and the carrier tape, to affix itself to the exposed adhesive of the carrier tape at either side of the affixed fiberglass material.
References Cited (Backward Citations)
US2792626A
Cited
US3326741A
Cited
US3509936A
Cited
US3490065A
Cited
US3372852A
Cited
US3365566A
Cited
US3396935A
Cited
US3508938A
Cited
US3494020A
Cited
US3850684A
Cited
US3929270A
Cited
US3972466A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-16 | 1986-02-15 | 1986-08-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-16 | 1990-02-15 | 1990-08-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-16 | 1994-02-15 | 1994-08-17 | $7700.00 | Window Closed / Lapsed |