Abstract The present invention is a process wherein: the process includes a method during slabbing, in which, recesses in the thicknesswise direction are formed on a pair of opposite surfaces at each end of the top and bottom of said steel ingot, subsequently, the central portions which have not been rolled, are rolled to the depth of said recesses, then, recesses in the widthwise direction are formed at the same end as described above, next, the central portions, which have not been rolled, are rolled to the depth of said recess in the widthwise direction; and, when the thicknesswise reduction value is ΔH T and the widthwise reduction value is ΔH W in said thicknesswise and widthwise reduction rollings, ΔH W /ΔHt is regulated to 0.40˜0.65 in a region where the material has a comparatively large thickness and the side profile of the material presents a double barrelling, and ΔH W /ΔH T is regulated to 0.3 or less in a region where the thickness of the material has a comparatively small thickness and the side profile of the material presents a single barrelling; whereby fishtails are prevented from growing so that crop loss consisting of fishtails and double-plate shaped overlaps can be reduced, thereby improving the rolling yield to a considerable extent.
Inventors
👤 Minoru Matsuzaki
Bibliographic Details
Application Number—
JurisdictionUS
Data Sourcegoogle_patents
Last Synchronized2026-11-06 17:51
CPC Classifications
B; B21; B21B; B21B1/00; B21B1/02; B21B1/026
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
126 words
A process for preventing growth of fishtails during slabbing of a steel ingot effected by a reversible rolling mill, including a step of forming recesses at least on a pair of opposite surfaces at least at either the top or bottom of said steel ingot by use of rolling rolls, wherein said process further includes a method of forming recesses in the thicknesswise and widthwise directions, and the ratio between the widthwise reduction value and the thicknesswise reduction value for forming said recesses is regulated to 0.40˜0.65 in a region where the side profile of the material due to the thicknesswise reduction presents a double barrelling and the value in a region where said side profile presents a single barrelling is regulated to 0.3 or less.
Claim 2
Dependent Claim
126 words
A process for preventing growth of fishtails during slabbing of a steel ingot effected by a reversible rolling mill, including a step of forming recesses at least on a pair of opposite surfaces at least at either the top or bottom of said steel ingot by use of rolling rolls, wherein said process further includes a method of forming recesses in the thicknesswise and widthwise directions, and the ratio between the widthwise reduction value and the thicknesswise reduction value for forming said recesses is regulated to 0.40˜0.65 in a region where the side profile of the material due to the thicknesswise reduction presents a double barrelling and the value in a region where said side profile presents a single barrelling is regulated to 0.3 or less.
Claim 3
Dependent Claim
54 words
A process for preventing growth of fishtails during slabbing as set forth in claim 1, wherein, firstly said recesses are formed in the thicknesswise direction of the material and then ordinary thicknesswise reduction rolling is effected, and secondly said recesses are formed in the widthwise direction and thereafter ordinary widthwise reduction rolling is effected.
Claim 4
Dependent Claim
34 words
A process for preventing growth of fishtails during slabbing as set forth in claim 1, wherein, said recesses are formed in plural number of times in rolling schedule in the thicknesswise and widthwise directions.
Claim 5
Dependent Claim
24 words
A process for preventing growth of fishtails during slabbing as set forth in claim 1, the length of each recess is from 200˜400 mm.