Thermoplastic elastomer blends
Assignee: Bridgestone Firestone Inc
•
Filing: 1980-08-04
•
Granted: 1982-08-10
•
Expires: 2000-08-04
Abstract
Abstract Thermoplastic elastomer compositions of the present invention comprise a blend of from about 10 to about 50 parts by weight of a crystalline 1-olefin polymer, from about 80 to about 15 parts by weight of a styrene-butadiene rubber, and from about 5 to about 55 parts by weight of a highly saturated elastomer. The thermoplastic blends have very good physical properties, especially tear strength, tensile strength, elongation at break, low temperature impact resistance, minimum creep at high temperatures, and smooth surfaces when injection molded. The compositions, which may be partially cured, also have excellent aging properties, as well as paint adhesion. The compositions are a true thermoplastic in that they can be repeatedly processed and yet maintain their good physical properties.
Inventors
- 👤 Georg G. A. Bohm
- 👤 Gary R. Hamed
- 👤 Lee E. Vescelius
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:57
CPC Classifications
C; C08; C08L; C08L21/00; C08L23/00; C08L23/02; C08L23/10; C08L25/00; C08L25/02; C08L25/04; C08L25/08; C08L25/10; C08L53/00; C08L53/02; C08L53/025; C08L9/00; C08L9/06; C08L2205/00; C08L2205/03; C08L23/04; C08L23/08; C08L23/0846; C08L23/0853; C08L23/0869; C08L23/16; C08L23/18; C08L23/20; C08L23/22
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
211 words
A process for making a thermoplastic elastomer blend composition, comprising the steps of: providing a blend of a 1-olefin polymer, a random styrene-butadiene rubber copolymer and a highly saturated elastomer, the amount of said 1-olefin homopolymer, ranging from about 10 to about 50 parts by weight, the amount of said styrene-butadiene rubber ranging from about 80 to about 15 parts by weight, the amount of said highly saturated elastomer ranging from about 5 to about 55 parts by weight, said 1-olefin polymer selected from the group consisting of a homopolymer and a copolymer made from 1-olefin monomers having from 2 to about 20 carbon atoms, said homopolymer or said copolymer having a melting point of at least 90° C., wherein said highly saturated elastomer is selected from the group consisting of hydrogenated polymer made from dienes having from 4 to 10 carbon atoms and a hydrogenated diblock or triblock copolymer made from conjugated dienes having from 4 to 10 carbon atoms and vinyl substituted aromatics having from 8 to 12 carbon atoms, the amount of said saturation of said elastomer being at least 70%, and mixing said blend at a temperature at or above the melting point of said crystalline 1-olefin polymer so that a reprocessable thermoplastic elastomer blend is formed.
Claim 2
Dependent Claim
211 words
A process for making a thermoplastic elastomer blend composition, comprising the steps of: providing a blend of a 1-olefin polymer, a random styrene-butadiene rubber copolymer and a highly saturated elastomer, the amount of said 1-olefin homopolymer, ranging from about 10 to about 50 parts by weight, the amount of said styrene-butadiene rubber ranging from about 80 to about 15 parts by weight, the amount of said highly saturated elastomer ranging from about 5 to about 55 parts by weight, said 1-olefin polymer selected from the group consisting of a homopolymer and a copolymer made from 1-olefin monomers having from 2 to about 20 carbon atoms, said homopolymer or said copolymer having a melting point of at least 90° C., wherein said highly saturated elastomer is selected from the group consisting of hydrogenated polymer made from dienes having from 4 to 10 carbon atoms and a hydrogenated diblock or triblock copolymer made from conjugated dienes having from 4 to 10 carbon atoms and vinyl substituted aromatics having from 8 to 12 carbon atoms, the amount of said saturation of said elastomer being at least 70%, and mixing said blend at a temperature at or above the melting point of said crystalline 1-olefin polymer so that a reprocessable thermoplastic elastomer blend is formed.
Claim 3
Dependent Claim
107 words
A process according to claim 1 wherein the amount of said 1-olefin polymer ranges from about 30 to about 45 parts, wherein the amount of said sytrene-butadiene rubber ranges from about 50 to about 20 parts, and has from about 60% to about 90% by weight of butadiene, and wherein the amount of said highly saturated elastomer ranges from about 8 to about 35 parts, wherein said 1-olefin copolymer is made from a major amount by weight of propylene monomers and a minor amount by weight of ethylene monomers, and wherein said highly saturated elastomer is selected from the group consisting of hydrogenated polybutadiene and hydrogenated polyisoprene.
Claim 4
Dependent Claim
70 words
A process according to claim 2 wherein the molecular weight of said styrene-butadiene rubber ranges from about 50,000 to about 1,000,000, wherein the melting point of said 1-olefin polymer or copolymer is at least 130° C., wherein the moecular weight of said 1-olefin polymer or copolymer ranges from about 20,000 to about 1,000,000, and wherein the molecular weight of said highly saturated elastomer ranges from about 10,000 to about 1,000,000.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-09 | 1986-02-08 | 1986-08-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-09 | 1990-02-08 | 1990-08-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-09 | 1994-02-08 | 1994-08-10 | $7700.00 | Window Closed / Lapsed |