Abstract
Abstract Silicon carbide powders suitable for producing sintered body having a high density are produced by reacting 1.7 to 2.1 parts by weight of silicon monoxide with 1.0 part by weight of finely divided carbon at a temperature of 1,200° to 1,500° C. under a reduced pressure of lower than 10 mmHg.
Inventors
- 👤 Hiroshige Suzuki
- 👤 Teizo Hase
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 19:34
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/565; C01; C01B; C01B32/00; C01B32/90; C01B32/914; C01B32/956; C01B32/963; C01B32/97; C01B32/984; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/10; C01P2006/12; C01P2006/90
Claims Analysis
Total Claims: 3
Claim 1
Independent Claim
136 words
Sinterable silicon carbide powders having submicron grain size produced by reacting 1.8 to 2.0 parts by weight of silicon monoxide with to 1.0 part by weight of finely divided carbon at a temperature of 1,340° to 1,440° C. under an essentially inert atmosphere at a reduced pressure of less than 10 mmHg, the partial pressure of oxygen in said atmosphere being less than 10 -10 atmospheres, said powders when mixed with 1% by weight each of boron and carbon and then heated at 2,100° C. for 60 minutes forming a sintered body having a density of 96% of theoretical density, a fine particle structure of less than 10 μm, a bending strength of 82.0 kg/mm 2 in the three point bending test at 1700° C. at 10 -6 mmHg and containing more than 90%-β-type silicon carbide.
Claim 2
Dependent Claim
136 words
Sinterable silicon carbide powders having submicron grain size produced by reacting 1.8 to 2.0 parts by weight of silicon monoxide with to 1.0 part by weight of finely divided carbon at a temperature of 1,340° to 1,440° C. under an essentially inert atmosphere at a reduced pressure of less than 10 mmHg, the partial pressure of oxygen in said atmosphere being less than 10 -10 atmospheres, said powders when mixed with 1% by weight each of boron and carbon and then heated at 2,100° C. for 60 minutes forming a sintered body having a density of 96% of theoretical density, a fine particle structure of less than 10 μm, a bending strength of 82.0 kg/mm 2 in the three point bending test at 1700° C. at 10 -6 mmHg and containing more than 90%-β-type silicon carbide.
Claim 3
Dependent Claim
82 words
A sintered body produced by mixing the sinterable silicon carbide powders of claim 1 with 1% by weight each of boron and carbon, and heating said mixture at 2,100° C. for 60 minutes said sintered body having a density of 96% of theoretical density, a fine particle structure of less than 10 μm, a bending strength of 82.0 kg/mm 2 in the three point bending test at 1700° C. at 10 -6 mmHg and containing more than 90% of β-type silicon carbide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-08-02 | 1986-02-01 | 1986-08-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-08-02 | 1990-02-01 | 1990-08-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-08-02 | 1994-02-01 | 1994-08-03 | $7700.00 | Window Closed / Lapsed |