Magnetic particle inspection process useable with simultaneous illumination by ultra-violet and white light
Assignee: Illinois Tool Works Inc
•
Filing: 1979-11-14
•
Granted: 1982-07-27
•
Expires: 1999-11-14
Abstract
Abstract A method and composition for non-destructive testing of a magnetizable workpiece in which the surface of the workpiece is coated with a composition containing discrete magnetic particles consisting of a ferromagnetic particle core, fluorescent pigment particles attached to said core and a cascading opacifier combined therewith, preferably by means of a film-forming encapsulating resin. The particles of the daylight fluorescent pigment are sufficiently large so that they fluoresce with sufficient intensity to be seen in normal lighting conditions. Consequently, the magnetizable pieces to be inspected can be simultaneously inspected under ultra-violet and white light excitation to reveal both fine cracks and large voids.
Inventors
- 👤 Kenneth P. Borrows
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 06:41
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/72; G01N27/82; G01N27/83; G01N27/84; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/032; H01F1/04; H01F1/06; H01F1/061; H01F1/10; H01F1/11; H01F1/113
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
148 words
A method of non-destructive testing of a magnetizable workpiece which comprises: applying to the surface of said workpiece discrete magnetic particles having a ferromagnetic particle core, fluorescent pigment particles physically attached to said core and a cascading opacifier, said fluorescent pigment particles being at least 10 microns in maximum dimension, said magnetic core particles having a maximum dimension at least twice as large as the maximum dimension of said fluorescent pigment particles, creating a magnetic field along said workpiece so that the particles are attracted to imperfections therein, and inspecting said workpiece for imperfections while simultaneously illuminating said workpiece with separate sources of ultra-violet and white light, said magnetic particles having the property of fluorescing with a brightness of at least 20 foot-lamberts when irradiated with 365 nm ultra-violet light at an intensity of 1000 microwatts/cm 2 , the ambient white light level being at least 10 foot-lamberts.
Claim 2
Independent Claim
148 words
A method of non-destructive testing of a magnetizable workpiece which comprises: applying to the surface of said workpiece discrete magnetic particles having a ferromagnetic particle core, fluorescent pigment particles physically attached to said core and a cascading opacifier, said fluorescent pigment particles being at least 10 microns in maximum dimension, said magnetic core particles having a maximum dimension at least twice as large as the maximum dimension of said fluorescent pigment particles, creating a magnetic field along said workpiece so that the particles are attracted to imperfections therein, and inspecting said workpiece for imperfections while simultaneously illuminating said workpiece with separate sources of ultra-violet and white light, said magnetic particles having the property of fluorescing with a brightness of at least 20 foot-lamberts when irradiated with 365 nm ultra-violet light at an intensity of 1000 microwatts/cm 2 , the ambient white light level being at least 10 foot-lamberts.
Claim 3
Dependent Claim
12 words
A method according to claim 1 in which said opacifier is fluoranthene.
Claim 4
Dependent Claim
21 words
A method according to claim 1 in which: said core particles have a maximum dimension of from 25 to 150 microns.
Claim 5
Dependent Claim
22 words
A method according to claim 1 in which: said fluorescent pigment particles have a maximum dimension of from 10 to 50 microns.
Claim 6
Dependent Claim
24 words
A method according to claim 1 in which: said magnetic particles, said opacifier and said fluorescent pigment particles are encapsulated in a film-forming resin.
References Cited (Backward Citations)
US3402349A
Cited
GB1154462A
Cited
US3485758A
Cited
GB1289727A
Cited
US3609532A
Cited
GB1527745A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-26 | 1986-01-25 | 1986-07-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-26 | 1990-01-25 | 1990-07-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-26 | 1994-01-25 | 1994-07-27 | $7700.00 | Window Closed / Lapsed |