Vinyl gum cure accelerators for addition-cure silicone
Assignee: General Electric Co
•
Filing: 1981-05-22
•
Granted: 1982-07-20
•
Expires: 2001-05-22
Abstract
Abstract There are provided addition-curable silicone release compositions comprised of a vinyl or silanol functional polymer base, a crosslinker containing silanic hydrogen, a precious metal catalyst such as platinum or rhodium, an optional carboxylic ester inhgibitor and silicone vinyl gum cure accelerations effective for allowing thermal cure at relatively lower temperatures while minimizing the necessity of excess metal catalyst.
Inventors
- 👤 Richard P. Eckberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 06:53
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/10; D; D21; D21H; D21H19/00; D21H19/10; D21H19/14; D21H19/24; D21H19/32; C08; C08K; C08K5/00; C08K5/04; C08K5/10; C08K5/11; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/16; C08G77/20; Y; Y10; Y10T; Y10T428/00; Y10T428/27; Y10T428/273; Y10T428/277; Y10T428/31504; Y10T428/31551; Y10T428/31609; Y10T428/31612; Y10T428/31634
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
182 words
A silicone release coating composition comprising: A. A solventless addition curable composition comprised of: (i) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl or silanol functional groups and having a viscosity ranging from approximately 50 to approximately 100,000 centipoise at 25° C.; (ii) a polymethylhydrogen siloxane fluid crosslinking agent having up to approximately 100% by weight SiH-containing siloxy groups and having a viscosity in the range of approximately 25 to approximately 1000 centipoise at 25° C.; (iii) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction between said base polymer and said crosslinking agent at temperatures between, approximately, 90° C. to 300° C.; (iv) an amount of dialkyl carboxylic ester containing carbon to carbon unsaturation effective to inhibit the precious metal catalyzed hydrosilation cure reaction of said silicone composition at temperatures below the heat cure temperature of said silicone composition, and B. an amount of dimethylvinyl chainstopped polydimethylmethylvinylsiloxane polymer gum effective for accelerating the cure of said addition curable composition wherein said gum has an average molecular weight of, approximately, 200,000 to 400,000.
Claim 2
Dependent Claim
182 words
A silicone release coating composition comprising: A. A solventless addition curable composition comprised of: (i) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl or silanol functional groups and having a viscosity ranging from approximately 50 to approximately 100,000 centipoise at 25° C.; (ii) a polymethylhydrogen siloxane fluid crosslinking agent having up to approximately 100% by weight SiH-containing siloxy groups and having a viscosity in the range of approximately 25 to approximately 1000 centipoise at 25° C.; (iii) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction between said base polymer and said crosslinking agent at temperatures between, approximately, 90° C. to 300° C.; (iv) an amount of dialkyl carboxylic ester containing carbon to carbon unsaturation effective to inhibit the precious metal catalyzed hydrosilation cure reaction of said silicone composition at temperatures below the heat cure temperature of said silicone composition, and B. an amount of dimethylvinyl chainstopped polydimethylmethylvinylsiloxane polymer gum effective for accelerating the cure of said addition curable composition wherein said gum has an average molecular weight of, approximately, 200,000 to 400,000.
Claim 3
Dependent Claim
25 words
A composition as in claim 1 wherein said gum is present in an amount of at least 0.5 weight percent of said addition curable composition.
Claim 4
Dependent Claim
24 words
A composition as in claim 1 wherein said gum has a methyl-vinyl siloxy unit content if 0 to 5 mole % of said gum.
Claim 5
Dependent Claim
158 words
A silicone release coating composition comprising: A. a solvent based addition curable composition comprised of: (i) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl or silanol functional groups and having a viscosity ranging from approximately 50 to approximately 100,000 centipoise at 25° C.; (ii) a polymethylhydrogen siloxane fluid crosslinking agent having up to approximately 100% by weight SiH-containing siloxy groups and having a viscosity in the range of approximately 25 to approximately 1000 centipoise at 25° C.; (iii) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction between said base polymer and said crosslinking agent at temperatures between approximately, 90° to 300° C.; (iv) an amount of hydrocarbon solvent effective for dispersing said addition curable composition; and B. an amount of dimethylvinyl chainstopped polydimethylmethylvinylsiloxane polymer gum effective for accelerating the cure of said addition curable composition wherein said gum has an average molecular weight of, approximately, 200,000 to 400,000.
Claim 6
Dependent Claim
158 words
A silicone release coating composition comprising: A. a solvent based addition curable composition comprised of: (i) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl or silanol functional groups and having a viscosity ranging from approximately 50 to approximately 100,000 centipoise at 25° C.; (ii) a polymethylhydrogen siloxane fluid crosslinking agent having up to approximately 100% by weight SiH-containing siloxy groups and having a viscosity in the range of approximately 25 to approximately 1000 centipoise at 25° C.; (iii) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction between said base polymer and said crosslinking agent at temperatures between approximately, 90° to 300° C.; (iv) an amount of hydrocarbon solvent effective for dispersing said addition curable composition; and B. an amount of dimethylvinyl chainstopped polydimethylmethylvinylsiloxane polymer gum effective for accelerating the cure of said addition curable composition wherein said gum has an average molecular weight of, approximately, 200,000 to 400,000.
Claim 7
Dependent Claim
25 words
A composition as in claim 4 wherein said gum is present in an amount of at least 0.5 weight percent of said addition curable composition.
Claim 8
Dependent Claim
25 words
A composition as in claim 4 wherein said solvent is selected from the group consisting of hexane, toluene, naptha, xylene, and benzene and mixtures thereof.
Claim 9
Dependent Claim
23 words
A composition as in claim 4 wherein said gum has a methyl-vinyl siloxy content of 0 to 5 mole % of said gum.
Claim 10
Dependent Claim
28 words
A composition as in claim 2 or 5 wherein said gum is present in an amount of, approximately, 5 to 10 weight percent of said addition curable composition.
Claim 11
Dependent Claim
8 words
The cured product of claim 1 or 4.
Claim 12
Dependent Claim
17 words
An article of manufacture comprising a paper substrate coated with the composition of claim 1 or 4.
Claim 13
Independent Claim
164 words
A method for rendering substrates relatively nonadherent to substances that would normally adhere thereto, comprising the steps of: A. combining (a) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl or silanol functional groups and having a viscosity ranging from approximately 50 to approximately 100,000 centipoise at 25° C.; (b) a polymethylhydrogen siloxane fluid crosslinking agent having up to approximately 100% by weight SiH-containing siloxy groups and having a viscosity in the range of approximately 25 to approximately 1000 centipoise at 25° C.; (c) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction between said base polymer and said crosslinking agent at temperatures between, approximately, 90° to 300° C.; and (d) an amount of dimethylvinyl chainstopped polydimethylmethylvinyl siloxane polymer gum effective for accelerating the cure of an addition curable composition wherein said gum has an average molecular weight of, approximately, 200,000 to 400,000 and a methyl-vinyl siloxy unit content of, approximately, 0 to 5.0 mole %.
Claim 14
Independent Claim
164 words
A method for rendering substrates relatively nonadherent to substances that would normally adhere thereto, comprising the steps of: A. combining (a) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl or silanol functional groups and having a viscosity ranging from approximately 50 to approximately 100,000 centipoise at 25° C.; (b) a polymethylhydrogen siloxane fluid crosslinking agent having up to approximately 100% by weight SiH-containing siloxy groups and having a viscosity in the range of approximately 25 to approximately 1000 centipoise at 25° C.; (c) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction between said base polymer and said crosslinking agent at temperatures between, approximately, 90° to 300° C.; and (d) an amount of dimethylvinyl chainstopped polydimethylmethylvinyl siloxane polymer gum effective for accelerating the cure of an addition curable composition wherein said gum has an average molecular weight of, approximately, 200,000 to 400,000 and a methyl-vinyl siloxy unit content of, approximately, 0 to 5.0 mole %.
Claim 15
Dependent Claim
17 words
A method as in claim 11 further comprising the step of coating said composition upon a substrate.
Claim 16
Dependent Claim
14 words
A method as in claim 12 further comprising the step of curing said composition.
Claim 17
Dependent Claim
11 words
A process as in claim 12 wherein said substrate is paper.
Claim 18
Dependent Claim
50 words
A process in claim 11 wherein said addition curable composition is further comprised of an amount of dialkyl carboxylic ester containing carbon to carbon unsaturation effective to inhibit the precious metal catalyzed hydrosilation cure reaction of said silicone composition at temperatures below the heat cure temperature of said silicone composition.
Claim 19
Dependent Claim
16 words
A process as in claim 11 wherein said addition curable composition is dispersed in a solvent.
Claim 20
Dependent Claim
25 words
A process as in claim 11 wherein said gum is present in an amount of at least 0.5 weight percent of said addition curable composition.
Claim 21
Dependent Claim
9 words
A product made by the process of claim 11.
Claim 22
Dependent Claim
115 words
A silicone composition capable of low temperature crosslinking to a nonadherent film when combined with a methyl hydrogen siloxy crosslinking fluid, comprised of: (a) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl and silanol functional groups and a viscosity of, approximately, 50 to 100,000 centipoise at 25° C.; (b) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction at temperatures between 90° to 300° C.; (c) an amount of dialkyl carboxylic ester effective to inhibit said hydrosilation cure reaction at temperatures below the heat cure temperature of said composition; and (d) an amount of dimethylvinyl chainstopped polydimethylvinylsiloxane gum effective for accelerating the cure of said composition.
Claim 23
Dependent Claim
115 words
A silicone composition capable of low temperature crosslinking to a nonadherent film when combined with a methyl hydrogen siloxy crosslinking fluid, comprised of: (a) a diorganopolysiloxane base polymer having up to approximately 20% by weight alkenyl and silanol functional groups and a viscosity of, approximately, 50 to 100,000 centipoise at 25° C.; (b) an effective amount of precious metal catalyst for facilitating an addition cure hydrosilation reaction at temperatures between 90° to 300° C.; (c) an amount of dialkyl carboxylic ester effective to inhibit said hydrosilation cure reaction at temperatures below the heat cure temperature of said composition; and (d) an amount of dimethylvinyl chainstopped polydimethylvinylsiloxane gum effective for accelerating the cure of said composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |