US4340635A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ceramic substrate for fine-line electrical circuitry
Assignee: COORS PROCELAIN COMPANY GOLDEN CO A CORP OF
•
Filing: 1980-12-15
•
Granted: 1982-07-20
•
Expires: 2000-12-15
Abstract
Abstract In accordance with the invention there is provided a sintered monolithic ceramic substrate for fine-line electrical circuitry, the substrate comprising a base layer containing at least 90% by weight crystalline alumina or beryllia and a thin upper layer containing at least 90% by weight crystalline material the same as that of the base layer but with an average grain size less than that of the crystalline material of the base layer, the upper layer having an irregular interface with the base layer but a planar upper surface with minimal surface irregularities for improved reception of the fine-line circuitry to be applied. Further in accordance with the invention such substrate is made by first forming and firing a ceramic plate of alumina or beryllia ceramic to provide the base layer and then applying and firing a coating of fine grain alumina or beryllia, as the case may be, on the plate to provide the upper layer.
Inventors
- 👤 Richard A. Langman
- 👤 Donald R. Giovanini
- 👤 Michael P. Letzig
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:42
CPC Classifications
H; H10; H10W; H10W70/00; H10W70/60; H10W70/67; H10W70/69; H10W70/692; C; C04; C04B; C04B35/00; C04B35/01; C04B35/10; C04B35/111; C04B41/00; C04B41/45; C04B41/50; C04B41/5025; C04B41/80; C04B41/81; C04B41/85; C04B41/87; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/0011; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24479; Y10T428/24521; Y10T428/24545; Y10T428/24612; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/24975; Y10T428/25; Y10T428/256; Y10T428/257; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/31
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
120 words
A sintered monolithic ceramic substrate for fine-line electrical circuitry, said substrate comprising a relatively thick base layer with an upper surface having irregularities therein thin upper layer with a relatively planar upper surface, said upper layer filling substantially all the surface irregularities in the upper surface of the base layer, each of said layers containing at least about 90% by weight crystalline material, the crystalline material of said base layer being substantially all an oxide selected from the group consisting of alumina and beryllia and the crystalline material of said upper layer being substantially all the same as that of the base layer but having an average grain size less than that of the crystalline material of said base layer.
Claim 2
Dependent Claim
120 words
A sintered monolithic ceramic substrate for fine-line electrical circuitry, said substrate comprising a relatively thick base layer with an upper surface having irregularities therein thin upper layer with a relatively planar upper surface, said upper layer filling substantially all the surface irregularities in the upper surface of the base layer, each of said layers containing at least about 90% by weight crystalline material, the crystalline material of said base layer being substantially all an oxide selected from the group consisting of alumina and beryllia and the crystalline material of said upper layer being substantially all the same as that of the base layer but having an average grain size less than that of the crystalline material of said base layer.
Claim 3
Dependent Claim
21 words
A sintered monolithic ceramic substrate as set forth in claim 1 wherein at least said base layer contains a glassy phase.
Claim 4
Dependent Claim
38 words
A sintered monolithic ceramic substrate as set forth in claim 2 wherein the average grain size of the crystalline material in said upper layer is no more than one-half that of the crystalline material in said base layer.
Claim 5
Dependent Claim
50 words
A sintered monolithic ceramic substrate as set forth in claim 2 wherein the average grain size of the crystalline material in said base layer is from about 6 to 8 microns and the average grain size of the crystalline material in said upper layer is from 2.5 to 3.5 microns.
Claim 6
Dependent Claim
28 words
A sintered monolithic ceramic substrate as set forth in claim 1, 2 or 4 wherein the thickness of the upper layer is from about 0.0002 to 0.001 inches.
Claim 7
Dependent Claim
29 words
A sintered monolithic ceramic substrate as set forth in claim 1, 2 or 4 wherein each of said layers contains at least 95% by weight of said crystalline material.
Claim 8
Dependent Claim
20 words
A sintered monolithic ceramic substrate as set forth in claim 1, 2 or 4 wherein the crystalline material is alumina.
References Cited (Backward Citations)
US3764444A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |