Spinning process
Assignee: EIDP Inc
•
Filing: 1980-10-31
•
Granted: 1982-07-20
•
Expires: 2000-10-31
Abstract
Abstract Improved aromatic polyamide fibers from aromatic polyamides whose chain-extending bonds are either coaxial or parallel and oppositely directed are obtained by dry spinneret wet spinning into a shallow coagulating bath having an orifice in its bottom for removal of coagulating liquid and fibers wherein no more than a minor portion of coagulating liquid is lower than the entrance of the bath orifice in the proximity of the bath orifice. Preferably, no more than 10% of the coagulating liquid is lower than the entrance of the bath orifice and most preferably none of the coagulating liquid is lower than the entrance of the bath orifice.
Inventors
- 👤 Hung H. Yang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 20:05
CPC Classifications
D; D01; D01F; D01F6/00; D01F6/58; D01F6/60; D01F6/605; D01D; D01D5/00; D01D5/06
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
182 words
A process for spinning high strength, high modulus aromatic polyamide filaments from aromatic polyamides having an inherent viscosity of at least 4.0 whose chain extending bonds are coaxial or parallel and oppositely directed by extruding downwardly an anisotropic solution in 98.0-100.2% sulfuric acid having a polyamide concentration of at least 30 g/100 ml solvent through a layer of noncoagulating fluid into a coagulating bath whereby overflowing coagulating liquid passes downwardly through an orifice along with the filaments, the filaments are separated from the coagulating liquid, forwarded at 500 to 2,000 m/min., washed, dried and wound up, wherein a shallow bath is used, said bath having sufficient width to provide substantially horizontal nonturbulent flow of coagulating liquid toward said orifice and having no more than a minor portion of the total coagulating liquid lower than the entrance of said orifice within the area of nonturbulent flow adjacent to said orifice, the orifice having a length to diameter ratio of 3 or less and the cross-sectional area of the orifice being such as to provide a mass flow ratio of quench liquid/polymer of 25-200.
Claim 2
Dependent Claim
182 words
A process for spinning high strength, high modulus aromatic polyamide filaments from aromatic polyamides having an inherent viscosity of at least 4.0 whose chain extending bonds are coaxial or parallel and oppositely directed by extruding downwardly an anisotropic solution in 98.0-100.2% sulfuric acid having a polyamide concentration of at least 30 g/100 ml solvent through a layer of noncoagulating fluid into a coagulating bath whereby overflowing coagulating liquid passes downwardly through an orifice along with the filaments, the filaments are separated from the coagulating liquid, forwarded at 500 to 2,000 m/min., washed, dried and wound up, wherein a shallow bath is used, said bath having sufficient width to provide substantially horizontal nonturbulent flow of coagulating liquid toward said orifice and having no more than a minor portion of the total coagulating liquid lower than the entrance of said orifice within the area of nonturbulent flow adjacent to said orifice, the orifice having a length to diameter ratio of 3 or less and the cross-sectional area of the orifice being such as to provide a mass flow ratio of quench liquid/polymer of 25-200.
Claim 3
Dependent Claim
30 words
The process of claim 1 wherein the volume of coagulating liquid lower than the orifice entrance is less than 10% of the coagulating liquid in the area of nonturbulent flow.
Claim 4
Dependent Claim
22 words
The process of claim 1 wherein there is no coagulating liquid in the area of nonturbulent flow lower than the orifice entrance.
Claim 5
Dependent Claim
91 words
The process of claim 1 wherein the orifice is followed immediately by a jet device whereby additional coagulating liquid is applied symmetrically about the filaments in a downward direction forming an angle θ of 0° to 85° with respect to the filaments within 2.0 milliseconds from the time the filaments enter the orifice, the total flow rate of both overflowing coagulating liquid and additional coagulating liquid being maintained constant such that the momentum ratio θ is from 0.5 to 6.0 and the mass flow ratio of total quench liquid/polymer is 25-200.
Claim 6
Dependent Claim
35 words
The process of claim 3 wherein the depth of the coagulating liquid in the coagulating bath measured from the level of its upper surface to the orifice entrance is less than 1 inch (2.54 cm.).
Claim 7
Dependent Claim
22 words
The process of claim 5 wherein the depth of coagulating liquid in the coagulating bath is less than 0.625 inch (1.6 cm.).
References Cited (Backward Citations)
US3767756A
Cited
US4078034A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-19 | 1986-01-18 | 1986-07-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-19 | 1990-01-18 | 1990-07-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-19 | 1994-01-18 | 1994-07-20 | $7700.00 | Window Closed / Lapsed |