Process for producing propylene-ethylene block copolymer
Assignee: Mitsubishi Chemical Corp
•
Filing: 1980-09-02
•
Granted: 1982-07-13
•
Expires: 2000-09-02
Abstract
Abstract A propylene-ethylene block copolymer is produced in the presence of a catalytic system essentially comprising an organoaluminum compound and a solid titanium trichloride catalytic complex having an atomic ratio of Al to Ti of less than 0.15 and having a complexing agent in two stages of polymerization; (a) a first stage for polymerizing propylene in the presence of a liquid propylene and hydrogen to produce a propylene homopolymer having a melt flow index of 1 to 150 at a ratio of 70 to 95% by weight based on a total of polymers; and (b) a second stage for copolymerizing propylene and ethylene in the presence of hydrogen and a liquid propylene at a concentration of propylene in vapor phase based on a total of propylene and ethylene in vapor phase of 50 to 85 mol. % and at a concentration of hydrogen in vapor phase based on a total of propylene and ethylene in vapor phase of 0.5 to 30 mol %, to produce ethylene-propylene copolymer having a melt flow index of 10-7 to 0.1 at a ratio of 5 to 30% by weight based on a total of polymers.
Inventors
- 👤 Masayoshi Hasuo
- 👤 Yoshinori Suga
- 👤 Kazuhisa Kojima
- 👤 Masatoshi Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 21:32
CPC Classifications
C; C08; C08F; C08F297/00; C08F297/06; C08F297/08; C08F297/083
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
205 words
A process for producing a propylene-ethylene block copolymer in two stages of polymerization in the presence of a catalyst system comprising an organo aluminum compound and a solid titanium trichloride catalyst complex having an atomic ratio of Al to Ti of less than 0.15 and containing a complexing agent, comprising: (a) a first stage of polymerizing propylene in the presence of liquid propylene and hydrogen, thereby producing a propylene homopolymer having a melt flow index of 1-150 in an amount of 70% to 95% by wt. based on the total amount of block copolymer; and (b) a second stage of copolymerizing propylene and ethylene at a temperature of 25° C. to 70° C. in the presence of hydrogen and liquid propylene at a concentration of propylene in the vapor phase based on the total amount of propylene and ethylene in the vapor phase of 50-85 mole % and at a concentration of hydrogen in the vapor phase based on the total amount of propylene and ethylene in the vapor phase of 0.5-30 mole %, thereby producing an ethylene-propylene random copolymer having a melt flow index of 10 -7 -0.1 in an amount of 5-30% by wt. based on the total amount of block copolymer material.
Claim 2
Dependent Claim
205 words
A process for producing a propylene-ethylene block copolymer in two stages of polymerization in the presence of a catalyst system comprising an organo aluminum compound and a solid titanium trichloride catalyst complex having an atomic ratio of Al to Ti of less than 0.15 and containing a complexing agent, comprising: (a) a first stage of polymerizing propylene in the presence of liquid propylene and hydrogen, thereby producing a propylene homopolymer having a melt flow index of 1-150 in an amount of 70% to 95% by wt. based on the total amount of block copolymer; and (b) a second stage of copolymerizing propylene and ethylene at a temperature of 25° C. to 70° C. in the presence of hydrogen and liquid propylene at a concentration of propylene in the vapor phase based on the total amount of propylene and ethylene in the vapor phase of 50-85 mole % and at a concentration of hydrogen in the vapor phase based on the total amount of propylene and ethylene in the vapor phase of 0.5-30 mole %, thereby producing an ethylene-propylene random copolymer having a melt flow index of 10 -7 -0.1 in an amount of 5-30% by wt. based on the total amount of block copolymer material.
Claim 3
Dependent Claim
92 words
The process of claim 1, wherein said solid titanium trichloride catalyst complex comprises a titanium trichloride component; an aluminum halide component having the formula: AlR.sub.P.sup.3 X.sub.3-P, wherein R 3 represents a C 1 -C 20 hydrocarbon moiety, X represents a halogen atom, and 0≦P≦2, the amounts of said aluminum halide and titanium trichloride components being such that the atomic ratio of Al to Ti is less than 0.15; and a complexing agent, the molar ratio of said complexing agent relative to said titanium trichloride and aluminum halide components being more than 0.001.
Claim 4
Dependent Claim
39 words
The process of claim 1 or 2, wherein said solid titanium trichloride catalyst complex has an integrated micropore volume of more than 0.02 cm 3 /g and a pore radii of 20-500 A as measured by a mercury porosimeter.
Claim 5
Dependent Claim
37 words
The process of claim 1 or 2, wherein said solid titanium trichloride catalyst complex is obtained by precipitation from a solution of titanium trichloride in an ether or a thioether at a temperature less than 150° C.
Claim 6
Dependent Claim
41 words
The process of claim 1 or 2, wherein said solid titanium trichloride catalyst complex is obtained by reducing titanium tetrachloride with an organoaluminum compound or metallic aluminum and treating the resulting solid titanium trichloride with a complexing agent and a halide.
Claim 7
Dependent Claim
25 words
The method of claim 1, wherein the amount of hydrogen in the vapor phase in said first stage ranges from 1 to 30 mole %.
Claim 8
Dependent Claim
26 words
The method of claim 1, wherein the content of propylene in the random copolymer produced in said second stage ranges from 30% to 70% by wt.
Claim 9
Dependent Claim
20 words
The method of claim 1, wherein the temperature of polymerization in said first stage ranges from 40° to 100° C.
Claim 10
Dependent Claim
34 words
The method of claim 1, wherein the polymerization of propylene in said first stage is conducted in an inert liquid hydrocarbon selected from the group consisting of aliphatic hydrocarbons, alicyclic hydrocarbons and aromatic hydrocarbons.
References Cited (Backward Citations)
US3970719A
Cited
US3970719B1
Cited
US3873642A
Cited
US3358056A
Cited
US3401212A
Cited
US3318976A
Cited
US3859387A
Cited
US4066718A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-07-12 | 1986-01-11 | 1986-07-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-07-12 | 1990-01-11 | 1990-07-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-07-12 | 1994-01-11 | 1994-07-13 | $7700.00 | Window Closed / Lapsed |